Electrically Conductive/Static Dissipative

Product Volume Resistivity Viscosity Cure System Durometer Tensile Data Sheet Comment
CV-1500 3 ohmcm N/A Oxime 80 Type A 650 psi Download CV-1500 data sheet Carbon filled, 3 ohmcm, versatile adhesive. Tack Free in 10 minutes.

Product Details

Property Average Result
Volume Resistivity 3 ohmcm
Cure System Oxime
Durometer 80 Type A
Tensile 650 psi (4.48 MPa)
Appearance Black
Cure 7 days / RTV
Elongation 20 %
Flow Rate 0 in
Lap Shear 325 psi (2.24 MPa)
Specific Gravity 1.25
Tack Free Time 10 minutes
Comment Carbon filled, 3 ohmcm, versatile adhesive. Tack Free in 10 minutes.

View more

CV1-2640 25 ohmcm N/A Platinum 40 Type A 525 psi Download CV1-2640 data sheet Carbon filled.

Product Details

Property Average Result
Volume Resistivity 25 ohmcm
Cure System Platinum
Durometer 40 Type A
Tensile 525 psi (3.62 MPa)
Appearance Black
Cure 2 hours / 65 °C
Elongation 225 %
Extrusion Rate 300 g/minute
Mix Ratio 10:1
Specific Gravity 1.07
Comment Carbon filled.

View more

CV3-2640 2,200,000 ohmcm 14,100 cP Platinum 25 Type A 70 psi Download CV3-2640 data sheet Carbon filled. Designed for broad operating temperature.

Product Details

Property Average Result
Volume Resistivity 2,200,000 ohmcm
Viscosity 14,100 cP (14,100 mPa*s)
Cure System Platinum
Durometer 25 Type A
Tensile 70 psi (0.48 MPa)
Appearance Black
Cure 7 days / RTV
Elongation 120 %
Lap Shear 50 psi (0.34 MPa)
Mix Ratio 1:1
Specific Gravity 1.01
Tack Free Time 10 hours
Comment Carbon filled. Designed for broad operating temperature.

View more

R-2631 70 ohmcm N/A Platinum 45 Type A 615 psi Download R-2631 data sheet Carbon filled.

Product Details

Property Average Result
Volume Resistivity 70 ohmcm
Cure System Platinum
Durometer 45 Type A
Tensile 615 psi (4.24 MPa)
Appearance Black
Cure 30 minutes / 150 °C
Elongation 275 %
Extrusion Rate 100 g/minute
Mix Ratio 1:1
Specific Gravity 1.08
Tear 55 ppi (9.7 kN/m)
Comment Carbon filled.

View more

R-2637 0.01 ohmcm N/A Platinum 60 Type A 210 psi Download R-2637 data sheet Electrically Conductive RTV Silicone. Mixes to smooth paste, can be screen printed.

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Cure System Platinum
Durometer 60 Type A
Tensile 210 psi (1.45 MPa)
Appearance Tan
Cure 30 minutes / 150 °C
Dielectric Strength 5 volts/mil (0.2 kV/mm)
Elongation 275 %
Mix Ratio 20:1
Specific Gravity 3.6
Tack Free Time 5 hours
Thermal Conductivity 1.5 W/(mK)
Work Time 4 hours
Comment Electrically Conductive RTV Silicone. Mixes to smooth paste, can be screen printed.

View more

Thermally Conductive

Product Thermal Conductivity Mix Ratio Viscosity Extrusion Rate Cure System Data Sheet Comment
CF1-3800 1.25 W/(mK) 15:1 N/A N/A Platinum Download CF1-3800 data sheet 50% M Fluoro. Recommended for short term exposure to solvents and fuel. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 1.25 W/(mK)
Cure System Platinum
Tensile 125 psi (0.86 MPa)
Appearance White
Cure 30 minutes / 150 °C
Durometer 50 Type A
Elongation 50 %
Mix Ratio 15:1
Specific Gravity 1.53
Work Time 90 minutes
Comment 50% M Fluoro. Recommended for short term exposure to solvents and fuel. (Contains Boron Nitride)

View more

CV-2963 0.64 W/(mK) 20:1 N/A N/A Platinum Download CV-2963 data sheet Primed w/CF1-135, Contains Boron Nitride

Product Details

Property Average Result
Thermal Conductivity 0.64 W/(mK)
Cure System Platinum
Tensile 425 psi (2.93 MPa)
Appearance White
Cure 4 hours / 65 °C
Durometer 60 Type A
Elongation 250 %
Lap Shear 275 psi (1.9 MPa)
Mix Ratio 20:1
Specific Gravity 1.27
Tear 50 ppi (8.82 kN/m)
Work Time 2 hours
Comment Primed w/CF1-135, Contains Boron Nitride

View more

EPM-2401 0.7 W/(mK) N/A N/A N/A Non-Curing Download EPM-2401 data sheet Versatile, low volatility, thermally conductive grease where thin bondlines or a compressible grease is needed. Non-curing.

