Coatings/Dispersions

Product Cure System Viscosity Non Volatile Content Durometer Data Sheet Comment
CV-1152 Oxime 7,300 cP N/A N/A Download CV-1152 data sheet Soft, very low modulus coating

Product Details

Property Average Result
Viscosity 7,300 cP (7,300 mPa*s)
Appearance Translucent
Tack Free Time 50 minutes
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Refractive Index 1.43
Specific Gravity 1.01
Comment Soft, very low modulus coating

View more

R-1008-0 Oxime 1,300 cP 70 % 23 Type A Download R-1008-0 data sheet N/A

Product Details

Property Average Result
Viscosity 1,300 cP (1,300 mPa*s)
Non Volatile Content 70 %
Appearance Translucent
Dielectric Strength 513 volts/mil (20.01 kV/mm)
Durometer 23 Type A
Elongation 223 %
Tack Free Time 50 minutes
Tensile 235 psi (1.62 MPa)
Thermal Conductivity 0.17 W/(mK)

View more

R-1009 Oxime 6,150 cP 32 % 45 Type A Download R-1009 data sheet High strength coating recommend for coating PCBs and other electronic assemblies.

Product Details

Property Average Result
Viscosity 6,150 cP (6,150 mPa*s)
Non Volatile Content 32 %
Appearance Translucent
Tack Free Time 1.5 hours
Cure 7 days / RTV
Cure System Oxime
Durometer 45 Type A
Elongation 650 %
Specific Gravity 1.1
Tear 95 ppi (16.75 kN/m)
Tensile 1,150 psi (7.93 MPa)
Comment High strength coating recommend for coating PCBs and other electronic assemblies.

View more

R-1077 N/A 3,400 cP 60 % 40 Type A Download R-1077 data sheet N/A

Product Details

Property Average Result
Viscosity 3,400 cP (3,400 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Tack Free Time 20 minutes
Cure 6 days / RTV
Durometer 40 Type A
Elongation 330 %
Tensile 745 psi (5.14 MPa)

View more

R-1082 Acetoxy 700 cP 29 % 25 Type A Download R-1082 data sheet Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

Product Details

Property Average Result
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Appearance Translucent
Cure 5 days / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 950 %
Refractive Index 1.41
Specific Gravity 1.09
Stress at Strain 160 psi / 300 % (1.1 Mpa / 300 %)
Tear 125 ppi (22.05 kN/m)
Tensile 1,425 psi (9.83 MPa)
Comment Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

View more

R-1099 Condensation 6,600 cP 30 % 40 Type A Download R-1099 data sheet N/A

Product Details

Property Average Result
Viscosity 6,600 cP (6,600 mPa*s)
Non Volatile Content 30 %
Appearance Translucent
Tack Free Time 10 minutes
Cure 7 days / RTV
Cure System Condensation
Dielectric Strength 635 volts/mil (24.77 kV/mm)
Durometer 40 Type A
Elongation 570 %
Mix Ratio 1 Part
Tensile 1,050 psi (7.24 MPa)

View more

R-1182 Acetoxy N/A 7 % N/A Download R-1182 data sheet One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

Product Details

Property Average Result
Non Volatile Content 7 %
Appearance Translucent
Cure RTV
Cure System Acetoxy
Comment One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

View more

R-2180 Platinum 3,075 cP 20 % 40 Type A Download R-2180 data sheet High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

Product Details

Property Average Result
Viscosity 3,075 cP (3,075 mPa*s)
Non Volatile Content 20 %
Appearance Translucent
Cure 45 minutes / 75 °C 135 minutes / 150 °C
Cure System Platinum
Durometer 40 Type A
Elongation 1,050 %
Mix Ratio 1:1
Refractive Index 1.41
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Work Time 72 hours
Comment High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

View more

R-2182 Platinum 24 cP 25 % N/A Download R-2182 data sheet Requires minimum heat to cure. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

Product Details

Property Average Result
Viscosity 24 cP (24 mPa*s)
Non Volatile Content 25 %
Appearance Translucent
Cure 5 minutes / RTV
Cure System Platinum
Mix Ratio 1:1
Post Cure 5 minutes / 150 °C
Specific Gravity 0.96
Work Time 24 hours
Comment Requires minimum heat to cure. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

View more

R-3930 Acetoxy 735 cP 60 % 30 Type A Download R-3930 data sheet 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

