Refine results

Active filters Clear criteria
Thermally Conductive Electrically Conductive/Static Dissipative

Apply

  • Show more

Add filters

Electrically Conductive/Static Dissipative

Refine results
Product Volume Resistivity Viscosity Cure System Durometer Tensile Data Sheet Comment
CV-1500 3 ohmcm N/A Oxime 80 Type A 650 psi Download CV-1500 data sheet Carbon filled, 3 ohmcm, versatile adhesive. Tack Free in 10 minutes.

Product Details

Property Average Result
Volume Resistivity 3 ohmcm
Cure System Oxime
Durometer 80 Type A
Tensile 650 psi (4.48 MPa)
Appearance Black
Cure 7 days / RTV
Elongation 20 %
Flow Rate 0 in
Lap Shear 325 psi (2.24 MPa)
Specific Gravity 1.25
Tack Free Time 10 minutes
Comment Carbon filled, 3 ohmcm, versatile adhesive. Tack Free in 10 minutes.

View more

CV-2640 2.5 ohmcm N/A Platinum 75 Type A 475 psi Download CV-2640 data sheet 2.5 ohmcm, *4) Primed Lap Shear 250 psi (1.7 MPa), Carbon Fiber Filled

Product Details

Property Average Result
Volume Resistivity 2.5 ohmcm
Cure System Platinum
Durometer 75 Type A
Tensile 475 psi (3.28 MPa)
Appearance Black
Cure 30 minutes / 150 °C
Elongation 90 %
Lap Shear 250 psi (1.72 MPa)
Mix Ratio 10:1
Specific Gravity 1.19
Work Time 2 hours
Comment 2.5 ohmcm, *4) Primed Lap Shear 250 psi (1.7 MPa), Carbon Fiber Filled

View more

CV-2644 0.01 ohmcm 224,500 cP Platinum 85 Type A 525 psi Download CV-2644 data sheet 0.005 ohmcm, *22) 1.2 W/mK

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Viscosity 224,500 cP (224,500 mPa*s)
Cure System Platinum
Durometer 85 Type A
Tensile 525 psi (3.62 MPa)
Appearance Tan
Cure 30 minutes / 150 °C
Elongation 86 %
Mix Ratio 20:1
Specific Gravity 3.39
Thermal Conductivity 1.2 W/(mK)
Work Time 2.75 hours
Comment 0.005 ohmcm, *22) 1.2 W/mK

View more

CV-2646 0.01 ohmcm N/A Alkoxy 80 Type A 400 psi Download CV-2646 data sheet Electrically Conductive, 0.007 ohmcm

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Cure System Alkoxy
Durometer 80 Type A
Tensile 400 psi (2.76 MPa)
Appearance Tan
Cure 10 days / RTV
Elongation 90 %
Lap Shear 325 psi (2.24 MPa)
Mix Ratio 100:0.5
Specific Gravity 3.86
Tear 60 ppi (10.58 kN/m)
Thermal Conductivity 1 W/(mK)
Work Time 3.5 hours
Comment Electrically Conductive, 0.007 ohmcm

View more

CV1-2640 25 ohmcm N/A Platinum 40 Type A 525 psi Download CV1-2640 data sheet Carbon filled.

Product Details

Property Average Result
Volume Resistivity 25 ohmcm
Cure System Platinum
Durometer 40 Type A
Tensile 525 psi (3.62 MPa)
Appearance Black
Cure 2 hours / 65 °C
Elongation 225 %
Extrusion Rate 300 g/minute
Mix Ratio 10:1
Specific Gravity 1.07
Comment Carbon filled.

View more

CV1-2646 0.01 ohmcm N/A Alkoxy 80 Type A 400 psi Download CV1-2646 data sheet 0.005 ohmcm

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Cure System Alkoxy
Durometer 80 Type A
Tensile 400 psi (2.76 MPa)
Appearance Tan
Cure 10 days / RTV
Elongation 90 %
Lap Shear 325 psi (2.24 MPa)
Mix Ratio 100:0.5
Specific Gravity 3.86
Tear 60 ppi (10.58 kN/m)
Thermal Conductivity 1 W/(mK)
Work Time 3.5 hours
Comment 0.005 ohmcm

View more

CV2-1148 9,000,000,000 ohmcm N/A Oxime 45 Type A N/A Download CV2-1148 data sheet 100% Solids

Product Details

Property Average Result
Volume Resistivity 9,000,000,000 ohmcm
Cure System Oxime
Durometer 45 Type A
Appearance Black
Cure 7 days / RTV
Mix Ratio 1 PART
Specific Gravity 1.07
Comment 100% Solids

View more

CV2-2640 1 ohmcm 675,000 cP Platinum 30 Type A 500 psi Download CV2-2640 data sheet Carbon Black Filled

