Product Cure System Rheology Work Time Durometer Data Sheet Comment
CV-1142 Oxime Thixotropic / non-slump N/A 45 Type A Download CV-1142 data sheet For applications requiring a broader operating temperature range. Available in black and white. 200 psi (1.4 MPa), Unprimed lap shear.

Product Details

Property Average Result
Cure System Oxime
Extrusion Rate 35 g/minute
Lap Shear 375 psi (2.59 MPa)
Durometer 45 Type A
Appearance Translucent
Cure 7 days / RTV
Dielectric Strength 1,100 volts/mil (42.9 kV/mm)
Elongation 300 %
Mix Ratio 1 PART
Refractive Index 1.43
Specific Gravity 1.11
Tack Free Time 20 minutes
Tensile 700 psi (4.83 MPa)
Comment For applications requiring a broader operating temperature range. Available in black and white. 200 psi (1.4 MPa), Unprimed lap shear.

View more

CV-2187 Platinum Flowable / Self Leveling 3 hours 35 Type A Download CV-2187 data sheet Tough, self leveling and good adhesion to various metals.

Product Details

Property Average Result
Cure System Platinum
Viscosity 90,000 cP (90,000 mPa*s)
Durometer 35 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Elongation 400 %
Mix Ratio 10:1
Specific Gravity 1.1
Tack Free Time 15 hours
Tear 75 ppi (13.23 kN/m)
Tensile 925 psi (6.38 MPa)
Work Time 3 hours
Comment Tough, self leveling and good adhesion to various metals.

View more

CV-2289 Platinum Flowable / Self Leveling 30 minutes 30 Type A Download CV-2289 data sheet Tough, self leveling and good adhesion to various metals. Recommended for broad temperature applications. 400 psi (2.8 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 50,000 cP (50,000 mPa*s)
Lap Shear 400 psi (2.76 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Elongation 350 %
Mix Ratio 1:1
Tensile 750 psi (5.17 MPa)
Work Time 30 minutes
Comment Tough, self leveling and good adhesion to various metals. Recommended for broad temperature applications. 400 psi (2.8 MPa), primed (CF1-135) lap shear.

View more

CV-2680-12 Platinum N/A N/A N/A Download CV-2680-12 data sheet Low Outgassing version of R-2682-12.

Product Details

Property Average Result
Cure System Platinum
Lap Shear 250 psi (1.72 MPa)
Appearance Translucent
Application Life 7 minutes
Cure 4 hours / 65 °C
Elongation 400 %
Tear 115 ppi (20.28 kN/m)
Tensile 1,450 psi (10 MPa)
Comment Low Outgassing version of R-2682-12.

View more

CV-2686-12 Platinum N/A N/A N/A Download CV-2686-12 data sheet Use for RFI and EMI shielding in electrical and space applications. For applications requiring shorter work times, easy clean-up, and consistent bond thickness.

Product Details

Property Average Result
Cure System Platinum
Appearance Black
Cure 4 hours / 65 °C
Volume Resistivity 150 ohmcm
Comment Use for RFI and EMI shielding in electrical and space applications. For applications requiring shorter work times, easy clean-up, and consistent bond thickness.

View more

CV-2688-12 Platinum Thixotropic / Non-slump N/A N/A Download CV-2688-12 data sheet For applications requiring shorter work times, easy clean-up, and consistent bond thickness

Product Details

Property Average Result
Appearance Translucent
Cure 4 hours / 65 °C
Cure System Platinum
Cure Type RTV
Elongation 850 %
Lap Shear 250 psi (1.7 MPa)
Rheology Thixotropic / Non-slump
Substrate Primerless: ABS / Aluminum / Glass / Metal / PEEK / Plastic / PMMA / Polycarbonate / Polyetherimide / Polymide / Polyurethane / Silicone / Stainless steel / Titanium
Tear 115 ppi (20.3 kN/m)
Tensile 1,450 psi (10.0 MPa)

View more

CV1-1142 Oxime Flowable / Self Leveling N/A 30 Type A Download CV1-1142 data sheet Low viscosity and self leveling. Recommended for board temperature applications. 65 psi (0.45 Mpa) primed (SP-120), lap shear.

Product Details

Property Average Result
Cure System Oxime
Viscosity 13,000 cP (13,000 mPa*s)
Extrusion Rate 70 g/minute
Lap Shear 65 psi (0.45 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 200 %
Specific Gravity 1.05
Tensile 400 psi (2.76 MPa)
Comment Low viscosity and self leveling. Recommended for board temperature applications. 65 psi (0.45 Mpa) primed (SP-120), lap shear.

View more

CV1-2289-1 Platinum Flowable / Self Leveling 4 hours 30 Type A Download CV1-2289-1 data sheet White, versatile adhesive with 3 hr pot life. Recommended for broad temperature applications. 450 psi (3.1 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 52,500 cP (52,500 mPa*s)
Lap Shear 450 psi (3.1 MPa)
Durometer 30 Type A
Appearance White
Cure 15 minutes / 150 °C
Elongation 350 %
Mix Ratio 1:1
Specific Gravity 1.1
Tack Free Time 17 hours
Tensile 750 psi (5.17 MPa)
Work Time 4 hours
Comment White, versatile adhesive with 3 hr pot life. Recommended for broad temperature applications. 450 psi (3.1 MPa), primed (CF1-135) lap shear.

View more

CV2-1142 Oxime Thixotropic / non-slump N/A 50 Type A Download CV2-1142 data sheet Non-slump and excellent for applications where minimal flow is desired. For applications requiring a broader operating temperature range. Available in black and white.