Product Details

Property Average Result
Viscosity 735 cP (735 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 30 Type A
Elongation 400 %
Specific Gravity 1.36
Tear 40 ppi (7.05 kN/m)
Tensile 750 psi (5.17 MPa)
Comment 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

View more

Foams

Product Foam Density Viscosity Cure System Application Life Appearance Data Sheet Comment
CF1-3710-2 50 lbs/ft3 N/A Platinum N/A Gray Download CF1-3710-2 data sheet Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

Product Details

Property Average Result
Cure System Platinum
Foam Density 50 lbs/ft3 (0.8 g/cm3)
Appearance Gray
Cure 1 minutes / RTV
Extrusion Rate 1 g/minute
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Tack Free Time 10 minutes
Comment Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

View more

CF3-2350 25 lbs/ft³ 90,000 cP Platinum N/A Gray Download CF3-2350 data sheet Useful where stability at higher and lower temperatures is required.

Product Details

Property Average Result
Foam Density 25 lbs/ft³ (0.4 g/cm³)
Viscosity 90,000 cP (90,000 mPa*s)
Cure System Platinum
Appearance Gray
Cure 45 minutes / 100 °C
Cure Type RTV
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Specific Gravity 1.1

View more

CV-2391 20 lbs/ft3 3,000 cP Platinum 6 minutes White Download CV-2391 data sheet Cure in place versatile low outgassing foam, application life 6 minutes

Product Details

Property Average Result
Viscosity 3,000 cP (3,000 mPa*s)
Cure System Platinum
Foam Density 20 lbs/ft3 (0.32 g/cm3)
Application Life 6 minutes
Appearance White
Cure 60 minutes / RTV
Mix Ratio 1:10
Comment Cure in place versatile low outgassing foam, application life 6 minutes

View more

R-2360 12 lbs/ft3 40,000 cP Platinum 2 minutes White Download R-2360 data sheet Flexible cure in place low density foam. Application life 2 minutes.

Product Details

Property Average Result
Viscosity 40,000 cP (40,000 mPa*s)
Cure System Platinum
Foam Density 12 lbs/ft3 (0.19 g/cm3)
Application Life 2 minutes
Appearance White
Cure 20 minutes / RTV
Mix Ratio 1:1
Comment Flexible cure in place low density foam. Application life 2 minutes.

View more

SFM5-2350 25 lbs/ft3 52,500 cP Platinum N/A Black Download SFM5-2350 data sheet Cure in place versatile tough foam. Application life 6 minutes.

Product Details

Property Average Result
Viscosity 52,500 cP (52,500 mPa*s)
Cure System Platinum
Foam Density 25 lbs/ft3 (0.4 g/cm3)
Appearance Black
Cure 33 minutes / 100 °C
Dielectric Strength 190 volts/mil (7.41 kV/mm)
Mix Ratio 1:1
Specific Gravity 1.1
Volume Resistivity 2,200,000,000,000,000 ohmcm
Work Time 23 minutes
Comment Cure in place versatile tough foam. Application life 6 minutes.

View more

Gels

Product Viscosity Penetration Work Time Mix Ratio Data Sheet Comment
EPM-2480 2,500 cP 4 mm 30 hours 1:1 Download EPM-2480 data sheet Soft High Tack Gel

Product Details

Property Average Result
Viscosity 2,500 cP (2,500 mPa*s)
Penetration 4 mm
Work Time 30 hours
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <2 ppm
Mix Ratio 1:1
Volume Resistivity 100,000,000,000,000 ohmcm
Comment Soft High Tack Gel

View more

EPM-2482 1,800 cP 3 mm N/A 1:1 Download EPM-2482 data sheet Soft High Tack Gel;For applications requiring low volatility. Useful for potting intricate assemblies due to a low viscosity. As a low modulus embedding or potting compound for environmental protection of electronic assemblies and components

Product Details

Property Average Result
Viscosity 1,800 cP (1,800 mPa*s)
Penetration 3 mm
Appearance Clear
Cure 40 minutes / 150 °C
Cure System Platinum
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <4 ppm
Mix Ratio 1:1
Volatile Content 0.3 %
Comment Soft High Tack Gel;For applications requiring low volatility. Useful for potting intricate assemblies due to a low viscosity. As a low modulus embedding or potting compound for environmental protection of electronic assemblies and components

