Coatings/Dispersions

Product Cure System Viscosity Non Volatile Content Durometer Data Sheet Comment
MED-2214 Platinum 3,700 cP 35 % 35 Type A Download MED-2214 data sheet One Part, Requires heat to cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,700 cP (3,700 mPa*s)
Non Volatile Content 35 %
Durometer 35 Type A
Appearance Translucent
Cure 60 minutes / 50 °C
Elongation 850 %
Mix Ratio 1 Part
Tear 170 ppi (29.98 kN/m)
Tensile 1,700 psi (11.72 MPa)
Comment One Part, Requires heat to cure

View more

MED-6400 Platinum 860 cP 35 % 30 Type A Download MED-6400 data sheet 1.43 R.I. in Xylene

Product Details

Property Average Result
Cure System Platinum
Viscosity 860 cP (860 mPa*s)
Non Volatile Content 35 %
Durometer 30 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Cure Type Heat Cure
Elongation 850 %
Mix Ratio 1:1
Refractive Index 1.43
Rheology Flowable/Self Leveling
Tear 160 ppi (28.22 kN/m)
Tensile 1,600 psi (11.03 MPa)

View more

MED-6600 Platinum 350 cP 35 % 25 Type A Download MED-6600 data sheet 1.46 R.I. in Xylene

Product Details

Property Average Result
Cure System Platinum
Viscosity 350 cP (350 mPa*s)
Non Volatile Content 35 %
Durometer 25 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 800 %
Mix Ratio 1:1
Refractive Index 1.46
Specific Gravity 1.1
Stress at Strain 300 psi / 300 % (2.07 Mpa / 300 %)
Tear 160 ppi (28.22 kN/m)
Tensile 1,200 psi (8.28 MPa)
Work Time 24 hours
Comment 1.46 R.I. in Xylene

View more

MED-6601 N/A N/A N/A 24 Type A Download MED-6601 data sheet 100% solids

Product Details

Property Average Result
Durometer 24 Type A
Appearance Translucent
Elongation 800 %
Stress at Strain 320 psi / 300 % (2.21 Mpa / 300 %)
Tear 150 ppi (26.46 kN/m)
Tensile 1,200 psi (8.28 MPa)
Comment 100% solids

View more

MED-6605 Acetoxy 700 cP 29 % 25 Type A Download MED-6605 data sheet One Part, in Xylene

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Durometer 25 Type A
Appearance Translucent
Cure 5 days / RTV
Elongation 980 %
Mix Ratio 1 PART
Refractive Index 1.40
Specific Gravity 1.09
Stress at Strain 110 psi / 300 % (0.76 Mpa / 300 %)
Tear 120 ppi (21.16 kN/m)
Tensile 1,500 psi (10.34 MPa)
Comment One Part, in Xylene

View more

MED-6615 Platinum 65 cP 32 % 72 Type 00 Download MED-6615 data sheet Silicone adhesive dispersed in heptane, cures rapidly with heat

Product Details

Property Average Result
Cure Type Heat Cure
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 30 minutes / RTV
Cure System Platinum
Durometer 72 Type 00
Elongation 750 %
Non Volatile Content 32 %
Substrate Primerless: Aluminum / Glass / PMMA / Silicone / With Primer: ABS / PEEK / Polycarbonate / Polyimide / Polysulphone / Polyetherimide / Polyurethane / Stainless steel
Tear 120 ppi (21.16 kN/m)
Tensile 1,060 psi (7.31 MPa)
Viscosity 65 cP (65 mPa*s)
Comment Silicone adhesive dispersed in heptane, cures rapidly with heat

View more

MED-6629 Platinum 400 cP 33 % 35 Type A Download MED-6629 data sheet High Strength Silicone Dispersion

Product Details

Property Average Result
Cure System Platinum
Viscosity 400 cP (400 mPa*s)
Non Volatile Content 33 %
Durometer 35 Type A
Appearance Translucent
Cure 75 minutes / 50 °C 60 minutes / 150 °C
Elongation 900 %
Mix Ratio 1:1
Refractive Index 1.46
Stress at Strain 305 psi / 300 % (2.1 Mpa / 300 %)
Tear 310 ppi (54.67 kN/m)
Tensile 1,800 psi (12.41 MPa)
Comment High Strength Silicone Dispersion

View more

MED-6640 Platinum 3,000 cP 20 % 40 Type A Download MED-6640 data sheet Ultra High Tear, in Xylene

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,000 cP (3,000 mPa*s)
Non Volatile Content 20 %
Durometer 40 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 1,000 %
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.41
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Work Time 24 hours
Comment Ultra High Tear, in Xylene

View more

MED-6655 Acetoxy 700 cP 60 % 35 Type A Download MED-6655 data sheet 100M% Fluorosilicone

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 60 %
Durometer 35 Type A
Appearance White
Cure 3 days / RTV
Cure Type RTV
Elongation 425 %
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Tack Free Time 80 minutes
Tear 45 ppi (7.94 kN/m)
Tensile 775 psi (5.34 MPa)
Comment 100M% Fluorosilicone

View more

MED-6670 Platinum N/A 25 % N/A Download MED-6670 data sheet Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Platinum
Non Volatile Content 25 %
Appearance Translucent
Cure 5 minutes / RTV
Mix Ratio 1:1
Specific Gravity 0.96
Work Time 24 hours
Comment Low Coefficient of Friction Coating

View more

MED-6671 Acetoxy N/A N/A N/A Download MED-6671 data sheet RTV, Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Acetoxy
Appearance Translucent
Cure 24 hours / RTV
Mix Ratio 1 Part
Comment RTV, Low Coefficient of Friction Coating

View more

MED1-4161 Condensation 140 cSt 33 % 25 Type 00 Download MED1-4161 data sheet 25 '00' durometer lubricious coating

Product Details

Property Average Result
Cure System Condensation
Viscosity 140 cSt (121.43 mPa*s)
Non Volatile Content 33 %
Durometer 25 Type 00
Appearance Clear
Cure 5 days / 25 °C
Mix Ratio 1 Part
Solvent Xylene
Specific Gravity 0.87
Comment 25 '00' durometer lubricious coating

View more

MED6-6606 Acetoxy 95 cP 30 % 20 Type A Download MED6-6606 data sheet Silicone adhesive dispersed in heptane

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 3 days / RTV
Cure System Acetoxy
Durometer 20 Type A
Elongation 800 %
Non Volatile Content 30 %
Specific Gravity 1.11
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate / Stainless steel
Tear 115 ppi (20.28 kN/m)
Tensile 1,190 psi (8.21 MPa)
Viscosity 95 cP (95 mPa*s)
Comment Silicone adhesive dispersed in heptane

View more