Product Cure System Viscosity Non Volatile Content Durometer Data Sheet Comment
MED-2014 Platinum 1,800 cP 35 % N/A Download MED-2014 data sheet One Part, Requires heat to cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,800 cP (1,800 mPa*s)
Non Volatile Content 35 %
Appearance Translucent
Cure 60 minutes / 50 °C 60 minutes / 150 °C 3 minutes / RTV
Elongation 900 %
Mix Ratio 1 PART
Solvent Xylene
Tear 160 ppi (28.22 kN/m)
Tensile 1,700 psi (11.72 MPa)
Comment One Part, Requires heat to cure

View more

MED-4159 Amine 200 cSt 53 % N/A Download MED-4159 data sheet Low Crosslink Density, Amino Functional Lubricious Silicone Coating

Product Details

Property Average Result
Cure System Amine
Viscosity 200 cSt
Non Volatile Content 53 %
Appearance Clear
Cure 7 days / RTV
Mix Ratio 1 PART
Solvent Stoddard Solvent & IPA
Comment Low Crosslink Density, Amino Functional Lubricious Silicone Coating

View more

MED-4162 Non-Curing 27,000 cP 31 % N/A Download MED-4162 data sheet Lubricious Coating

Product Details

Property Average Result
Cure System Non-Curing
Viscosity 27,000 cP (27,000 mPa*s)
Non Volatile Content 31 %
Appearance Translucent
Mix Ratio 1 PART
Solvent Xylene
Comment Lubricious Coating

View more

MED10-4161 Amine 140 cSt 33 % 25 Type 00 Download MED10-4161 data sheet Amino Functional Lubricious Silicone Coating

Product Details

Property Average Result
Cure System Amine
Viscosity 140 cSt (120.04 mPa*s)
Non Volatile Content 33 %
Durometer 25 Type 00
Appearance Clear
Cure 5 days / 25 °C
Mix Ratio 1 PART
Solvent Xylene
Specific Gravity 0.86
Comment Amino Functional Lubricious Silicone Coating

View more

MED10-6400 Platinum 800 cP 35 % 30 Type A Download MED10-6400 data sheet 1.43 R.I.

Product Details

Property Average Result
Cure System Platinum
Viscosity 800 cP (800 mPa*s)
Non Volatile Content 35 %
Durometer 30 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 800 %
Mix Ratio 1:1
Solvent Xylene
Tear 150 ppi (26.46 kN/m)
Tensile 1,500 psi (10.34 MPa)
Comment 1.43 R.I.

View more

MED10-6600 Platinum 400 cP 35 % 25 Type A Download MED10-6600 data sheet 1.46 R.I.

Product Details

Property Average Result
Cure System Platinum
Viscosity 400 cP (400 mPa*s)
Non Volatile Content 35 %
Durometer 25 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 750 %
Mix Ratio 1:1
Refractive Index 1.46
Solvent Xylene
Stress at Strain 325 psi / 300 % (2.24 Mpa / 300 %)
Tear 145 ppi (25.57 kN/m)
Tensile 1,200 psi (8.28 MPa)
Comment 1.46 R.I.

View more

MED10-6605 Acetoxy 700 cP 29 % 25 Type A Download MED10-6605 data sheet One Part

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Durometer 25 Type A
Appearance Translucent
Cure 5 days / RTV
Elongation 950 %
Mix Ratio 1 PART
Solvent Xylene
Stress at Strain 160 psi / 300 % (1.1 Mpa / 300 %)
Tear 125 ppi (22.05 kN/m)
Tensile 1,500 psi (10.34 MPa)
Comment One Part

View more

MED10-6607 Oxime 6,000 cP 35 % 40 Type A Download MED10-6607 data sheet One Part

Product Details

Property Average Result
Cure System Oxime
Viscosity 6,000 cP (6,000 mPa*s)
Non Volatile Content 35 %
Durometer 40 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 650 %
Mix Ratio 1 PART
Solvent Naptha
Specific Gravity 1.1
Tear 95 ppi (16.75 kN/m)
Tensile 1,200 psi (8.28 MPa)
Comment One Part

View more

MED10-6615 Platinum 65 cP 32 % 72 Type 00 Download MED10-6615 data sheet Silicone adhesive dispersed in heptane, cures rapidly with heat

Product Details

Property Average Result
Cure Type Heat Cure
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 30 minutes / RTV
Cure System Platinum
Durometer 72 Type 00
Elongation 750 %
Non Volatile Content 32 %
Substrate Primerless: Aluminum / Glass / PMMA / Silicone / With Primer: PEEK / Polycarbonate / Polyetherimide / ABS / Polyimide / Polysulphone / Polyurethane / Stainless steel
Tear 120 ppi (21.16 kN/m)
Tensile 1,060 psi (7.31 MPa)
Viscosity 65 cP (65 mPa*s)
Comment Silicone adhesive dispersed in heptane, cures rapidly with heat