Product Details

Property Average Result
Volume Resistivity 1 ohmcm
Viscosity 675,000 cP (675,000 mPa*s)
Cure System Platinum
Durometer 30 Type A
Tensile 500 psi (3.45 MPa)
Appearance Black
Cure 24 hours / RTV
Elongation 350 %
Mix Ratio 1:1
Specific Gravity 1.06
Tear 30 ppi (5.29 kN/m)
Thermal Conductivity 0.22 W/(mK)
Work Time 1 hours
Comment Carbon Black Filled

View more

CV2-2644 0 ohmcm N/A Platinum 85 Type A 500 psi Download CV2-2644 data sheet 0.004 ohmcm

Product Details

Property Average Result
Volume Resistivity 0 ohmcm
Cure System Platinum
Durometer 85 Type A
Tensile 500 psi (3.45 MPa)
Appearance Tan
Cure 30 minutes / 150 °C
Elongation 100 %
Mix Ratio 20:1
Specific Gravity 3.04
Work Time 2.5 hours
Comment 0.004 ohmcm

View more

CV3-2640 2,200,000 ohmcm 14,100 cP Platinum 25 Type A 70 psi Download CV3-2640 data sheet Carbon filled. Designed for broad operating temperature.

Product Details

Property Average Result
Volume Resistivity 2,200,000 ohmcm
Viscosity 14,100 cP (14,100 mPa*s)
Cure System Platinum
Durometer 25 Type A
Tensile 70 psi (0.48 MPa)
Appearance Black
Cure 7 days / RTV
Elongation 120 %
Lap Shear 50 psi (0.34 MPa)
Mix Ratio 1:1
Specific Gravity 1.01
Tack Free Time 10 hours
Comment Carbon filled. Designed for broad operating temperature.

View more

SCV-2596 2.5 ohmcm N/A Platinum 75 Type A 475 psi Download SCV-2596 data sheet Electrically Conductive, 2.5 ohmcm, Carbon Fiber Filled

Product Details

Property Average Result
Volume Resistivity 2.5 ohmcm
Cure System Platinum
Durometer 75 Type A
Tensile 475 psi (3.28 MPa)
Appearance Black
Cure 30 minutes / 150 °C
Elongation 90 %
Lap Shear 250 psi (1.72 MPa)
Lap Shear 250 psi (1.72 MPa)
Mix Ratio 10:1
Specific Gravity 1.19
Work Time 2 hours

View more

SCV1-2596 0.01 ohmcm N/A Platinum 85 Type A 450 psi Download SCV1-2596 data sheet Electricaly Conductive, 0.005 ohmcm ,*21, 22) 1.2 W /mK

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Cure System Platinum
Durometer 85 Type A
Tensile 450 psi (3.1 MPa)
Appearance Tan
Cure 30 minutes / 150 °C
Mix Ratio 20:1
Specific Gravity 3.42
Thermal Conductivity 1.2 W/(mK)
Work Time 2.5 hours
Comment Electricaly Conductive, 0.005 ohmcm ,*21, 22) 1.2 W /mK

View more

Thermally Conductive

Product Thermal Conductivity Mix Ratio Viscosity Extrusion Rate Cure System Data Sheet Comment
CV-2900 0.61 W/(mK) 1 PART N/A 40 g/minute Oxime Download CV-2900 data sheet *22) 0.6 W/mK, Low Temperature

Product Details

Property Average Result
Thermal Conductivity 0.61 W/(mK)
Extrusion Rate 40 g/minute
Cure System Oxime
Tensile 400 psi (2.76 MPa)
Appearance White
Cure 72 hours / RTV
Durometer 65 Type A
Elongation 150 %
Ionic Content Cl <5 ppm
Ionic Content K <5 ppm
Ionic Content Na <5 ppm
Mix Ratio 1 PART
Specific Gravity 2.33
Tack Free Time 40 minutes
Comment *22) 0.6 W/mK, Low Temperature

View more

CV-2942 1 W/(mK) 20:1 N/A N/A Platinum Download CV-2942 data sheet *22) 1.0 W/mK, *4) Primed Lap Shear 375 psi (2.6 MPa)

Product Details

Property Average Result
Thermal Conductivity 1 W/(mK)
Cure System Platinum
Tensile 650 psi (4.48 MPa)
Appearance Gray
Cure 24 hours / RTV
Dielectric Strength 430 volts/mil (16.77 kV/mm)
Durometer 85 Type A
Elongation 15 %
Lap Shear 375 psi (2.59 MPa)
Mix Ratio 20:1
Specific Gravity 2.4
Tack Free Time 4 hours
Tear 55 ppi (9.7 kN/m)
Volume Resistivity 140,000,000,000,000 ohmcm
Work Time 2.5 hours
Comment *22) 1.0 W/mK, *4) Primed Lap Shear 375 psi (2.6 MPa)