View more

FS-3502-1 1,200 cP N/A N/A 1:1 Download FS-3502-1 data sheet Firm Fluoro Gel;Recommended for long term solvent / fuel exposure, 6,000 cP maximum mixed viscosity after 3 hrs

Product Details

Property Average Result
Viscosity 1,200 cP (1,200 mPa*s)
Appearance White
Cure 4 hours / 50 °C
Cure System Platinum
Durometer 10 Type 00
Mix Ratio 1:1
Comment Firm Fluoro Gel;Recommended for long term solvent / fuel exposure, 6,000 cP maximum mixed viscosity after 3 hrs

View more

GEL-3500 11,250 cP N/A 12 hours 1:1 Download GEL-3500 data sheet Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

Product Details

Property Average Result
Viscosity 11,250 cP (11,250 mPa*s)
Work Time 12 hours
Appearance Translucent
Cure 45 minutes / 150 °C
Cure System Platinum
Durometer 50 Type 00
Mix Ratio 1:1
Operating Temperature -65 °C / 220 °C
Comment Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

View more

GEL-8100 535 cP N/A N/A 1:1 Download GEL-8100 data sheet N/A

Product Details

Property Average Result
Viscosity 535 cP (535 mPa*s)
Appearance Clear
Cure 1 hours / 100 °C
Mix Ratio 1:1
Specific Gravity 0.98

View more

GEL-8111 535 cP N/A N/A 1:1 Download GEL-8111 data sheet For applications requiring a low viscosity and low volatility soft gel

Product Details

Property Average Result
Appearance Clear
Cure 1 hour / 100°C
Cure System Platinum
Cure Type Heat Cure
Mix Ratio 1:1
Refractive Index 1.40
Rheology Flowable / Self Leveling
Viscosity 535 cP (535 mPa*s)
Volatile Content 0.09 %

View more

GEL-8127 530 cP 8 mm N/A N/A Download GEL-8127 data sheet N/A

Product Details

Property Average Result
Viscosity 530 cP (530 mPa*s)
Penetration 8 mm
Appearance Translucent
Cure 35 minutes / 150 °C

View more

GEL-8130 25,200 cP 2.2 mm 2.5 hours 1:1 Download GEL-8130 data sheet Medium tack, low penetration, for use as adhesive layer on removable tacky films and tapes. (5 seconds)

Product Details

Property Average Result
Viscosity 25,200 cP (25,200 mPa*s)
Penetration 2.2 mm
Work Time 2.5 hours
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Mix Ratio 1:1
Volatile Content 1.4 %
Comment Medium tack, low penetration, for use as adhesive layer on removable tacky films and tapes. (5 seconds)

View more

GEL-8132 12,000 cP 1.1 mm N/A 1:1 Download GEL-8132 data sheet High tack, low penetration, for use as adhesive layer on removable tacky films and tapes. (5 seconds)

Product Details

Property Average Result
Viscosity 12,000 cP (12,000 mPa*s)
Penetration 1.1 mm
Appearance Translucent
Cure System Platinum
Mix Ratio 1:1
Comment High tack, low penetration, for use as adhesive layer on removable tacky films and tapes. (5 seconds)

View more

GEL-8136 450 cP 14 mm N/A N/A Download GEL-8136 data sheet N/A

Product Details

Property Average Result
Viscosity 450 cP (450 mPa*s)
Penetration 14 mm
Appearance Clear
Cure 60 minutes / 140 °C

View more

GEL-8150 500 cP 5 mm 4 hours 1:1 Download GEL-8150 data sheet Soft High Tack Gel

Product Details

Property Average Result
Viscosity 500 cP (500 mPa*s)
Penetration 5 mm
Work Time 4 hours
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Refractive Index 1.40
Specific Gravity 0.97
Volatile Content 1 %
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft High Tack Gel

View more

GEL-8170 600 cP 9 mm N/A 1:1 Download GEL-8170 data sheet Very Soft High Tack Gel;Max viscosity after 6 hrs is 2,000 cP

Product Details

Property Average Result
Viscosity 600 cP (600 mPa*s)
Penetration 9 mm
Appearance Translucent
Cure 90 minutes / 80 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Very Soft High Tack Gel;Max viscosity after 6 hrs is 2,000 cP

View more

GEL-8246 35,000 cP N/A N/A N/A Download GEL-8246 data sheet N/A

Product Details

Property Average Result
Viscosity 35,000 cP (35,000 mPa*s)
Appearance Clear
Durometer 55 Type 00
Refractive Index 1.47
Specific Gravity 1.05
Volatile Content 0.4 %

View more

GEL-8250 650 cP 5 mm 2 hours 1:1 Download GEL-8250 data sheet Soft Med Tack Gel;For applications requiring a broader operating temperature range.