Product Details

Property Average Result
Thermal Conductivity 0.7 W/(mK)
Cure System Non-Curing
Appearance White
Ionic Content Cl <5 ppm
Ionic Content K <2 ppm
Ionic Content Na <4 ppm
Specific Gravity 2.3
Comment Versatile, low volatility, thermally conductive grease where thin bondlines or a compressible grease is needed. Non-curing.

View more

EPM-2490 1.49 W/(mK) 15:1 3,672,800 cP N/A Platinum Download EPM-2490 data sheet 1.5 W/mK, 160 psi lap shear primed w/CF1-135, 2 hr. pot life. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 1.49 W/(mK)
Viscosity 3,672,800 cP (3,672,800 mPa*s)
Cure System Platinum
Tensile 200 psi (1.38 MPa)
Appearance White
Durometer 75 Type A
Elongation 30 %
Flow Rate 0.3 in (7.62 mm)
Ionic Content Cl <3 ppm
Ionic Content K <3 ppm
Ionic Content Na <6 ppm
Lap Shear 160 psi (1.1 MPa)
Mix Ratio 15:1
Specific Gravity 1.53
Tack Free Time 4.5 hours
Tear 50 ppi (8.82 kN/m)
Work Time 2 hours
Comment 1.5 W/mK, 160 psi lap shear primed w/CF1-135, 2 hr. pot life. (Contains Boron Nitride)

View more

EPM-2495 0.64 W/(mK) 20:1 N/A 140 g/minute Platinum Download EPM-2495 data sheet Recommended for bondlines 50 micron or greater. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 0.64 W/(mK)
Extrusion Rate 140 g/minute
Cure System Platinum
Tensile 400 psi (2.76 MPa)
Appearance White
Cure 30 minutes / 150 °C
Durometer 55 Type A
Elongation 225 %
Ionic Content Cl <6 ppm
Ionic Content K <3 ppm
Ionic Content Na <3 ppm
Mix Ratio 20:1
Tear 55 ppi (9.7 kN/m)
Work Time 3 hours
Comment Recommended for bondlines 50 micron or greater. (Contains Boron Nitride)

View more

EPM-2496 0.5 W/(mK) N/A 4,500 cP N/A N/A Download EPM-2496 data sheet N/A

Product Details

Property Average Result
Thermal Conductivity 0.5 W/(mK)
Viscosity 4,500 cP (4,500 mPa*s)
Tensile 700 psi (4.83 MPa)
Appearance Gray
Cure 10 minutes / 150 °C
Durometer 65 Type A
Elongation 115 %
Specific Gravity 1.5
Volatile Content 0.5 %
Work Time 25 minutes

View more

EPM-2890 0.61 W/(mK) 1 PART N/A 40 g/minute Oxime Download EPM-2890 data sheet Excellent for bonding in thin layers and does not contain Boron Nitride.

Product Details

Property Average Result
Thermal Conductivity 0.61 W/(mK)
Extrusion Rate 40 g/minute
Cure System Oxime
Tensile 400 psi (2.76 MPa)
Appearance White
Cure 72 hours / RTV
Durometer 65 Type A
Elongation 150 %
Ionic Content Cl <5 ppm
Ionic Content K <5 ppm
Ionic Content Na <5 ppm
Lap Shear 225 psi (1.55 MPa)
Mix Ratio 1 PART
Specific Gravity 2.33
Tack Free Time 40 minutes
Tear 55 ppi (9.7 kN/m)
Comment Excellent for bonding in thin layers and does not contain Boron Nitride.

View more

EPM1-2493 0.95 W/(mK) 1:1 36,000 cP N/A Platinum Download EPM1-2493 data sheet Recommended for bondlines 5 micron or greater.

Product Details

Property Average Result
Thermal Conductivity 0.95 W/(mK)
Viscosity 36,000 cP (36,000 mPa*s)
Cure System Platinum
Tensile 180 psi (1.24 MPa)
Appearance White
Cure 14 minutes / 150 °C
Dielectric Strength 465 volts/mil (18.14 kV/mm)
Durometer 65 Type A
Elongation 50 %
Ionic Content Cl <5 ppm
Ionic Content K <3 ppm
Ionic Content Na <5 ppm
Lap Shear 120 psi (0.83 MPa)
Mix Ratio 1:1
Specific Gravity 2.34
Tack Free Time 13 hours
Volatile Content 0.35 %
Volume Resistivity 34,000,000,000,000 ohmcm
Comment Recommended for bondlines 5 micron or greater.

View more

G-9340 0.68 W/(mK) N/A N/A N/A Non-Curing Download G-9340 data sheet Versatile, thermally conductive grease where thin bondlines or a compressible grease is needed. Non-curing.

Product Details

Property Average Result
Thermal Conductivity 0.68 W/(mK)
Cure System Non-Curing
Appearance White
Flow Rate 0.2 in (5.08 mm)
Specific Gravity 2.26
Comment Versatile, thermally conductive grease where thin bondlines or a compressible grease is needed. Non-curing.

View more

R-2165 0.5 W/(mK) 1:1 4,000 cP N/A Platinum Download R-2165 data sheet 0.6 W/mK, versatile, moderate thermally conductive silicone. Will RTV.

