Low Viscosity Elastomers

Product Viscosity Durometer Work Time Tensile Data Sheet Comment
CF1-3510 70,000 cP 20 Type A 7 hours 185 psi Download CF1-3510 data sheet LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

Product Details

Property Average Result
Cure System Platinum
Viscosity 70,000 cP (70,000 mPa*s)
Durometer 20 Type A
Tensile 185 psi (1.28 MPa)
Elongation 135 %
Appearance Red
Mix Ratio 10:1
Specific Gravity 1.44
Work Time 7 hours
Comment LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

View more

CF19-2186 75,000 cP 25 Type A 15 minutes 1,100 psi Download CF19-2186 data sheet Dielectric properties are excellent for actuators and other applications where dielectric properties are critical

Product Details

Property Average Result
Cure System Platinum
Viscosity 75,000 cP (75,000 mPa*s)
Durometer 25 Type A
Tensile 1,100 psi (7.59 MPa)
Elongation 600 %
Appearance Translucent
Cure 30 minutes / 150 °C
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 1.11
Tear 80 ppi (14.11 kN/m)
Work Time 15 minutes
Comment Dielectric properties are excellent for actuators and other applications where dielectric properties are critical

View more

CF19-2615 1,300 cP 30 Type A 4 hours 120 psi Download CF19-2615 data sheet Versatile, clear coating, cure can be heat accelerated.

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,300 cP (1,300 mPa*s)
Durometer 30 Type A
Tensile 120 psi (0.83 MPa)
Elongation 100 %
Appearance Clear
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Refractive Index 1.41
Volume Resistivity 1,000,000,000,000,000 ohmcm
Work Time 4 hours
Comment Versatile, clear coating, cure can be heat accelerated.

View more

CF3-3521 N/A 30 Type A 12 hours 700 psi Download CF3-3521 data sheet LCE Fluoro Elastomer;Recommend for short term fuel or solvent exposure.

Product Details

Property Average Result
Cure System Platinum
Durometer 30 Type A
Tensile 700 psi (4.83 MPa)
Elongation 360 %
Appearance Translucent
Cure 30 minutes / 150 °C
Extrusion Rate 120 g/minute
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.26
Work Time 12 hours
Comment LCE Fluoro Elastomer;Recommend for short term fuel or solvent exposure.

View more

CV4-2500 1,500 cP 28 Type A N/A N/A Download CV4-2500 data sheet Low Outgassing clear coating, cure can be heat accelerated.

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,500 cP (1,500 mPa*s)
Durometer 28 Type A
Appearance Clear
Cure 1 hours / 65 °C
Dielectric Strength 670 volts/mil (26.13 kV/mm)
Mix Ratio 1:1
Refractive Index 1.41
Tack Free Time 15 hours
Thermal Conductivity 0.15 W/(mK)
Volume Resistivity 200,000,000,000,000 ohmcm
Comment Low Outgassing clear coating, cure can be heat accelerated.

View more

EPM-2420 2,600 cP 30 Type A N/A 425 psi Download EPM-2420 data sheet Clear, self leveling and good adhesion to various plastics.

Product Details

Property Average Result
Cure System Platinum
Viscosity 2,600 cP (2,600 mPa*s)
Durometer 30 Type A
Tensile 425 psi (2.93 MPa)
Elongation 150 %
Appearance Clear
Cure 1 minutes / 65 °C
Ionic Content Cl <2 ppm
Ionic Content K <1 ppm
Ionic Content Na <8 ppm
Mix Ratio 1:1
Specific Gravity 1.01
Volatile Content 0.85 %
Comment Clear, self leveling and good adhesion to various plastics.

View more

EPM-2421 3,225 cP 50 Type A 3 hours 850 psi Download EPM-2421 data sheet N/A

Product Details

Property Average Result
Viscosity 3,225 cP (3,225 mPa*s)
Durometer 50 Type A
Tensile 850 psi (5.86 MPa)
Elongation 90 %
Appearance Clear
Dielectric Strength 610 volts/mil (23.79 kV/mm)
Lap Shear 250 psi (1.72 MPa)
Specific Gravity 1.02
Tack Free Time 5 hours
Volatile Content 0.70 %
Work Time 3 hours

View more

LS-6140 3,125 cP 50 Type A 3 hours 850 psi Download LS-6140 data sheet RTV; Low volatility

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,125 cP (3,125 mPa*s)
Durometer 50 Type A
Tensile 850 psi (5.86 MPa)
Elongation 90 %
Appearance Clear
Cure 15 minutes / 150 °C
Dielectric Strength 520 volts/mil (20.28 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <2 ppm
Ionic Content Na <4 ppm
Lap Shear 200 psi (1.38 MPa)
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 1.02
Tack Free Time 6 hours
Volume Resistivity 1,100,000,000,000,000 ohmcm
Work Time 3 hours
Comment RTV; Low volatility