Product Details

Property Average Result
Cure System Oxime
Durometer 50 Type A
Appearance Translucent
Cure 7 days / RTV
Comment Non-slump and excellent for applications where minimal flow is desired. For applications requiring a broader operating temperature range. Available in black and white.

View more

CV2-2289-1 Platinum Flowable / Self Leveling N/A 30 Type A Download CV2-2289-1 data sheet White, versatile adhesive with short pot life, tack free in 20 hrs Recommended for broad temperature applications. 300 psi (2.1 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 12,300 cP (12,300 mPa*s)
Lap Shear 300 psi (2.07 MPa)
Durometer 30 Type A
Appearance White
Cure 4 hours / 65 °C
Elongation 250 %
Mix Ratio 1:1
Specific Gravity 1.1
Tack Free Time 20 hours
Tensile 450 psi (3.1 MPa)
Comment White, versatile adhesive with short pot life, tack free in 20 hrs Recommended for broad temperature applications. 300 psi (2.1 MPa) primed (CF1-135) lap shear.

View more

CV2-2646 Alkoxy Flowable / Self Leveling 2 hours 75 Type A Download CV2-2646 data sheet 0.003 ohmcm at 200 C

Product Details

Property Average Result
Cure System Alkoxy
Lap Shear 185 psi (1.28 MPa)
Durometer 75 Type A
Appearance Gray
Cure 7 days / RTV
Elongation 70 %
Flow Rate 4 in (101.6 mm)
Mix Ratio 100:0.5
Specific Gravity 3.23
Tear 55 ppi (9.7 kN/m)
Tensile 300 psi (2.07 MPa)
Thermal Conductivity 1.5 W/(mK)
Volume Resistivity 0 ohmcm
Work Time 2 hours
Comment 0.003 ohmcm at 200 C

View more

CV7-1142-1 Oxime Flowable / Self Leveling N/A 40 Type A Download CV7-1142-1 data sheet Recommended for extended operation at elevated temperatures.

Product Details

Property Average Result
Cure System Oxime
Rheology Flowable / Self Leveling
Durometer 40 Type A
Appearance White
Cure 7 days / RTV
Cure Type RTV
Dielectric Strength 1,180 volts/mil (46.02 kV/mm)
Elongation 300 %
Extrusion Rate 20 g/minute
Flow Rate 0.7 in (17.78 mm)
Mix Ratio 1 PART
Specific Gravity 1.13
Tack Free Time 20 minutes
Tear 60 ppi (10.58 kN/m)
Tensile 700 psi (4.83 MPa)

View more

EPM-2411-2 Platinum Thixotropic / non-slump N/A 20 Type A Download EPM-2411-2 data sheet Low volatility, Thixotropic, dispensable and 0.5 mm maximum slump. Shipped and stored frozen.

Product Details

Property Average Result
Cure System Platinum
Viscosity 300,000 cP (300,000 mPa*s)
Extrusion Rate 0.9 g/minute
Durometer 20 Type A
Appearance Black
Cure 15 minutes / 200 °C
Elongation 700 %
Mix Ratio 1 PART
Specific Gravity 1.15
Stress at Strain 50 psi / 100 % (0.34 MPa / 100 %)
Tear 50 ppi (8.82 kN/m)
Tensile 750 psi (5.17 MPa)
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Low volatility, Thixotropic, dispensable and 0.5 mm maximum slump. Shipped and stored frozen.

View more

EPM-2412 Platinum Flowable / Self Leveling 20 minutes 30 Type A Download EPM-2412 data sheet Mobile Devices, Displace

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 0.08 g/minute
Durometer 30 Type A
Appearance Translucent
Cure 24 hours / RTV
Dielectric Strength 530 volts/mil (20.67 kV/mm)
Elongation 450 %
Tensile 850 psi (5.86 MPa)
Thermal Conductivity 0.18 W/(mK)
Volume Resistivity 100,000,000,000,000 ohmcm
Work Time 20 minutes
Comment Mobile Devices, Displace

View more

EPM-2461 Platinum Thixotropic / non-slump 1 minutes 30 Type A Download EPM-2461 data sheet Carbon filled.

Product Details

Property Average Result
Cure System Platinum
Viscosity 675,000 cP (675,000 mPa*s)
Lap Shear 325 psi (2.24 MPa)
Durometer 30 Type A
Appearance Black
Cure 24 hours / RTV
Elongation 350 %
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <6 ppm
Mix Ratio 1:1
Operating Temperature -100 °C / 300 °C
Specific Gravity 1.05
Tear 30 ppi (5.29 kN/m)
Tensile 500 psi (3.45 MPa)
Thermal Conductivity 0.22 W/(mK)
Volume Resistivity 535 ohmcm
Work Time 1 minutes
Comment Carbon filled.

View more

EPM-2462 Platinum Thixotropic / non-slump 2.75 hours 85 Type A Download EPM-2462 data sheet N/A

Product Details

Property Average Result
Cure System Platinum
Viscosity 186,200 cP (186,200 mPa*s)
Durometer 85 Type A
Appearance Tan
Cure 30 minutes / 150 C
Elongation 70 %
Ionic Content Cl <5 ppm
Ionic Content K <7 ppm
Ionic Content Na <5 ppm
Mix Ratio 20:1
Specific Gravity 3.39
Tensile 525 psi (3.62 MPa)
Thermal Conductivity 1.2 W/(mK)
Volume Resistivity 0.01 ohmcm
Work Time 2.75 hours

View more

FS-3730 Acetoxy Thixotropic / non-slump N/A 33 Type A Download FS-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 180 g/minute
Lap Shear 350 psi (2.41 MPa)
Durometer 33 Type A
Appearance White
Cure 72 hours / RTV
Elongation 440 %
Mix Ratio 1 PART
Specific Gravity 1.4
Tack Free Time 25 minutes
Tear 55 ppi (9.7 kN/m)
Tensile 900 psi (6.21 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

View more

FS3-3730 Acetoxy Thixotropic / non-slump N/A 35 Type A Download FS3-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 230 g/minute
Lap Shear 200 psi (1.38 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 400 %
Specific Gravity 1.35
Tack Free Time 15 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 820 psi (5.66 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

View more

R-1130 Oxime Thixotropic / non-slump N/A 35 Type A Download R-1130 data sheet Non-slump. Adhesive for a variety of substrates on or near electronic components. 485 psi (3.6 MPa), primed (SP-120) lap shear.