Product Details

Property Average Result
Viscosity 650 cP (650 mPa*s)
Penetration 5 mm
Work Time 2 hours
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -115 °C / 265 °C
Refractive Index 1.43
Specific Gravity 1
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft Med Tack Gel;For applications requiring a broader operating temperature range.

View more

GEL1-8155 14,500 cP 0.4 mm N/A 1:1 Download GEL1-8155 data sheet Soft Low Tack Gel;Viscosity increases ~ 1.5X in 24 hrs (¼” diameter foot, 1.5 seconds)

Product Details

Property Average Result
Viscosity 14,500 cP (14,500 mPa*s)
Penetration 0.4 mm
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Non Volatile Content 100 %
Operating Temperature -65 °C / 200 °C
Refractive Index 1.40
Comment Soft Low Tack Gel;Viscosity increases ~ 1.5X in 24 hrs (¼” diameter foot, 1.5 seconds)

View more

GEL8-8150 500 cP 4 mm 1.5 hours 1:1 Download GEL8-8150 data sheet Soft High Tack Gel

Product Details

Property Average Result
Viscosity 500 cP (500 mPa*s)
Penetration 4 mm
Work Time 1.5 hours
Appearance Clear
Cure 30 minutes / 100 °C
Cure System Platinum
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 0.97
Comment Soft High Tack Gel

View more

LS-3140 19,800 cP 0.4 mm 24 hours 1:1 Download LS-3140 data sheet Soft Low Tack Gel;Low volatility, 24 hr minimum potlife based on 2X initial viscosity

Product Details

Property Average Result
Viscosity 19,800 cP (19,800 mPa*s)
Penetration 0.4 mm
Work Time 24 hours
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Dielectric Strength 350 volts/mil (13.65 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <2 ppm
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.40
Volume Resistivity 100,000,000,000,000 ohmcm
Comment Soft Low Tack Gel;Low volatility, 24 hr minimum potlife based on 2X initial viscosity

View more

LS-3238 1,500 cP N/A 11 hours 1:1 Download LS-3238 data sheet Resistant to hydrocarbon solvents. Index matches Magnesium Fluoride. Potlife based on 3,000 cPs maximum mixed viscosity after 6hrs

Product Details

Property Average Result
Viscosity 1,500 cP (1,500 mPa*s)
Work Time 11 hours
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Durometer 15 Type 00
Mix Ratio 1:1
Operating Temperature -40 °C / 200 °C
Refractive Index 1.38
Specific Gravity 1.28
Volatile Content 0.14 %
Comment Resistant to hydrocarbon solvents. Index matches Magnesium Fluoride. Potlife based on 3,000 cPs maximum mixed viscosity after 6hrs

View more

LS-3246 1,000 cP N/A 8 hours 1:1 Download LS-3246 data sheet Firm Gel;Index Matches 1.46 RI such as fused silica. Will RTV within 24 hrs. 5 hr. minimum potlife based on 2X initial viscosity.

Product Details

Property Average Result
Viscosity 1,000 cP (1,000 mPa*s)
Work Time 8 hours
Appearance Clear
Cure 1 minutes / 65 °C
Cure System Platinum
Durometer 10 Type 00
Mix Ratio 1:1
Operating Temperature -40 °C / 200 °C
Refractive Index 1.46
Specific Gravity 1.04
Comment Firm Gel;Index Matches 1.46 RI such as fused silica. Will RTV within 24 hrs. 5 hr. minimum potlife based on 2X initial viscosity.