View more

CV-2943 1.22 W/(mK) 100:0.2 N/A N/A Alkoxy Download CV-2943 data sheet *22) 1.2 W/mK, *3) Primed Lap Shear 475 psi (3.3 MPa)

Product Details

Property Average Result
Thermal Conductivity 1.22 W/(mK)
Cure System Alkoxy
Tensile 750 psi (5.17 MPa)
Appearance Gray
Cure 7 days / RTV
Durometer 90 Type A
Elongation 35 %
Lap Shear 475 psi (3.28 MPa)
Mix Ratio 100:0.2
Specific Gravity 2.55
Tear 90 ppi (15.87 kN/m)
Work Time 2 hours
Comment *22) 1.2 W/mK, *3) Primed Lap Shear 475 psi (3.3 MPa)

View more

CV-2946 1.49 W/(mK) 15:1 3,560,000 cP N/A Platinum Download CV-2946 data sheet *22) 1.5 W/mK *,4 ) Primed Lap Shear 160 psi (1.1 MPa)

Product Details

Property Average Result
Thermal Conductivity 1.49 W/(mK)
Viscosity 3,560,000 cP (3,560,000 mPa*s)
Cure System Platinum
Tensile 200 psi (1.38 MPa)
Appearance White
Cure 7 days / RTV
Dielectric Strength 540 volts/mil (21.06 kV/mm)
Durometer 75 Type A
Elongation 30 %
Lap Shear 160 psi (1.1 MPa)
Mix Ratio 15:1
Specific Gravity 1.53
Tack Free Time 4.5 hours
Tear 50 ppi (8.82 kN/m)
Volume Resistivity 530,000,000,000,000 ohmcm
Work Time 2 hours
Comment *22) 1.5 W/mK *,4 ) Primed Lap Shear 160 psi (1.1 MPa)

View more

CV-2948 1.95 W/(mK) 100:0.2 N/A N/A Alkoxy Download CV-2948 data sheet *22) 2.0 W/mK, *3) Primed Lap Shear 150 psi (1.0 MPa)

Product Details

Property Average Result
Thermal Conductivity 1.95 W/(mK)
Cure System Alkoxy
Tensile 250 psi (1.72 MPa)
Appearance White
Cure 7 days / RTV
Durometer 80 Type A
Elongation 30 %
Lap Shear 150 psi (1.03 MPa)
Mix Ratio 100:0.2
Specific Gravity 1.57
Tear 45 ppi (7.94 kN/m)
Work Time 2.5 hours
Comment *22) 2.0 W/mK, *3) Primed Lap Shear 150 psi (1.0 MPa)

View more

CV-2960 0.83 W/(mK) 10:1 130,000 cP N/A Platinum Download CV-2960 data sheet *22) 0.8 W/mK, *4) Primed Lap Shear 205 psi (1.4 MPa), Low Viscosity

Product Details

Property Average Result
Thermal Conductivity 0.83 W/(mK)
Viscosity 130,000 cP (130,000 mPa*s)
Cure System Platinum
Tensile 200 psi (1.38 MPa)
Appearance White
Cure 7 days / RTV
Durometer 60 Type A
Elongation 110 %
Lap Shear 205 psi (1.41 MPa)
Mix Ratio 10:1
Specific Gravity 1.34
Tack Free Time 3 hours
Tear 45 ppi (7.94 kN/m)
Work Time 1.5 hours
Comment *22) 0.8 W/mK, *4) Primed Lap Shear 205 psi (1.4 MPa), Low Viscosity

View more

CV-2961 0.79 W/(mK) 10:1 300,000 cP N/A Platinum Download CV-2961 data sheet *22) 0.8 W/mK Low Viscosity, *3) Primed Lap Shear 205 psi (1.4 MPa), Low Temp

Product Details

Property Average Result
Thermal Conductivity 0.79 W/(mK)
Viscosity 300,000 cP (300,000 mPa*s)
Cure System Platinum
Tensile 275 psi (1.9 MPa)
Appearance White
Cure 30 minutes / 150 °C
Durometer 75 Type A
Elongation 40 %
Lap Shear 205 psi (1.41 MPa)
Mix Ratio 10:1
Specific Gravity 1.38
Tack Free Time 3.5 hours
Tear 45 ppi (7.94 kN/m)
Work Time 2 hours
Comment *22) 0.8 W/mK Low Viscosity, *3) Primed Lap Shear 205 psi (1.4 MPa), Low Temp

View more

CV-2963 0.64 W/(mK) 20:1 N/A N/A Platinum Download CV-2963 data sheet Primed w/CF1-135, Contains Boron Nitride