Product Details

Property Average Result
Cure System Oxime
Extrusion Rate 70 g/minute
Lap Shear 485 psi (3.34 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 325 %
Flow Rate 0.5 in (12.7 mm)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.1
Tack Free Time 25 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 850 psi (5.86 MPa)
Comment Non-slump. Adhesive for a variety of substrates on or near electronic components. 485 psi (3.6 MPa), primed (SP-120) lap shear.

View more

R-1140 Acetoxy Thixotropic / non-slump N/A 30 Type A Download R-1140 data sheet Non-slump. General all purpose adhesive for a variety of substrates. 625 psi (4.3 MPa), primed (SP-120) lap shear.

Product Details

Property Average Result
Cure System Acetoxy
Lap Shear 625 psi (4.31 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 350 %
Flow Rate 1.5 in (38.1 mm)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.09
Tack Free Time 7 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Non-slump. General all purpose adhesive for a variety of substrates. 625 psi (4.3 MPa), primed (SP-120) lap shear.

View more

R-1400 Platinum Thixotropic / non-slump N/A 19 Type A Download R-1400 data sheet Thixotropic, dispensable, and 0.5mm maximum slump. Shipped and stored frozen.

Product Details

Property Average Result
Cure System Platinum
Viscosity 400,000 cP (400,000 mPa*s)
Extrusion Rate 120 g/minute
Durometer 19 Type A
Appearance Black
Cure 15 minutes / 200 °C
Dielectric Strength 400 volts/mil (15.6 kV/mm)
Elongation 750 %
Mix Ratio 1 PART
Specific Gravity 1.18
Stress at Strain 50 psi / 100 % (0.34 MPa / 100 %)
Tear 110 ppi (19.4 kN/m)
Tensile 825 psi (5.69 MPa)
Comment Thixotropic, dispensable, and 0.5mm maximum slump. Shipped and stored frozen.

View more

R-2141 N/A Flowable / Self Leveling 1.5 hours 40 Type A Download R-2141 data sheet N/A

Product Details

Property Average Result
Viscosity 180,000 cP (180,000 mPa*s)
Durometer 40 Type A
Appearance Translucent
Dielectric Strength 630 volts/mil (24.57 kV/mm)
Elongation 250 %
Flow Rate 0.3 in (7.62 mm)
Specific Gravity 1.1
Tack Free Time 4 hours
Tensile 650 psi (4.48 MPa)
Volatile Content 0.3 %
Work Time 1.5 hours

View more

R-2145 Platinum Flowable / Self Leveling 15 minutes 45 Type A Download R-2145 data sheet Primerless Adhesive;Gray, tough, fast cure adhesive. Will RTV. 145 psi (1.0 MPa), unprimed and 600 psi (4.1 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 180 g/minute
Lap Shear 145 psi (1 MPa)
Durometer 45 Type A
Appearance Dark Gray
Cure 2 hours / 65 °C
Dielectric Strength 825 volts/mil (32.18 kV/mm)
Elongation 400 %
Mix Ratio 1:1
Specific Gravity 1.17
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Tear 150 ppi (26.46 kN/m)
Tensile 1,050 psi (7.24 MPa)
Work Time 15 minutes
Comment Primerless Adhesive;Gray, tough, fast cure adhesive. Will RTV. 145 psi (1.0 MPa), unprimed and 600 psi (4.1 MPa) primed (CF1-135) lap shear.

View more

R-2160 Platinum Flowable / Self Leveling 1.5 hours 20 Type A Download R-2160 data sheet Iron Red, flowable legacy high performance elastomer at elevated temperatures.

Product Details

Property Average Result
Cure System Platinum
Viscosity 280,000 cP (280,000 mPa*s)
Durometer 20 Type A
Appearance Red
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Elongation 625 %
Mix Ratio 10:1
Non Volatile Content 100 %
Operating Temperature -65 °C / 315 °C
Specific Gravity 1.2
Tear 140 ppi (24.69 kN/m)
Tensile 750 psi (5.17 MPa)
Volume Resistivity 100,000,000,000,000 ohmcm
Work Time 1.5 hours
Comment Iron Red, flowable legacy high performance elastomer at elevated temperatures.

View more

R-2186 Platinum Flowable / Self Leveling 2.5 hours 30 Type A Download R-2186 data sheet Legacy general all purpose adhesive. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 83,000 cP (83,000 mPa*s)
Lap Shear 475 psi (3.28 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Dielectric Strength 640 volts/mil (24.96 kV/mm)
Elongation 450 %
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.12
Tear 100 ppi (17.64 kN/m)
Tensile 1,050 psi (7.24 MPa)
Work Time 2.5 hours
Comment Legacy general all purpose adhesive. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

View more

R-2550 Alkoxy Flowable / Self Leveling 6 hours 35 Type A Download R-2550 data sheet Resists breakdown at high temperatures. Translucent and 1 hr. pot life. Not recommended for deep section cures.