View more

LS-3441 14,500 cP 0.4 mm N/A 1:1 Download LS-3441 data sheet Soft Low Tack Gel; Tough gel and 24 hr minimum potlife based on 2X initial viscosity

Product Details

Property Average Result
Viscosity 14,500 cP (14,500 mPa*s)
Penetration 0.4 mm
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Refractive Index 1.41
Comment Soft Low Tack Gel; Tough gel and 24 hr minimum potlife based on 2X initial viscosity

View more

LS-3443 650 cP 5 mm N/A 1:1 Download LS-3443 data sheet Soft High Tack Gel;Recommended as an optically robust alter-te to index match to 1.46 substrates;will LTV , 2hr minimum potlife based on 2X initial viscosity

Product Details

Property Average Result
Viscosity 650 cP (650 mPa*s)
Penetration 5 mm
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -115 °C / 265 °C
Refractive Index 1.43
Specific Gravity 1
Volatile Content 0.35 %
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft High Tack Gel;Recommended as an optically robust alter-te to index match to 1.46 substrates;will LTV , 2hr minimum potlife based on 2X initial viscosity

View more

LS1-3252 360 cP N/A N/A N/A Download LS1-3252 data sheet 1.52 Refractive Index firm gel for encapsulating LEDs, and to reduce lightloss for other optical applications.

Product Details

Property Average Result
Viscosity 360 cP (360 mPa*s)
Appearance Clear
Cure 30 minutes / 150 °C
Durometer 25 Type 00
Refractive Index 1.52
Specific Gravity 1.07
Comment 1.52 Refractive Index firm gel for encapsulating LEDs, and to reduce lightloss for other optical applications.

View more

LS1-3443 2,500 cP 6 mm N/A N/A Download LS1-3443 data sheet N/A

Product Details

Property Average Result
Viscosity 2,500 cP (2,500 mPa*s)
Penetration 6 mm
Appearance Clear
Specific Gravity 1

View more

LS3-3354 5,200 cP N/A 80 minutes 1:1 Download LS3-3354 data sheet Soft Gel;Excellent for phosphor coatings.

Product Details

Property Average Result
Viscosity 5,200 cP (5,200 mPa*s)
Work Time 80 minutes
Appearance Clear
Cure 1 minutes / 70 °C
Cure System Platinum
Durometer 60 Type 000
Mix Ratio 1:1
Operating Temperature -40 °C / 200 °C
Refractive Index 1.54
Comment Soft Gel;Excellent for phosphor coatings.

View more

Low Viscosity Elastomers

Product Viscosity Durometer Work Time Tensile Data Sheet Comment
CF1-3510 70,000 cP 20 Type A 7 hours 185 psi Download CF1-3510 data sheet LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

Product Details

Property Average Result
Cure System Platinum
Viscosity 70,000 cP (70,000 mPa*s)
Durometer 20 Type A
Tensile 185 psi (1.28 MPa)
Elongation 135 %
Appearance Red
Mix Ratio 10:1
Specific Gravity 1.44
Work Time 7 hours
Comment LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

View more

CF19-2186 75,000 cP 25 Type A 15 minutes 1,100 psi Download CF19-2186 data sheet Dielectric properties are excellent for actuators and other applications where dielectric properties are critical

Product Details

Property Average Result
Cure System Platinum
Viscosity 75,000 cP (75,000 mPa*s)
Durometer 25 Type A
Tensile 1,100 psi (7.59 MPa)
Elongation 600 %
Appearance Translucent
Cure 30 minutes / 150 °C
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 1.11
Tear 80 ppi (14.11 kN/m)
Work Time 15 minutes
Comment Dielectric properties are excellent for actuators and other applications where dielectric properties are critical

View more

CF19-2615 1,300 cP 30 Type A 4 hours 120 psi Download CF19-2615 data sheet Versatile, clear coating, cure can be heat accelerated.

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,300 cP (1,300 mPa*s)
Durometer 30 Type A
Tensile 120 psi (0.83 MPa)
Elongation 100 %
Appearance Clear
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Refractive Index 1.41
Volume Resistivity 1,000,000,000,000,000 ohmcm
Work Time 4 hours
Comment Versatile, clear coating, cure can be heat accelerated.

View more

CF3-3521 N/A 30 Type A 12 hours 700 psi Download CF3-3521 data sheet LCE Fluoro Elastomer;Recommend for short term fuel or solvent exposure.

Product Details

Property Average Result
Cure System Platinum
Durometer 30 Type A
Tensile 700 psi (4.83 MPa)
Elongation 360 %
Appearance Translucent
Cure 30 minutes / 150 °C
Extrusion Rate 120 g/minute
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.26
Work Time 12 hours
Comment LCE Fluoro Elastomer;Recommend for short term fuel or solvent exposure.