Product Details

Property Average Result
Thermal Conductivity 0.64 W/(mK)
Cure System Platinum
Tensile 425 psi (2.93 MPa)
Appearance White
Cure 4 hours / 65 °C
Durometer 60 Type A
Elongation 250 %
Lap Shear 275 psi (1.9 MPa)
Mix Ratio 20:1
Specific Gravity 1.27
Tear 50 ppi (8.82 kN/m)
Work Time 2 hours
Comment Primed w/CF1-135, Contains Boron Nitride

View more

CV1-2960 1.11 W/(mK) 10:1 900,000 cP N/A Platinum Download CV1-2960 data sheet *22) 1.1 W/mK

Product Details

Property Average Result
Thermal Conductivity 1.11 W/(mK)
Viscosity 900,000 cP (900,000 mPa*s)
Cure System Platinum
Tensile 250 psi (1.72 MPa)
Appearance White
Cure 4 hours / 65 °C
Durometer 75 Type A
Elongation 60 %
Mix Ratio 10:1
Specific Gravity 1.45
Tack Free Time 4 hours
Tear 55 ppi (9.7 kN/m)
Work Time 2 hours
Comment *22) 1.1 W/mK

View more

CV1-2964 0.95 W/(mK) 1:1 50,000 cP N/A Platinum Download CV1-2964 data sheet *22) 1.0 W /mK, *5) Primed Lap Shear 120 psi (0.8 MPa)

Product Details

Property Average Result
Thermal Conductivity 0.95 W/(mK)
Viscosity 50,000 cP (50,000 mPa*s)
Cure System Platinum
Tensile 180 psi (1.24 MPa)
Appearance White
Cure 15 minutes / 150 °C
Durometer 65 Type A
Elongation 50 %
Lap Shear 120 psi (0.83 MPa)
Mix Ratio 1:1
Specific Gravity 2.34
Tack Free Time 13 hours
Comment *22) 1.0 W /mK, *5) Primed Lap Shear 120 psi (0.8 MPa)

View more

CV2-2946 0.64 W/(mK) 20:1 N/A 140 g/minute Platinum Download CV2-2946 data sheet *22) 0.6 W/mK, Thin Bond Line

Product Details

Property Average Result
Thermal Conductivity 0.64 W/(mK)
Extrusion Rate 140 g/minute
Cure System Platinum
Tensile 400 psi (2.76 MPa)
Appearance White
Cure 30 minutes / 150 °C
Durometer 55 Type A
Elongation 225 %
Mix Ratio 20:1
Tear 55 ppi (9.7 kN/m)
Work Time 3 hours
Comment *22) 0.6 W/mK, Thin Bond Line

View more

CV4-2946 0.95 W/(mK) N/A N/A 122 g/minute Platinum Download CV4-2946 data sheet Gel, soft and compliant

Product Details

Property Average Result
Thermal Conductivity 0.95 W/(mK)
Extrusion Rate 122 g/minute
Cure System Platinum
Appearance White
Cure 72 hours / 25 °C
Durometer 36 Type 00
Lap Shear 27 psi (0.19 MPa)
Specific Gravity 1.3
Tack Free Time 16.5 hours
Volatile Content 0.01 %
Work Time 5.5 hours
Comment Gel, soft and compliant

View more

SCV1-2599 1.6 W/(mK) 15:1 3,750,000 cP N/A Platinum Download SCV1-2599 data sheet Primed w/CF1-135, Contains Boron Nitride

Product Details

Property Average Result
Thermal Conductivity 1.6 W/(mK)
Viscosity 3,750,000 cP (3,750,000 mPa*s)
Cure System Platinum
Tensile 200 psi (1.38 MPa)
Appearance White
Cure 7 days / RTV
Dielectric Strength 540 volts/mil (21.06 kV/mm)
Durometer 75 Type A
Elongation 30 %
Lap Shear 150 psi (1.03 MPa)
Mix Ratio 15:1
Specific Gravity 1.53
Tear 50 ppi (8.82 kN/m)
Volume Resistivity 530,000,000,000,000 ohmcm
Work Time 2 hours
Comment Primed w/CF1-135, Contains Boron Nitride

View more

SCV2-2599 0.64 W/(mK) 20:1 N/A 140 g/minute Platinum Download SCV2-2599 data sheet 0.64 W /mK (Tested per ASTM E1530)

Product Details

Property Average Result
Thermal Conductivity 0.64 W/(mK)
Extrusion Rate 140 g/minute
Cure System Platinum
Tensile 400 psi (2.76 MPa)
Appearance White
Cure 30 minutes / 150 °C
Durometer 55 Type A
Elongation 225 %
Mix Ratio 20:1
Tear 55 ppi (9.7 kN/m)
Work Time 3 hours
Comment 0.64 W /mK (Tested per ASTM E1530)

View more