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 9,000 cP (9,000 mPa*s)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 175 %
Mix Ratio 100:0.5
Non Volatile Content 100 %
Operating Temperature -115 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.08
Tear 20 ppi (3.53 kN/m)
Tensile 500 psi (3.45 MPa)
Work Time 6 hours
Comment Resists breakdown at high temperatures. Translucent and 1 hr. pot life. Not recommended for deep section cures.

View more

R-2560 Alkoxy Flowable / Self Leveling 1 minutes 55 Type A Download R-2560 data sheet Resists breakdown at high temperatures. Red and 1 hr. pot life. Not recommended for deep section cures.

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 31,000 cP (31,000 mPa*s)
Lap Shear 385 psi (2.66 MPa)
Durometer 55 Type A
Appearance Red
Cure 7 days / RTV
Elongation 125 %
Mix Ratio 100:0.5
Non Volatile Content 100 %
Operating Temperature -115 °C / 260 °C
Specific Gravity 1.41
Tack Free Time 2 hours
Tensile 700 psi (4.83 MPa)
Work Time 1 minutes
Comment Resists breakdown at high temperatures. Red and 1 hr. pot life. Not recommended for deep section cures.

View more

R-2630 Platinum Flowable / Self Leveling 15 hours 60 Type A Download R-2630 data sheet Carbon filled.

Product Details

Property Average Result
Cure System Platinum
Durometer 60 Type A
Appearance Black
Cure 30 minutes / 150 °C
Elongation 95 %
Mix Ratio 10:1
Operating Temperature -65 °C / 200 °C
Specific Gravity 1.1
Tear 40 ppi (7.05 kN/m)
Tensile 690 psi (4.76 MPa)
Volume Resistivity 6 ohmcm
Work Time 15 hours
Comment Carbon filled.

View more

R-2634 Alkoxy Thixotropic / non-slump 3 hours 80 Type A Download R-2634 data sheet 200 psi lap shear primed w/SP-121. Conductive at elevated temperatures.

Product Details

Property Average Result
Cure System Alkoxy
Extrusion Rate 160 g/minute
Lap Shear 200 psi (1.38 MPa)
Durometer 80 Type A
Appearance Gray
Cure 7 days / RTV
Elongation 90 %
Flow Rate 1.2 in (30.48 mm)
Mix Ratio 100:0.5
Specific Gravity 3.41
Tear 50 ppi (8.82 kN/m)
Tensile 250 psi (1.72 MPa)
Volume Resistivity 0 ohmcm
Work Time 3 hours
Comment 200 psi lap shear primed w/SP-121. Conductive at elevated temperatures.

View more

R-2682-12 Platinum N/A N/A N/A Download R-2682-12 data sheet For applications requiring shorter processing times, easy clean-up, and consistent bond thickness. Adheres to silicone, and some metals or plastics. Sheet is 0.013 inches (0.3 mm) and cures on surfaces where the Activator is applied. Cures at room temperature or rapidly with heat.

Product Details

Property Average Result
Cure System Platinum
Lap Shear 100 psi (0.69 MPa)
Appearance Translucent
Application Life 4 minutes
Cure 4 hours / 65 °C
Comment For applications requiring shorter processing times, easy clean-up, and consistent bond thickness. Adheres to silicone, and some metals or plastics. Sheet is 0.013 inches (0.3 mm) and cures on surfaces where the Activator is applied. Cures at room temperature or rapidly with heat.

View more

R1-2145 Platinum Flowable / Self Leveling 1 minutes 45 Type A Download R1-2145 data sheet Primerless Adhesive;Gray tough, fast cure adhesive with 1 hour pot life. Will RTV. 145 psi (1.0 MPa), unprimed and 625 psi (4.3 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 140 g/minute
Lap Shear 145 psi (1 MPa)
Durometer 45 Type A
Appearance Dark Gray
Cure 2 hours / 65 °C
Dielectric Strength 825 volts/mil (32.18 kV/mm)
Elongation 400 %
Mix Ratio 1:1
Specific Gravity 1.16
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Tear 190 ppi (33.51 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 1 minutes
Comment Primerless Adhesive;Gray tough, fast cure adhesive with 1 hour pot life. Will RTV. 145 psi (1.0 MPa), unprimed and 625 psi (4.3 MPa) primed (CF1-135) lap shear.

View more

R31-2186 Platinum Flowable / Self Leveling 15 minutes 20 Type A Download R31-2186 data sheet RTV Primerless Adhesive;Very fast cure.

Product Details

Property Average Result
Cure System Platinum
Viscosity 142,500 cP (142,500 mPa*s)
Extrusion Rate 15 g/minute
Lap Shear 110 psi (0.76 MPa)
Durometer 20 Type A
Appearance Translucent
Cure 24 hours / RTV
Dielectric Strength 905 volts/mil (35.3 kV/mm)
Elongation 775 %
Flow Rate 0.5 in (12.7 mm)
Mix Ratio 1:1
Specific Gravity 1.12
Tear 125 ppi (22.05 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 15 minutes
Comment RTV Primerless Adhesive;Very fast cure.

View more

R32-2186 Platinum Flowable / Self Leveling 15 hours 15 Type A Download R32-2186 data sheet Primerless Adhesive;Heat Cure. Flow 0.5 per 5 minutes. Requires heat to cure. 150 psi (1.0 MPa), unprimed lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 170,000 cP (170,000 mPa*s)
Extrusion Rate 15 g/minute
Lap Shear 150 psi (1.03 MPa)
Durometer 15 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Dielectric Strength 905 volts/mil (35.3 kV/mm)
Elongation 850 %
Flow Rate 0.5 in (12.7 mm)
Mix Ratio 1:1
Specific Gravity 1.12
Stress at Strain 35 psi / 100 % (0.24 MPa / 100 %)
Tear 125 ppi (22.05 kN/m)
Tensile 975 psi (6.72 MPa)
Work Time 15 hours
Comment Primerless Adhesive;Heat Cure. Flow 0.5 per 5 minutes. Requires heat to cure. 150 psi (1.0 MPa), unprimed lap shear.