View more

CV4-2500 1,500 cP 28 Type A N/A N/A Download CV4-2500 data sheet Low Outgassing clear coating, cure can be heat accelerated.

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,500 cP (1,500 mPa*s)
Durometer 28 Type A
Appearance Clear
Cure 1 hours / 65 °C
Dielectric Strength 670 volts/mil (26.13 kV/mm)
Mix Ratio 1:1
Refractive Index 1.41
Tack Free Time 15 hours
Thermal Conductivity 0.15 W/(mK)
Volume Resistivity 200,000,000,000,000 ohmcm
Comment Low Outgassing clear coating, cure can be heat accelerated.

View more

EPM-2420 2,600 cP 30 Type A N/A 425 psi Download EPM-2420 data sheet Clear, self leveling and good adhesion to various plastics.

Product Details

Property Average Result
Cure System Platinum
Viscosity 2,600 cP (2,600 mPa*s)
Durometer 30 Type A
Tensile 425 psi (2.93 MPa)
Elongation 150 %
Appearance Clear
Cure 1 minutes / 65 °C
Ionic Content Cl <2 ppm
Ionic Content K <1 ppm
Ionic Content Na <8 ppm
Mix Ratio 1:1
Specific Gravity 1.01
Volatile Content 0.85 %
Comment Clear, self leveling and good adhesion to various plastics.

View more

EPM-2421 3,225 cP 50 Type A 3 hours 850 psi Download EPM-2421 data sheet N/A

Product Details

Property Average Result
Viscosity 3,225 cP (3,225 mPa*s)
Durometer 50 Type A
Tensile 850 psi (5.86 MPa)
Elongation 90 %
Appearance Clear
Dielectric Strength 610 volts/mil (23.79 kV/mm)
Lap Shear 250 psi (1.72 MPa)
Specific Gravity 1.02
Tack Free Time 5 hours
Volatile Content 0.70 %
Work Time 3 hours

View more

LS-6140 3,125 cP 50 Type A 3 hours 850 psi Download LS-6140 data sheet RTV; Low volatility

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,125 cP (3,125 mPa*s)
Durometer 50 Type A
Tensile 850 psi (5.86 MPa)
Elongation 90 %
Appearance Clear
Cure 15 minutes / 150 °C
Dielectric Strength 520 volts/mil (20.28 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <2 ppm
Ionic Content Na <4 ppm
Lap Shear 200 psi (1.38 MPa)
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 1.02
Tack Free Time 6 hours
Volume Resistivity 1,100,000,000,000,000 ohmcm
Work Time 3 hours
Comment RTV; Low volatility

View more

LS-6143 5,500 cP 40 Type A 2 hours 600 psi Download LS-6143 data sheet Low Volatility, 1.43 Refractive Index at 589nm. For applications requiring a broader operating temperature range. 180 psi (1.2 MPa), primed (LS1-3200) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,500 cP (5,500 mPa*s)
Durometer 40 Type A
Tensile 600 psi (4.14 MPa)
Elongation 125 %
Appearance Translucent
Cure 4 hours / 65 °C
Dielectric Strength 550 volts/mil (21.45 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <1 ppm
Lap Shear 180 psi (1.24 MPa)
Mix Ratio 10:1
Operating Temperature -115 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.04
Volume Resistivity 1,100,000,000,000,000 ohmcm
Work Time 2 hours
Comment Low Volatility, 1.43 Refractive Index at 589nm. For applications requiring a broader operating temperature range. 180 psi (1.2 MPa), primed (LS1-3200) lap shear.

View more

LS-6941 5,300 cP 50 Type A 5.5 hours 1,300 psi Download LS-6941 data sheet General use RTV clear adhesive

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,300 cP (5,300 mPa*s)
Durometer 50 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 95 %
Appearance Clear
Cure 15 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.41
Specific Gravity 1.03
Tack Free Time 15 hours
Tear 20 ppi (3.53 kN/m)
Volume Resistivity 1,000,000,000,000,000 ohmcm
Work Time 5.5 hours
Comment General use RTV clear adhesive

View more

LS-6943 5,400 cP 40 Type A N/A 900 psi Download LS-6943 data sheet 1.43 Refractive Index at 589nm. For applications requiring a broader operating temperature range.