View more

MED10-6640 Platinum 2,500 cP 20 % 40 Type A Download MED10-6640 data sheet Ultra High Tear

Product Details

Property Average Result
Cure System Platinum
Viscosity 2,500 cP (2,500 mPa*s)
Non Volatile Content 20 %
Durometer 40 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 1,000 %
Mix Ratio 1:1
Refractive Index 1.41
Solvent Xylene
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Comment Ultra High Tear

View more

MED10-6655 Acetoxy 700 cP 60 % 35 Type A Download MED10-6655 data sheet 100M% Fluorosilicone

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 60 %
Durometer 35 Type A
Appearance White
Cure 3 days / RTV
Elongation 425 %
Mix Ratio 1 PART
Solvent Butyl Acetate
Tear 45 ppi (7.94 kN/m)
Tensile 775 psi (5.34 MPa)
Comment 100M% Fluorosilicone

View more

MED10-6670 Platinum N/A 25 % N/A Download MED10-6670 data sheet Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Platinum
Non Volatile Content 25 %
Appearance Translucent
Cure 5 minutes / RTV
Mix Ratio 1:1
Solvent Xylene

View more

MED10-6671 Acetoxy N/A N/A N/A Download MED10-6671 data sheet RTV, Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Acetoxy
Appearance Translucent
Cure 24 hours / RTV
Mix Ratio 1 Part
Comment RTV, Low Coefficient of Friction Coating

View more

MED11-6604 Acetoxy 250 cP 50 % 15 Type A Download MED11-6604 data sheet One Part, Smooth Finish

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 250 cP (250 mPa*s)
Non Volatile Content 50 %
Durometer 15 Type A
Appearance Translucent
Cure 24 hours / RTV
Elongation 375 %
Mix Ratio 1 PART
Solvent THF
Specific Gravity 0.99
Tear 15 ppi (2.65 kN/m)
Tensile 75 psi (0.52 MPa)
Comment One Part, Smooth Finish

View more

MED16-6606 Acetoxy 95 cP 30 % 20 Type A Download MED16-6606 data sheet Silicone adhesive dispersed in heptane

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 20 Type A
Elongation 800 %
Non Volatile Content 30 %
Solvent Heptane
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate / Stainless steel
Tear 120 ppi (21.16 kN/m)
Tensile 1,200 psi (8.28 MPa)
Viscosity 95 cP (95 mPa*s)
Comment Silicone adhesive dispersed in heptane

View more

Foams

Product Foam Density Viscosity Cure System Application Life Appearance Data Sheet Comment
MED10-2310 N/A 40,000 cP Platinum 2 minutes White Download MED10-2310 data sheet Low Density

Product Details

Property Average Result
Viscosity 40,000 cP (40,000 mPa*s)
Cure System Platinum
Application Life 2 minutes
Appearance White
Mix Ratio 1:1
Comment Low Density

View more

Low Viscosity Elastomers

Product Viscosity Durometer Work Time Tensile Data Sheet Comment
MED-4011 N/A 27 Type A N/A 670 psi Download MED-4011 data sheet Flowable

Product Details

Property Average Result
Durometer 27 Type A
Viscosity 100,000 cP
Tensile 670 psi (4.62 MPa)
Appearance Translucent
Cure 3 minutes / 150 °C
Cure System Platinum
Elongation 530 %
Mix Ratio 10:1
Post Cure 1 hours / 150 °C
Specific Gravity 1.09
Comment Flowable

View more

MED-4044 73,400 cP 40 Type A 5 hours 875 psi Download MED-4044 data sheet Flowable, Medium Durometer

Product Details

Property Average Result
Durometer 40 Type A
Viscosity 73,400 cP (73,400 mPa*s)
Work Time 5 hours
Tensile 875 psi (6.03 MPa)
Appearance Translucent
Cure 5 minutes / 177 °C
Cure System Platinum
Elongation 360 %
Mix Ratio 10:1
Post Cure 1 minute / 150 °C
Specific Gravity 1.09
Stress at Strain 480 psi / 200 % (3.31 MPa / 200 %)
Tear 150 ppi (26.46 kN/m)
Comment Flowable, Medium Durometer

View more

MED-4086 6,450 cP 55 Type 000 18 hours 40 psi Download MED-4086 data sheet Ultra Soft Elastomer

Product Details

Property Average Result
Durometer 55 Type 000
Viscosity 6,450 cP (6,450 mPa*s)
Work Time 18 hours
Tensile 40 psi (0.28 MPa)
Cure 45 minutes / 150 °C
Cure System Platinum
Elongation 475 %
Mix Ratio 1:1
Stress at Strain 8 psi / 200 % (0.06 MPa / 200 %)
Comment Ultra Soft Elastomer

View more

MED-4917 11,750 cP 20 Type A 31 hours 500 psi Download MED-4917 data sheet Low Viscosity, Long Pot Life