View more

R33-2186 Platinum Flowable / Self Leveling 2 hours 20 Type A Download R33-2186 data sheet RTV Primerless Adhesive;Fast cure.

Product Details

Property Average Result
Cure System Platinum
Viscosity 124,350 cP (124,350 mPa*s)
Durometer 20 Type A
Appearance Translucent
Cure 24 hours / RTV
Elongation 725 %
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.12
Tear 150 ppi (26.46 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 2 hours
Comment RTV Primerless Adhesive;Fast cure.

View more

R33-2186-1 N/A Flowable / Self Leveling 2 hours 20 Type A Download R33-2186-1 data sheet N/A

Product Details

Property Average Result
Viscosity 80,000 cP (80,000 mPa*s)
Durometer 20 Type A
Appearance White
Elongation 740 %
Specific Gravity 1.12
Tear 135 ppi (23.81 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 2 hours

View more

R4-1140 Acetoxy Flowable / Self Leveling N/A 25 Type A Download R4-1140 data sheet Primerless Adhesive;Self leveling. General all purpose adhesive for a variety of substrates.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 100 g/minute
Durometer 25 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 750 %
Flow Rate 2 in (50.8 mm)
Mix Ratio 1 PART
Specific Gravity 1.12
Stress at Strain 110 psi / N/A (0.76 MPa / N/A)
Tack Free Time 10 minutes
Tear 100 ppi (17.64 kN/m)
Tensile 1,400 psi (9.66 MPa)
Volatile Content 2.4 %
Comment Primerless Adhesive;Self leveling. General all purpose adhesive for a variety of substrates.

View more

SCV-2585 Platinum Flowable / Self Leveling 1 hours 35 Type A Download SCV-2585 data sheet Ultra low Outgassing. Recommended for broad temperature applications. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Viscosity 77,000 cP (77,000 mPa*s)
Lap Shear 475 psi (3.28 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 15 minutes / 150 °C
Elongation 300 %
Mix Ratio 1:1
Specific Gravity 1.11
Tack Free Time 7 hours
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Work Time 1 hours
Comment Ultra low Outgassing. Recommended for broad temperature applications. 475 psi (3.3 MPa), primed (CF1-135) lap shear.

View more

Coatings/Dispersions

Product Cure System Viscosity Non Volatile Content Durometer Data Sheet Comment
CV-1152 Oxime 7,300 cP N/A N/A Download CV-1152 data sheet Soft, very low modulus coating

Product Details

Property Average Result
Viscosity 7,300 cP (7,300 mPa*s)
Appearance Translucent
Tack Free Time 50 minutes
Cure 7 days / RTV
Cure System Oxime
Mix Ratio 1 PART
Refractive Index 1.43
Specific Gravity 1.01
Comment Soft, very low modulus coating

View more

R-1008-0 Oxime 1,300 cP 70 % 23 Type A Download R-1008-0 data sheet N/A

Product Details

Property Average Result
Viscosity 1,300 cP (1,300 mPa*s)
Non Volatile Content 70 %
Appearance Translucent
Dielectric Strength 513 volts/mil (20.01 kV/mm)
Durometer 23 Type A
Elongation 223 %
Tack Free Time 50 minutes
Tensile 235 psi (1.62 MPa)
Thermal Conductivity 0.17 W/(mK)

View more

R-1009 Oxime 6,150 cP 32 % 45 Type A Download R-1009 data sheet High strength coating recommend for coating PCBs and other electronic assemblies.

Product Details

Property Average Result
Viscosity 6,150 cP (6,150 mPa*s)
Non Volatile Content 32 %
Appearance Translucent
Tack Free Time 1.5 hours
Cure 7 days / RTV
Cure System Oxime
Durometer 45 Type A
Elongation 650 %
Specific Gravity 1.1
Tear 95 ppi (16.75 kN/m)
Tensile 1,150 psi (7.93 MPa)
Comment High strength coating recommend for coating PCBs and other electronic assemblies.

View more

R-1077 N/A 3,400 cP 60 % 40 Type A Download R-1077 data sheet N/A

Product Details

Property Average Result
Viscosity 3,400 cP (3,400 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Tack Free Time 20 minutes
Cure 6 days / RTV
Durometer 40 Type A
Elongation 330 %
Tensile 745 psi (5.14 MPa)

View more

R-1082 Acetoxy 700 cP 29 % 25 Type A Download R-1082 data sheet Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

Product Details

Property Average Result
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Appearance Translucent
Cure 5 days / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 950 %
Refractive Index 1.41
Specific Gravity 1.09
Stress at Strain 160 psi / 300 % (1.1 Mpa / 300 %)
Tear 125 ppi (22.05 kN/m)
Tensile 1,425 psi (9.83 MPa)
Comment Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

View more

R-1099 Condensation 6,600 cP 30 % 40 Type A Download R-1099 data sheet N/A

Product Details

Property Average Result
Viscosity 6,600 cP (6,600 mPa*s)
Non Volatile Content 30 %
Appearance Translucent
Tack Free Time 10 minutes
Cure 7 days / RTV
Cure System Condensation
Dielectric Strength 635 volts/mil (24.77 kV/mm)
Durometer 40 Type A
Elongation 570 %
Mix Ratio 1 Part
Tensile 1,050 psi (7.24 MPa)

View more

R-1182 Acetoxy N/A 7 % N/A Download R-1182 data sheet One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

