Product Cure System Viscosity Non Volatile Content Durometer Data Sheet Comment
CV-1152 Oxime 7,300 cP N/A N/A Download CV-1152 data sheet Soft, very low modulus coating

Product Details

Property Average Result
Viscosity 7,300 cP (7,300 mPa*s)
Appearance Translucent
Tack Free Time 50 minutes
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Refractive Index 1.43
Specific Gravity 1.01
Comment Soft, very low modulus coating

View more

R-1008-0 Oxime 1,300 cP 70 % 23 Type A Download R-1008-0 data sheet N/A

Product Details

Property Average Result
Viscosity 1,300 cP (1,300 mPa*s)
Non Volatile Content 70 %
Appearance Translucent
Dielectric Strength 513 volts/mil (20.01 kV/mm)
Durometer 23 Type A
Elongation 223 %
Tack Free Time 50 minutes
Tensile 235 psi (1.62 MPa)
Thermal Conductivity 0.17 W/(mK)

View more

R-1009 Oxime 6,150 cP 32 % 45 Type A Download R-1009 data sheet High strength coating recommend for coating PCBs and other electronic assemblies.

Product Details

Property Average Result
Viscosity 6,150 cP (6,150 mPa*s)
Non Volatile Content 32 %
Appearance Translucent
Tack Free Time 1.5 hours
Cure 7 days / RTV
Cure System Oxime
Durometer 45 Type A
Elongation 650 %
Specific Gravity 1.1
Tear 95 ppi (16.75 kN/m)
Tensile 1,150 psi (7.93 MPa)
Comment High strength coating recommend for coating PCBs and other electronic assemblies.

View more

R-1077 N/A 3,400 cP 60 % 40 Type A Download R-1077 data sheet N/A

Product Details

Property Average Result
Viscosity 3,400 cP (3,400 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Tack Free Time 20 minutes
Cure 6 days / RTV
Durometer 40 Type A
Elongation 330 %
Tensile 745 psi (5.14 MPa)

View more

R-1082 Acetoxy 700 cP 29 % 25 Type A Download R-1082 data sheet Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

Product Details

Property Average Result
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Appearance Translucent
Cure 5 days / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 950 %
Refractive Index 1.41
Specific Gravity 1.09
Stress at Strain 160 psi / 300 % (1.1 Mpa / 300 %)
Tear 125 ppi (22.05 kN/m)
Tensile 1,425 psi (9.83 MPa)
Comment Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

View more

R-1099 Condensation 6,600 cP 30 % 40 Type A Download R-1099 data sheet N/A

Product Details

Property Average Result
Viscosity 6,600 cP (6,600 mPa*s)
Non Volatile Content 30 %
Appearance Translucent
Tack Free Time 10 minutes
Cure 7 days / RTV
Cure System Condensation
Dielectric Strength 635 volts/mil (24.77 kV/mm)
Durometer 40 Type A
Elongation 570 %
Mix Ratio 1 Part
Tensile 1,050 psi (7.24 MPa)

View more

R-1182 Acetoxy N/A 7 % N/A Download R-1182 data sheet One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

Product Details

Property Average Result
Non Volatile Content 7 %
Appearance Translucent
Cure RTV
Cure System Acetoxy
Comment One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

View more

R-2180 Platinum 3,075 cP 20 % 40 Type A Download R-2180 data sheet High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

Product Details

Property Average Result
Viscosity 3,075 cP (3,075 mPa*s)
Non Volatile Content 20 %
Appearance Translucent
Cure 45 minutes / 75 °C 135 minutes / 150 °C
Cure System Platinum
Durometer 40 Type A
Elongation 1,050 %
Mix Ratio 1:1
Refractive Index 1.41
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Work Time 72 hours
Comment High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

View more

R-2182 Platinum 24 cP 25 % N/A Download R-2182 data sheet Requires minimum heat to cure. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

Product Details

Property Average Result
Viscosity 24 cP (24 mPa*s)
Non Volatile Content 25 %
Appearance Translucent
Cure 5 minutes / RTV
Cure System Platinum
Mix Ratio 1:1
Post Cure 5 minutes / 150 °C
Specific Gravity 0.96
Work Time 24 hours
Comment Requires minimum heat to cure. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

View more

R-3930 Acetoxy 735 cP 60 % 30 Type A Download R-3930 data sheet 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

Product Details

Property Average Result
Viscosity 735 cP (735 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 30 Type A
Elongation 400 %
Specific Gravity 1.36
Tear 40 ppi (7.05 kN/m)
Tensile 750 psi (5.17 MPa)
Comment 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.