Product Details

Property Average Result
Thermal Conductivity 0.5 W/(mK)
Viscosity 4,000 cP (4,000 mPa*s)
Cure System Platinum
Tensile 500 psi (3.45 MPa)
Appearance Gray
Cure 10 minutes / 150 °C
Dielectric Strength 700 volts/mil (27.3 kV/mm)
Durometer 60 Type A
Elongation 100 %
Mix Ratio 1:1
Volume Resistivity 1,000,000,000,000,000 ohmcm
Work Time 10 minutes
Comment 0.6 W/mK, versatile, moderate thermally conductive silicone. Will RTV.

View more

R-2175 0.4 W/(mK) 1:1 2,000 cP N/A Platinum Download R-2175 data sheet 0.4 W/mk, pourable, heat resistant, tested per UL94 and passed V0. Will RTV.

Product Details

Property Average Result
Thermal Conductivity 0.4 W/(mK)
Viscosity 2,000 cP (2,000 mPa*s)
Cure System Platinum
Tensile 525 psi (3.62 MPa)
Appearance Black
Cure 60 minutes / 150 °C
Dielectric Strength 580 volts/mil (22.62 kV/mm)
Durometer 50 Type A
Elongation 130 %
Mix Ratio 1:1
Volume Resistivity 43,000,000,000,000 ohmcm
Work Time 1 hours
Comment 0.4 W/mk, pourable, heat resistant, tested per UL94 and passed V0. Will RTV.

View more

R-2930 1.46 W/(mK) 15:1 N/A N/A Platinum Download R-2930 data sheet Smooth Paste;1.45 W/mK, 3 hr. pot life. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 1.46 W/(mK)
Cure System Platinum
Tensile 260 psi (1.79 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 880 volts/mil (34.32 kV/mm)
Durometer 80 Type A
Elongation 20 %
Flow Rate 0.3 inches (7.62 mm)
Mix Ratio 15:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.55
Work Time 3 hours
Comment Smooth Paste;1.45 W/mK, 3 hr. pot life. (Contains Boron Nitride)

View more

R-2939 0.75 W/(mK) 15:1 70,000 cP N/A Platinum Download R-2939 data sheet 0.75 W/mK, 4 hr. pot life. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 0.75 W/(mK)
Viscosity 70,000 cP (70,000 mPa*s)
Cure System Platinum
Tensile 300 psi (2.07 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 810 volts/mil (31.59 kV/mm)
Durometer 70 Type A
Elongation 70 %
Mix Ratio 15:1
Specific Gravity 1.34
Tear 45 ppi (7.94 kN/m)
Work Time 4 hours
Comment 0.75 W/mK, 4 hr. pot life. (Contains Boron Nitride)

View more

R-2940 0.84 W/(mK) 20:1 N/A N/A Platinum Download R-2940 data sheet Smooth Paste;0.8 W/mK, 5 hr. pot life.

Product Details

Property Average Result
Thermal Conductivity 0.84 W/(mK)
Cure System Platinum
Tensile 700 psi (4.83 MPa)
Appearance Gray
Cure 30 minutes / 150 °C
Dielectric Strength 450 volts/mil (17.55 kV/mm)
Durometer 90 Type A
Elongation 35 %
Mix Ratio 20:1
Specific Gravity 2.41
Tack Free Time 24 hours
Tear 65 ppi (11.46 kN/m)
Work Time 5 hours
Comment Smooth Paste;0.8 W/mK, 5 hr. pot life.

View more

R-2949 0.75 W/(mK) 15:1 75,000 cP N/A Platinum Download R-2949 data sheet For applications requiring a broader operating temperature range. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 0.75 W/(mK)
Viscosity 75,000 cP (75,000 mPa*s)
Cure System Platinum
Tensile 275 psi (1.9 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 920 volts/mil (35.88 kV/mm)
Durometer 75 Type A
Elongation 50 %
Mix Ratio 15:1
Specific Gravity 1.37
Tear 45 ppi (7.94 kN/m)
Work Time 3.5 hours
Comment For applications requiring a broader operating temperature range. (Contains Boron Nitride)

View more

SCV1-2599 1.6 W/(mK) 15:1 3,750,000 cP N/A Platinum Download SCV1-2599 data sheet Primed w/CF1-135, Contains Boron Nitride

Product Details

Property Average Result
Thermal Conductivity 1.6 W/(mK)
Viscosity 3,750,000 cP (3,750,000 mPa*s)
Cure System Platinum
Tensile 200 psi (1.38 MPa)
Appearance White
Cure 7 days / RTV
Dielectric Strength 540 volts/mil (21.06 kV/mm)
Durometer 75 Type A
Elongation 30 %
Lap Shear 150 psi (1.03 MPa)
Mix Ratio 15:1
Specific Gravity 1.53
Tear 50 ppi (8.82 kN/m)
Volume Resistivity 530,000,000,000,000 ohmcm
Work Time 2 hours
Comment Primed w/CF1-135, Contains Boron Nitride

View more