Product Details

Property Average Result
Non Volatile Content 7 %
Appearance Translucent
Cure RTV
Cure System Acetoxy
Comment One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

View more

R-2180 Platinum 3,075 cP 20 % 40 Type A Download R-2180 data sheet High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

Product Details

Property Average Result
Viscosity 3,075 cP (3,075 mPa*s)
Non Volatile Content 20 %
Appearance Translucent
Cure 45 minutes / 75 °C 135 minutes / 150 °C
Cure System Platinum
Durometer 40 Type A
Elongation 1,050 %
Mix Ratio 1:1
Refractive Index 1.41
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Work Time 72 hours
Comment High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

View more

R-2182 Platinum 24 cP 25 % N/A Download R-2182 data sheet Requires minimum heat to cure. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

Product Details

Property Average Result
Viscosity 24 cP (24 mPa*s)
Non Volatile Content 25 %
Appearance Translucent
Cure 5 minutes / RTV
Cure System Platinum
Mix Ratio 1:1
Post Cure 5 minutes / 150 °C
Specific Gravity 0.96
Work Time 24 hours
Comment Requires minimum heat to cure. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

View more

R-3930 Acetoxy 735 cP 60 % 30 Type A Download R-3930 data sheet 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

Product Details

Property Average Result
Viscosity 735 cP (735 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 30 Type A
Elongation 400 %
Specific Gravity 1.36
Tear 40 ppi (7.05 kN/m)
Tensile 750 psi (5.17 MPa)
Comment 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

View more

Electrically Conductive/Static Dissipative

Product Volume Resistivity Viscosity Cure System Durometer Tensile Data Sheet Comment
CV-1500 3 ohmcm N/A Oxime 80 Type A 650 psi Download CV-1500 data sheet Carbon filled, 3 ohmcm, versatile adhesive. Tack Free in 10 minutes.

Product Details

Property Average Result
Volume Resistivity 3 ohmcm
Cure System Oxime
Durometer 80 Type A
Tensile 650 psi (4.48 MPa)
Appearance Black
Cure 7 days / RTV
Elongation 20 %
Flow Rate 0 in
Lap Shear 325 psi (2.24 MPa)
Specific Gravity 1.25
Tack Free Time 10 minutes
Comment Carbon filled, 3 ohmcm, versatile adhesive. Tack Free in 10 minutes.

View more

CV1-2640 25 ohmcm N/A Platinum 40 Type A 525 psi Download CV1-2640 data sheet Carbon filled.

Product Details

Property Average Result
Volume Resistivity 25 ohmcm
Cure System Platinum
Durometer 40 Type A
Tensile 525 psi (3.62 MPa)
Appearance Black
Cure 2 hours / 65 °C
Elongation 225 %
Extrusion Rate 300 g/minute
Mix Ratio 10:1
Specific Gravity 1.07
Comment Carbon filled.

View more

CV3-2640 2,200,000 ohmcm 14,100 cP Platinum 25 Type A 70 psi Download CV3-2640 data sheet Carbon filled. Designed for broad operating temperature.

Product Details

Property Average Result
Volume Resistivity 2,200,000 ohmcm
Viscosity 14,100 cP (14,100 mPa*s)
Cure System Platinum
Durometer 25 Type A
Tensile 70 psi (0.48 MPa)
Appearance Black
Cure 7 days / RTV
Elongation 120 %
Lap Shear 50 psi (0.34 MPa)
Mix Ratio 1:1
Specific Gravity 1.01
Tack Free Time 10 hours
Comment Carbon filled. Designed for broad operating temperature.

View more

R-2631 70 ohmcm N/A Platinum 45 Type A 615 psi Download R-2631 data sheet Carbon filled.

Product Details

Property Average Result
Volume Resistivity 70 ohmcm
Cure System Platinum
Durometer 45 Type A
Tensile 615 psi (4.24 MPa)
Appearance Black
Cure 30 minutes / 150 °C
Elongation 275 %
Extrusion Rate 100 g/minute
Mix Ratio 1:1
Specific Gravity 1.08
Tear 55 ppi (9.7 kN/m)
Comment Carbon filled.

View more

R-2637 0.01 ohmcm N/A Platinum 60 Type A 210 psi Download R-2637 data sheet Electrically Conductive RTV Silicone. Mixes to smooth paste, can be screen printed.

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Cure System Platinum
Durometer 60 Type A
Tensile 210 psi (1.45 MPa)
Appearance Tan
Cure 30 minutes / 150 °C
Dielectric Strength 5 volts/mil (0.2 kV/mm)
Elongation 275 %
Mix Ratio 20:1
Specific Gravity 3.6
Tack Free Time 5 hours
Thermal Conductivity 1.5 W/(mK)
Work Time 4 hours
Comment Electrically Conductive RTV Silicone. Mixes to smooth paste, can be screen printed.

View more

Fluids

Product Substrate Volatile Content Viscosity Data Sheet Comment
FS-3602 Silicone 0.1 % N/A Download FS-3602 data sheet N/A

Product Details

Property Average Result
Volatile Content 0.1 %
Appearance Translucent
Refractive Index 1.39

View more

PLY-7602 N/A N/A N/A Download PLY-7602 data sheet A processing aid or plasticizer for elastomeric systems

Product Details

Property Average Result
Appearance Clear
Cure System Non-Curing
Mix Ratio 1 PART
Non Volatile Content 52%
Rheology Flowable / Self Leveling
Special Feature Phenyl processing aid
Comment A processing aid or plasticizer for elastomeric systems

View more

PLY-7700 N/A 48 % 6 cSt Download PLY-7700 data sheet Low viscosity fluid

Product Details

Property Average Result
Volatile Content 48 %
Viscosity 6 cSt
Appearance Clear
Cure System Non-Curing
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Special Feature Ethoxy functional
Specific Gravity 0.95
Comment Low viscosity fluid

View more

S-7200 Glass / Metal / Plastic 2 % 7,000,000 cP Download S-7200 data sheet 100% Dimethylsiloxane non-reactive polymer. Custom viscosities available.