Product Details

Property Average Result
Durometer 20 Type A
Viscosity 11,750 cP (11,750 mPa*s)
Work Time 31 hours
Tensile 500 psi (3.45 MPa)
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Elongation 385 %
Mix Ratio 1:1
Specific Gravity 1.06
Comment Low Viscosity, Long Pot Life

View more

MED-6010 16,000 cP 50 Type A 4 hours 950 psi Download MED-6010 data sheet 1.43 R.I., Optically Clear

Product Details

Property Average Result
Durometer 50 Type A
Viscosity 16,000 cP (16,000 mPa*s)
Work Time 4 hours
Tensile 950 psi (6.55 MPa)
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Elongation 140 %
Mix Ratio 1:1
Refractive Index 1.43
Specific Gravity 1.05
Tear 30 ppi (5.29 kN/m)
Comment 1.43 R.I., Optically Clear

View more

MED-6015 3,800 cP 50 Type A 5.5 hours 1,200 psi Download MED-6015 data sheet 1.41 R.I., Optically Clear, Low Viscosity

Product Details

Property Average Result
Durometer 50 Type A
Viscosity 3,800 cP (3,800 mPa*s)
Work Time 5.5 hours
Tensile 1,200 psi (8.28 MPa)
Appearance Clear
Cure 15 minutes / 150 °C
Cure System Platinum
Elongation 100 %
Mix Ratio 10:1
Specific Gravity 1.03
Comment 1.41 R.I., Optically Clear, Low Viscosity

View more

MED-6019 25,500 cP 75 Type A 2.5 hours 1,300 psi Download MED-6019 data sheet Low Viscosity, High Durometer

Product Details

Property Average Result
Durometer 75 Type A
Viscosity 25,500 cP (25,500 mPa*s)
Work Time 2.5 hours
Tensile 1,300 psi (8.97 MPa)
Appearance Clear
Cure 2 hours / 50 °C
Cure System Platinum
Elongation 65 %
Mix Ratio 1:1
Specific Gravity 1.07
Tear 35 ppi (6.17 kN/m)
Comment Low Viscosity, High Durometer

View more

MED-6020 65,000 cP 40 Type A 4 hours 640 psi Download MED-6020 data sheet 1.43 R.I., Optically Clear

Product Details

Property Average Result
Durometer 40 Type A
Viscosity 65,000 cP (65,000 mPa*s)
Work Time 4 hours
Tensile 640 psi (4.41 MPa)
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Elongation 215 %
Mix Ratio 1:1
Refractive Index 1.43
Tear 40 ppi (7.05 kN/m)
Comment 1.43 R.I., Optically Clear

View more

MED-6033 72,000 cP 50 Type A 50 hours 730 psi Download MED-6033 data sheet 1.41 R.I., Optically Clear, Pourable

Product Details

Property Average Result
Durometer 50 Type A
Viscosity 72,000 cP (72,000 mPa*s)
Work Time 50 hours
Tensile 730 psi (5.03 MPa)
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Elongation 390 %
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.03
Tear 80 ppi (14.11 kN/m)
Comment 1.41 R.I., Optically Clear, Pourable

View more

MED2-4220 19,500 cP 20 Type A 3 minutes 585 psi Download MED2-4220 data sheet Low Viscosity, Rapid RTV Cure

Product Details

Property Average Result
Durometer 20 Type A
Viscosity 19,500 cP (19,500 mPa*s)
Work Time 3 minutes
Tensile 585 psi (4.03 MPa)
Appearance Translucent
Cure 15 minutes / 150 °C
Cure System Platinum
Elongation 500 %
Mix Ratio 1:1
Specific Gravity 1.07
Stress at Strain 100 psi / 200 % (0.69 MPa / 200 %)
Comment Low Viscosity, Rapid RTV Cure

View more

MED3-4220 74,500 cP 25 Type A 15 minutes 1,100 psi Download MED3-4220 data sheet Flowable

Product Details

Property Average Result
Durometer 25 Type A
Viscosity 74,500 cP (74,500 mPa*s)
Work Time 15 minutes
Tensile 1,100 psi (7.59 MPa)
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Elongation 624 %
Mix Ratio 1:1
Specific Gravity 1.11
Tear 74 ppi (13.05 kN/m)
Comment Flowable

View more

MED4-4220 20,500 cP 17 Type A 27 minutes 660 psi Download MED4-4220 data sheet Low Viscosity

Product Details

Property Average Result
Durometer 17 Type A
Viscosity 20,500 cP (20,500 mPa*s)
Work Time 27 minutes
Tensile 660 psi (4.55 MPa)
Appearance Translucent
Cure 15 minutes / 150 °C
Cure System Platinum
Elongation 580 %
Mix Ratio 1:1
Tear 35 ppi (6.17 kN/m)
Comment Low Viscosity

View more