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,400 cP (5,400 mPa*s)
Durometer 40 Type A
Tensile 900 psi (6.21 MPa)
Elongation 120 %
Appearance Clear
Cure 60 minutes / 60 °C
Mix Ratio 10:1
Operating Temperature -115 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.03
Comment 1.43 Refractive Index at 589nm. For applications requiring a broader operating temperature range.

View more

LS-6946 37,500 cP 30 Type A 2 hours 675 psi Download LS-6946 data sheet 1.46 Refractive Index at 589nm and contains fumed silica.

Product Details

Property Average Result
Cure System Platinum
Viscosity 37,500 cP (37,500 mPa*s)
Durometer 30 Type A
Tensile 675 psi (4.66 MPa)
Elongation 275 %
Appearance Translucent
Cure 30 minutes / 150 °C
Dielectric Strength 510 volts/mil (19.89 kV/mm)
Lap Shear 510 psi (3.52 MPa)
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.46
Specific Gravity 1.14
Tear 40 ppi (7.05 kN/m)
Volatile Content 0.20 %
Work Time 2 hours
Comment 1.46 Refractive Index at 589nm and contains fumed silica.

View more

LS-8941 21,500 cP 80 Type A 24 hours 1,250 psi Download LS-8941 data sheet Hard and flexible elastomer. Can be casted and liquid injection molded. Requires heat to cure. Recommend SP-120 or SP-201 for overmolding.

Product Details

Property Average Result
Cure System Platinum
Viscosity 21,500 cP (21,500 mPa*s)
Durometer 80 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 65 %
Appearance Clear
Cure 30 minutes / 150 °C
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.07
Tear 55 ppi (9.7 kN/m)
Work Time 24 hours
Comment Hard and flexible elastomer. Can be casted and liquid injection molded. Requires heat to cure. Recommend SP-120 or SP-201 for overmolding.

View more

LS1-6140 3,200 cP 50 Type A N/A 900 psi Download LS1-6140 data sheet Low volatility and requires heat to cure, long pot life for dispensing

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,200 cP (3,200 mPa*s)
Durometer 50 Type A
Tensile 900 psi (6.21 MPa)
Elongation 90 %
Appearance Clear
Cure 60 minutes / 150 °C
Dielectric Strength 530 volts/mil (20.67 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <2.5 ppm
Ionic Content Na <2.5 ppm
Lap Shear 270 psi (1.86 MPa)
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 1.02
Comment Low volatility and requires heat to cure, long pot life for dispensing

View more

LS1-6941 62,500 cP 50 Type A 24 hours 750 psi Download LS1-6941 data sheet Versatile and tough clear elastomer. Requires heat to cure.

Product Details

Property Average Result
Cure System Platinum
Viscosity 62,500 cP (62,500 mPa*s)
Durometer 50 Type A
Tensile 750 psi (5.17 MPa)
Elongation 305 %
Appearance Clear
Cure 30 minutes / 150 °C
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.03
Tear 80 ppi (14.11 kN/m)
Work Time 24 hours
Comment Versatile and tough clear elastomer. Requires heat to cure.

View more

LS2-6140 2,740 cP 50 Type A N/A 1,130 psi Download LS2-6140 data sheet Low Volatility, 1.41 Refractive Index at 589nm. Long pot life and requires heat to cure (80 C). Primerless adhesion to ceramic, plastics and metals. Tested per UL94 and passes V0.

Product Details

Property Average Result
Cure System Platinum
Viscosity 2,740 cP (2,740 mPa*s)
Durometer 50 Type A
Tensile 1,130 psi (7.79 MPa)
Elongation 150 %
Appearance Clear
Cure 60 minutes / 150 °C
Ionic Content Cl <2.5 ppm
Ionic Content K <2.5 ppm
Ionic Content Na <5 ppm
Lap Shear 477 psi (3.29 MPa)
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.03
Volatile Content 1 %
Volume Resistivity 1,100,000,000,000,000 ohmcm
Comment Low Volatility, 1.41 Refractive Index at 589nm. Long pot life and requires heat to cure (80 C). Primerless adhesion to ceramic, plastics and metals. Tested per UL94 and passes V0.