Product Details

Property Average Result
Viscosity 7,000,000 cP (7,000,000 mPa*s)
Volatile Content 2 %
Specific Gravity 1
Appearance Clear
Dielectric Strength 400 volts/mil (15.6 kV/mm)
Operating Temperature -40 °C / 200 °C
Refractive Index 1.40
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment 100% Dimethylsiloxane non-reactive polymer. Custom viscosities available.

View more

S-7400 Glass / Metal / Plastic 4 % 60,000 cP Download S-7400 data sheet Recommend for extreme temperature (-100°C to 250°C). Higher and custom viscosities available.

Product Details

Property Average Result
Substrate Glass / Metal / Plastic
Volatile Content 4 %
Viscosity 60,000 cP
Appearance Translucent
Dielectric Strength 400 volts/mil (15.6 kV/mm)
Operating Temperature -65 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.1
Volume Resistivity 1,000,000,000,000,000 ohmcm

View more

Foams

Product Foam Density Viscosity Cure System Application Life Appearance Data Sheet Comment
CF1-3710-2 50 lbs/ft3 N/A Platinum N/A Gray Download CF1-3710-2 data sheet Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

Product Details

Property Average Result
Cure System Platinum
Foam Density 50 lbs/ft3 (0.8 g/cm3)
Appearance Gray
Cure 1 minutes / RTV
Extrusion Rate 1 g/minute
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Tack Free Time 10 minutes
Comment Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

View more

CF3-2350 25 lbs/ft³ 90,000 cP Platinum N/A Gray Download CF3-2350 data sheet Useful where stability at higher and lower temperatures is required.

Product Details

Property Average Result
Foam Density 25 lbs/ft³ (0.4 g/cm³)
Viscosity 90,000 cP (90,000 mPa*s)
Cure System Platinum
Appearance Gray
Cure 45 minutes / 100 °C
Cure Type RTV
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Specific Gravity 1.1

View more

CV-2391 20 lbs/ft3 3,000 cP Platinum 6 minutes White Download CV-2391 data sheet Cure in place versatile low outgassing foam, application life 6 minutes

Product Details

Property Average Result
Viscosity 3,000 cP (3,000 mPa*s)
Cure System Platinum
Foam Density 20 lbs/ft3 (0.32 g/cm3)
Application Life 6 minutes
Appearance White
Cure 60 minutes / RTV
Mix Ratio 1:10
Comment Cure in place versatile low outgassing foam, application life 6 minutes

View more

R-2360 12 lbs/ft3 40,000 cP Platinum 2 minutes White Download R-2360 data sheet Flexible cure in place low density foam. Application life 2 minutes.

Product Details

Property Average Result
Viscosity 40,000 cP (40,000 mPa*s)
Cure System Platinum
Foam Density 12 lbs/ft3 (0.19 g/cm3)
Application Life 2 minutes
Appearance White
Cure 20 minutes / RTV
Mix Ratio 1:1
Comment Flexible cure in place low density foam. Application life 2 minutes.

View more

SFM5-2350 25 lbs/ft3 52,500 cP Platinum N/A Black Download SFM5-2350 data sheet Cure in place versatile tough foam. Application life 6 minutes.

Product Details

Property Average Result
Viscosity 52,500 cP (52,500 mPa*s)
Cure System Platinum
Foam Density 25 lbs/ft3 (0.4 g/cm3)
Appearance Black
Cure 33 minutes / 100 °C
Dielectric Strength 190 volts/mil (7.41 kV/mm)
Mix Ratio 1:1
Specific Gravity 1.1
Volume Resistivity 2,200,000,000,000,000 ohmcm
Work Time 23 minutes
Comment Cure in place versatile tough foam. Application life 6 minutes.

View more

Gels

Product Viscosity Penetration Work Time Mix Ratio Data Sheet Comment
EPM-2480 2,500 cP 4 mm 30 hours 1:1 Download EPM-2480 data sheet Soft High Tack Gel

Product Details

Property Average Result
Viscosity 2,500 cP (2,500 mPa*s)
Penetration 4 mm
Work Time 30 hours
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <2 ppm
Mix Ratio 1:1
Volume Resistivity 100,000,000,000,000 ohmcm
Comment Soft High Tack Gel

View more

EPM-2482 1,800 cP 3 mm N/A 1:1 Download EPM-2482 data sheet Soft High Tack Gel;For applications requiring low volatility. Useful for potting intricate assemblies due to a low viscosity. As a low modulus embedding or potting compound for environmental protection of electronic assemblies and components

Product Details

Property Average Result
Viscosity 1,800 cP (1,800 mPa*s)
Penetration 3 mm
Appearance Clear
Cure 40 minutes / 150 °C
Cure System Platinum
Ionic Content Cl <5 ppm
Ionic Content K <1 ppm
Ionic Content Na <4 ppm
Mix Ratio 1:1
Volatile Content 0.3 %
Comment Soft High Tack Gel;For applications requiring low volatility. Useful for potting intricate assemblies due to a low viscosity. As a low modulus embedding or potting compound for environmental protection of electronic assemblies and components

View more

GEL-3500 11,250 cP N/A 12 hours 1:1 Download GEL-3500 data sheet Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

Product Details

Property Average Result
Viscosity 11,250 cP (11,250 mPa*s)
Work Time 12 hours
Appearance Translucent
Cure 45 minutes / 150 °C
Cure System Platinum
Durometer 50 Type 00
Mix Ratio 1:1
Operating Temperature -65 °C / 220 °C
Comment Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