View more

LS-6143 5,500 cP 40 Type A 2 hours 600 psi Download LS-6143 data sheet Low Volatility, 1.43 Refractive Index at 589nm. For applications requiring a broader operating temperature range. 180 psi (1.2 MPa), primed (LS1-3200) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,500 cP (5,500 mPa*s)
Durometer 40 Type A
Tensile 600 psi (4.14 MPa)
Elongation 125 %
Appearance Translucent
Cure 4 hours / 65 °C
Dielectric Strength 550 volts/mil (21.45 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <1 ppm
Lap Shear 180 psi (1.24 MPa)
Mix Ratio 10:1
Operating Temperature -115 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.04
Volume Resistivity 1,100,000,000,000,000 ohmcm
Work Time 2 hours
Comment Low Volatility, 1.43 Refractive Index at 589nm. For applications requiring a broader operating temperature range. 180 psi (1.2 MPa), primed (LS1-3200) lap shear.

View more

LS-6941 5,300 cP 50 Type A 5.5 hours 1,300 psi Download LS-6941 data sheet General use RTV clear adhesive

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,300 cP (5,300 mPa*s)
Durometer 50 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 95 %
Appearance Clear
Cure 15 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.41
Specific Gravity 1.03
Tack Free Time 15 hours
Tear 20 ppi (3.53 kN/m)
Volume Resistivity 1,000,000,000,000,000 ohmcm
Work Time 5.5 hours
Comment General use RTV clear adhesive

View more

LS-6943 5,400 cP 40 Type A N/A 900 psi Download LS-6943 data sheet 1.43 Refractive Index at 589nm. For applications requiring a broader operating temperature range.

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,400 cP (5,400 mPa*s)
Durometer 40 Type A
Tensile 900 psi (6.21 MPa)
Elongation 120 %
Appearance Clear
Cure 60 minutes / 60 °C
Mix Ratio 10:1
Operating Temperature -115 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.03
Comment 1.43 Refractive Index at 589nm. For applications requiring a broader operating temperature range.

View more

LS-6946 37,500 cP 30 Type A 2 hours 675 psi Download LS-6946 data sheet 1.46 Refractive Index at 589nm and contains fumed silica.

Product Details

Property Average Result
Cure System Platinum
Viscosity 37,500 cP (37,500 mPa*s)
Durometer 30 Type A
Tensile 675 psi (4.66 MPa)
Elongation 275 %
Appearance Translucent
Cure 30 minutes / 150 °C
Dielectric Strength 510 volts/mil (19.89 kV/mm)
Lap Shear 510 psi (3.52 MPa)
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.46
Specific Gravity 1.14
Tear 40 ppi (7.05 kN/m)
Volatile Content 0.20 %
Work Time 2 hours
Comment 1.46 Refractive Index at 589nm and contains fumed silica.

View more

LS-8941 21,500 cP 80 Type A 24 hours 1,250 psi Download LS-8941 data sheet Hard and flexible elastomer. Can be casted and liquid injection molded. Requires heat to cure. Recommend SP-120 or SP-201 for overmolding.

Product Details

Property Average Result
Cure System Platinum
Viscosity 21,500 cP (21,500 mPa*s)
Durometer 80 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 65 %
Appearance Clear
Cure 30 minutes / 150 °C
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.07
Tear 55 ppi (9.7 kN/m)
Work Time 24 hours
Comment Hard and flexible elastomer. Can be casted and liquid injection molded. Requires heat to cure. Recommend SP-120 or SP-201 for overmolding.

View more

LS1-6140 3,200 cP 50 Type A N/A 900 psi Download LS1-6140 data sheet Low volatility and requires heat to cure, long pot life for dispensing

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,200 cP (3,200 mPa*s)
Durometer 50 Type A
Tensile 900 psi (6.21 MPa)
Elongation 90 %
Appearance Clear
Cure 60 minutes / 150 °C
Dielectric Strength 530 volts/mil (20.67 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <2.5 ppm
Ionic Content Na <2.5 ppm
Lap Shear 270 psi (1.86 MPa)
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 1.02
Comment Low volatility and requires heat to cure, long pot life for dispensing

View more

LS1-6941 62,500 cP 50 Type A 24 hours 750 psi Download LS1-6941 data sheet Versatile and tough clear elastomer. Requires heat to cure.

Product Details

Property Average Result
Cure System Platinum
Viscosity 62,500 cP (62,500 mPa*s)
Durometer 50 Type A
Tensile 750 psi (5.17 MPa)
Elongation 305 %
Appearance Clear
Cure 30 minutes / 150 °C
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.03
Tear 80 ppi (14.11 kN/m)
Work Time 24 hours
Comment Versatile and tough clear elastomer. Requires heat to cure.

View more

LS2-6140 2,740 cP 50 Type A N/A 1,130 psi Download LS2-6140 data sheet Low Volatility, 1.41 Refractive Index at 589nm. Long pot life and requires heat to cure (80 C). Primerless adhesion to ceramic, plastics and metals. Tested per UL94 and passes V0.

