Coatings/Dispersions

Product Cure System Viscosity Non Volatile Content Durometer Data Sheet Comment
CV-1144-0 Oxime 240 cP 60 % N/A Download CV-1144-0 data sheet 60% Solids, Atomic Oxygen Protective Overcoat

Product Details

Property Average Result
Viscosity 240 cP (240 mPa*s)
Non Volatile Content 60 %
Appearance Clear
Tack Free Time 50 minutes
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Refractive Index 1.43
Specific Gravity 1
Comment 60% Solids, Atomic Oxygen Protective Overcoat

View more

CV-1146-2 Oxime 2,400 cP 72 % N/A Download CV-1146-2 data sheet 72% Solids

Product Details

Property Average Result
Viscosity 2,400 cP (2,400 mPa*s)
Non Volatile Content 72 %
Appearance Black
Cure 7 days / RTV
Cure System Oxime
Dielectric Strength 845 volts/mil (32.96 kV/mm)
Mix Ratio 1 PART
Specific Gravity 1.26
Comment 72% Solids

View more

CV-1152 Oxime 7,300 cP N/A N/A Download CV-1152 data sheet Soft, very low modulus coating

Product Details

Property Average Result
Viscosity 7,300 cP (7,300 mPa*s)
Appearance Translucent
Tack Free Time 50 minutes
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Refractive Index 1.43
Specific Gravity 1.01
Comment Soft, very low modulus coating

View more

CV1-1144-0 Oxime 850 cP 50 % N/A Download CV1-1144-0 data sheet 50% Solids

Product Details

Property Average Result
Viscosity 850 cP (850 mPa*s)
Non Volatile Content 50 %
Appearance Translucent
Tack Free Time 10 minutes
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Specific Gravity 1.11
Comment 50% Solids

View more

CV1-1146-2 Oxime 1,125 cP N/A N/A Download CV1-1146-2 data sheet N/A

Product Details

Property Average Result
Viscosity 1,125 cP (1,125 mPa*s)
Appearance Black
Tack Free Time 2 hours
Cure System Oxime

View more

CV1-1148 Oxime 5,000 cP 40 % N/A Download CV1-1148 data sheet 40% Solids

Product Details

Property Average Result
Viscosity 5,000 cP (5,000 mPa*s)
Non Volatile Content 40 %
Appearance Black
Tack Free Time 40 minutes
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Specific Gravity 1.07
Comment 40% Solids

View more

CV2-1147 Oxime 2,000 cP 60 % N/A Download CV2-1147 data sheet 60% Solids, Non-blocking Overcoat

Product Details

Property Average Result
Viscosity 2,000 cP (2,000 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Tack Free Time 2 hours
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Specific Gravity 1.12
Comment 60% Solids, Non-blocking Overcoat

View more

CV3-1144-1 Oxime 900 cP 60 % N/A Download CV3-1144-1 data sheet 60% Solids

Product Details

Property Average Result
Viscosity 900 cP (900 mPa*s)
Non Volatile Content 60 %
Appearance White
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Comment 60% Solids

View more

Foams

Product Foam Density Viscosity Cure System Application Life Appearance Data Sheet Comment
CV-2391 20 lbs/ft3 3,000 cP Platinum 6 minutes White Download CV-2391 data sheet Cure in place versatile low outgassing foam, application life 6 minutes

Product Details

Property Average Result
Viscosity 3,000 cP (3,000 mPa*s)
Cure System Platinum
Foam Density 20 lbs/ft3 (0.32 g/cm3)
Application Life 6 minutes
Appearance White
Cure 60 minutes / RTV
Mix Ratio 1:10
Comment Cure in place versatile low outgassing foam, application life 6 minutes

View more

Gels

Product Viscosity Penetration Work Time Mix Ratio Data Sheet Comment
CV-8151 2,500 cP 4 mm 30 hours 1:1 Download CV-8151 data sheet Low Viscosity, Penetration 4.0 mm

Product Details

Property Average Result
Viscosity 2,500 cP (2,500 mPa*s)
Penetration 4 mm
Work Time 30 hours
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Comment Low Viscosity, Penetration 4.0 mm

View more

CV-8251 1,800 cP 3 mm 24 hours 1:1 Download CV-8251 data sheet Low/High Temperature, Penetration 3 mm

Product Details

Property Average Result
Viscosity 1,800 cP (1,800 mPa*s)
Penetration 3 mm
Work Time 24 hours
Appearance Clear
Cure 40 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Comment Low/High Temperature, Penetration 3 mm

View more

CV1-8151 19,800 cP 0.4 mm N/A 1:1 Download CV1-8151 data sheet Penetration 0.4 mm

Product Details

Property Average Result
Viscosity 19,800 cP (19,800 mPa*s)
Penetration 0.4 mm
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Volume Resistivity 570,000,000,000,000 ohmcm
Comment Penetration 0.4 mm

View more