View more

LS2-6941 1,100 cP 30 Type A 5.5 hours 120 psi Download LS2-6941 data sheet General use RTV clear adhesive.

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,100 cP (1,100 mPa*s)
Durometer 30 Type A
Tensile 120 psi (0.83 MPa)
Elongation 100 %
Appearance Clear
Cure 30 minutes / 150 °C
Dielectric Strength 600 volts/mil (23.4 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <5 ppm
Ionic Content Na <10 ppm
Mix Ratio 1:1
Refractive Index 1.41
Volatile Content 0.7 %
Volume Resistivity 100,000,000,000,000 ohmcm
Work Time 5.5 hours
Comment General use RTV clear adhesive.

View more

R-2188 11,300 cP 20 Type A 8 hours 475 psi Download R-2188 data sheet Excellent dielectric properties, flexible cure with 14 hr pot life, tested per UL 94 and passed V1.

Product Details

Property Average Result
Cure System Platinum
Viscosity 11,300 cP (11,300 mPa*s)
Durometer 20 Type A
Tensile 475 psi (3.28 MPa)
Elongation 350 %
Appearance Translucent
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <3 ppm
Ionic Content Na <1 ppm
Mix Ratio 1:1
Specific Gravity 1.05
Work Time 8 hours
Comment Excellent dielectric properties, flexible cure with 14 hr pot life, tested per UL 94 and passed V1.

View more

R-2613 4,000 cP 45 Type A 2 hours 1,140 psi Download R-2613 data sheet N/A

Product Details

Property Average Result
Cure System Platinum
Viscosity 4,000 cP (4,000 mPa*s)
Durometer 45 Type A
Tensile 1,140 psi (7.86 MPa)
Elongation 150 %
Appearance Clear
Work Time 2 hours

View more

R-2615 5,300 cP 50 Type A 4 hours 1,300 psi Download R-2615 data sheet Self leveling, low temperature cure versatile encapsulant

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,300 cP (5,300 mPa*s)
Durometer 50 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 95 %
Appearance Clear
Cure 15 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.41
Specific Gravity 1.03
Tear 20 ppi (3.53 kN/m)
Volume Resistivity 1,100,000,000,000,000 ohmcm
Work Time 4 hours
Comment Self leveling, low temperature cure versatile encapsulant

View more

R-2615-3 N/A 50 Type A 2 hours 1,000 psi Download R-2615-3 data sheet N/A

Product Details

Property Average Result
Viscosity 4,250 cP
Durometer 50 Type A
Tensile 1,000 psi (6.9 MPa)
Elongation 100 %
Appearance Red
Cure 30 minutes / 150 °C
Dielectric Strength 830 volts/mil (32.37 kV/mm)
Specific Gravity 1.06
Work Time 2 hours

View more

R-2655 5,400 cP 40 Type A N/A 900 psi Download R-2655 data sheet For applications requiring a broader operating temperature range

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,400 cP (5,400 mPa*s)
Durometer 40 Type A
Tensile 900 psi (6.21 MPa)
Elongation 120 %
Appearance Clear
Cure 60 minutes / 100 °C
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.43
Specific Gravity 1.03
Comment For applications requiring a broader operating temperature range

View more

R2-6755 45,000 cP 20 Type A N/A 550 psi Download R2-6755 data sheet N/A

Product Details

Property Average Result
Cure System Platinum
Viscosity 45,000 cP (45,000 mPa*s)
Durometer 20 Type A
Tensile 550 psi (3.79 MPa)
Elongation 325 %
Appearance Translucent
Refractive Index 1.46
Specific Gravity 1.14
Stress at Strain 70 psi / 100 % (0.48 MPa / 100 %)
Tack Free Time 1 hours
Tear 25 ppi (4.41 kN/m)
Volatile Content 0.8 %

View more

R21-2615 25,000 cP 75 Type A 2 hours 1,200 psi Download R21-2615 data sheet Hard clear elastomer with 2 hr pot life and LTV cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 25,000 cP (25,000 mPa*s)
Durometer 75 Type A
Tensile 1,200 psi (8.28 MPa)
Elongation 65 %
Appearance Clear
Cure 2 hours / 50 °C
Mix Ratio 1:1
Specific Gravity 1.07
Tear 35 ppi (6.17 kN/m)
Work Time 2 hours
Comment Hard clear elastomer with 2 hr pot life and LTV cure

View more