Product Details

Property Average Result
Cure System Platinum
Viscosity 2,740 cP (2,740 mPa*s)
Durometer 50 Type A
Tensile 1,130 psi (7.79 MPa)
Elongation 150 %
Appearance Clear
Cure 60 minutes / 150 °C
Ionic Content Cl <2.5 ppm
Ionic Content K <2.5 ppm
Ionic Content Na <5 ppm
Lap Shear 477 psi (3.29 MPa)
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.03
Volatile Content 1 %
Volume Resistivity 1,100,000,000,000,000 ohmcm
Comment Low Volatility, 1.41 Refractive Index at 589nm. Long pot life and requires heat to cure (80 C). Primerless adhesion to ceramic, plastics and metals. Tested per UL94 and passes V0.

View more

LS2-6941 1,100 cP 30 Type A 5.5 hours 120 psi Download LS2-6941 data sheet General use RTV clear adhesive.

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,100 cP (1,100 mPa*s)
Durometer 30 Type A
Tensile 120 psi (0.83 MPa)
Elongation 100 %
Appearance Clear
Cure 30 minutes / 150 °C
Dielectric Strength 600 volts/mil (23.4 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <5 ppm
Ionic Content Na <10 ppm
Mix Ratio 1:1
Refractive Index 1.41
Volatile Content 0.7 %
Volume Resistivity 100,000,000,000,000 ohmcm
Work Time 5.5 hours
Comment General use RTV clear adhesive.

View more

R-2188 11,300 cP 20 Type A 8 hours 475 psi Download R-2188 data sheet Excellent dielectric properties, flexible cure with 14 hr pot life, tested per UL 94 and passed V1.

Product Details

Property Average Result
Cure System Platinum
Viscosity 11,300 cP (11,300 mPa*s)
Durometer 20 Type A
Tensile 475 psi (3.28 MPa)
Elongation 350 %
Appearance Translucent
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <3 ppm
Ionic Content Na <1 ppm
Mix Ratio 1:1
Specific Gravity 1.05
Work Time 8 hours
Comment Excellent dielectric properties, flexible cure with 14 hr pot life, tested per UL 94 and passed V1.

View more

R-2613 4,000 cP 45 Type A 2 hours 1,140 psi Download R-2613 data sheet N/A

Product Details

Property Average Result
Cure System Platinum
Viscosity 4,000 cP (4,000 mPa*s)
Durometer 45 Type A
Tensile 1,140 psi (7.86 MPa)
Elongation 150 %
Appearance Clear
Work Time 2 hours

View more

R-2615 5,300 cP 50 Type A 4 hours 1,300 psi Download R-2615 data sheet Self leveling, low temperature cure versatile encapsulant

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,300 cP (5,300 mPa*s)
Durometer 50 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 95 %
Appearance Clear
Cure 15 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.41
Specific Gravity 1.03
Tear 20 ppi (3.53 kN/m)
Volume Resistivity 1,100,000,000,000,000 ohmcm
Work Time 4 hours
Comment Self leveling, low temperature cure versatile encapsulant

View more

R-2615-3 N/A 50 Type A 2 hours 1,000 psi Download R-2615-3 data sheet N/A

Product Details

Property Average Result
Viscosity 4,250 cP
Durometer 50 Type A
Tensile 1,000 psi (6.9 MPa)
Elongation 100 %
Appearance Red
Cure 30 minutes / 150 °C
Dielectric Strength 830 volts/mil (32.37 kV/mm)
Specific Gravity 1.06
Work Time 2 hours

View more

R-2655 5,400 cP 40 Type A N/A 900 psi Download R-2655 data sheet For applications requiring a broader operating temperature range

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,400 cP (5,400 mPa*s)
Durometer 40 Type A
Tensile 900 psi (6.21 MPa)
Elongation 120 %
Appearance Clear
Cure 60 minutes / 100 °C
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.43
Specific Gravity 1.03
Comment For applications requiring a broader operating temperature range

View more

R2-6755 45,000 cP 20 Type A N/A 550 psi Download R2-6755 data sheet N/A

Product Details

Property Average Result
Cure System Platinum
Viscosity 45,000 cP (45,000 mPa*s)
Durometer 20 Type A
Tensile 550 psi (3.79 MPa)
Elongation 325 %
Appearance Translucent
Refractive Index 1.46
Specific Gravity 1.14
Stress at Strain 70 psi / 100 % (0.48 MPa / 100 %)
Tack Free Time 1 hours
Tear 25 ppi (4.41 kN/m)
Volatile Content 0.8 %

View more

R21-2615 25,000 cP 75 Type A 2 hours 1,200 psi Download R21-2615 data sheet Hard clear elastomer with 2 hr pot life and LTV cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 25,000 cP (25,000 mPa*s)
Durometer 75 Type A
Tensile 1,200 psi (8.28 MPa)
Elongation 65 %
Appearance Clear
Cure 2 hours / 50 °C
Mix Ratio 1:1
Specific Gravity 1.07
Tear 35 ppi (6.17 kN/m)
Work Time 2 hours
Comment Hard clear elastomer with 2 hr pot life and LTV cure