View more

GEL-8100 535 cP N/A N/A 1:1 Download GEL-8100 data sheet N/A

Product Details

Property Average Result
Viscosity 535 cP (535 mPa*s)
Appearance Clear
Cure 1 hours / 100 °C
Mix Ratio 1:1
Specific Gravity 0.98

View more

GEL-8111 535 cP N/A N/A 1:1 Download GEL-8111 data sheet For applications requiring a low viscosity and low volatility soft gel

Product Details

Property Average Result
Appearance Clear
Cure 1 hour / 100°C
Cure System Platinum
Cure Type Heat Cure
Mix Ratio 1:1
Refractive Index 1.40
Rheology Flowable / Self Leveling
Viscosity 535 cP (535 mPa*s)
Volatile Content 0.09 %

View more

GEL-8127 530 cP 8 mm N/A N/A Download GEL-8127 data sheet N/A

Product Details

Property Average Result
Viscosity 530 cP (530 mPa*s)
Penetration 8 mm
Appearance Translucent
Cure 35 minutes / 150 °C

View more

GEL-8136 450 cP 14 mm N/A N/A Download GEL-8136 data sheet N/A

Product Details

Property Average Result
Viscosity 450 cP (450 mPa*s)
Penetration 14 mm
Appearance Clear
Cure 60 minutes / 140 °C

View more

GEL-8150 500 cP 5 mm 4 hours 1:1 Download GEL-8150 data sheet Soft High Tack Gel

Product Details

Property Average Result
Viscosity 500 cP (500 mPa*s)
Penetration 5 mm
Work Time 4 hours
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Refractive Index 1.40
Specific Gravity 0.97
Volatile Content 1 %
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft High Tack Gel

View more

GEL-8170 600 cP 9 mm N/A 1:1 Download GEL-8170 data sheet Very Soft High Tack Gel;Max viscosity after 6 hrs is 2,000 cP

Product Details

Property Average Result
Viscosity 600 cP (600 mPa*s)
Penetration 9 mm
Appearance Translucent
Cure 90 minutes / 80 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Very Soft High Tack Gel;Max viscosity after 6 hrs is 2,000 cP

View more

GEL-8250 650 cP 5 mm 2 hours 1:1 Download GEL-8250 data sheet Soft Med Tack Gel;For applications requiring a broader operating temperature range.

Product Details

Property Average Result
Viscosity 650 cP (650 mPa*s)
Penetration 5 mm
Work Time 2 hours
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -115 °C / 265 °C
Refractive Index 1.43
Specific Gravity 1
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft Med Tack Gel;For applications requiring a broader operating temperature range.

View more

GEL1-8155 14,500 cP 0.4 mm N/A 1:1 Download GEL1-8155 data sheet Soft Low Tack Gel;Viscosity increases ~ 1.5X in 24 hrs (¼” diameter foot, 1.5 seconds)

Product Details

Property Average Result
Viscosity 14,500 cP (14,500 mPa*s)
Penetration 0.4 mm
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Non Volatile Content 100 %
Operating Temperature -65 °C / 200 °C
Refractive Index 1.40
Comment Soft Low Tack Gel;Viscosity increases ~ 1.5X in 24 hrs (¼” diameter foot, 1.5 seconds)

View more

GEL8-8150 500 cP 4 mm 1.5 hours 1:1 Download GEL8-8150 data sheet Soft High Tack Gel

Product Details

Property Average Result
Viscosity 500 cP (500 mPa*s)
Penetration 4 mm
Work Time 1.5 hours
Appearance Clear
Cure 30 minutes / 100 °C
Cure System Platinum
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 0.97
Comment Soft High Tack Gel

View more

LS-3238 1,500 cP N/A 11 hours 1:1 Download LS-3238 data sheet Resistant to hydrocarbon solvents. Index matches Magnesium Fluoride. Potlife based on 3,000 cPs maximum mixed viscosity after 6hrs

Product Details

Property Average Result
Viscosity 1,500 cP (1,500 mPa*s)
Work Time 11 hours
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Durometer 15 Type 00
Mix Ratio 1:1
Operating Temperature -40 °C / 200 °C
Refractive Index 1.38
Specific Gravity 1.28
Volatile Content 0.14 %
Comment Resistant to hydrocarbon solvents. Index matches Magnesium Fluoride. Potlife based on 3,000 cPs maximum mixed viscosity after 6hrs

View more

LS-3441 14,500 cP 0.4 mm N/A 1:1 Download LS-3441 data sheet Soft Low Tack Gel; Tough gel and 24 hr minimum potlife based on 2X initial viscosity

Product Details

Property Average Result
Viscosity 14,500 cP (14,500 mPa*s)
Penetration 0.4 mm
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Refractive Index 1.41
Comment Soft Low Tack Gel; Tough gel and 24 hr minimum potlife based on 2X initial viscosity

View more

LS-3443 650 cP 5 mm N/A 1:1 Download LS-3443 data sheet Soft High Tack Gel;Recommended as an optically robust alter-te to index match to 1.46 substrates;will LTV , 2hr minimum potlife based on 2X initial viscosity

Product Details

Property Average Result
Viscosity 650 cP (650 mPa*s)
Penetration 5 mm
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -115 °C / 265 °C
Refractive Index 1.43
Specific Gravity 1
Volatile Content 0.35 %
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft High Tack Gel;Recommended as an optically robust alter-te to index match to 1.46 substrates;will LTV , 2hr minimum potlife based on 2X initial viscosity

View more

LS1-3252 360 cP N/A N/A N/A Download LS1-3252 data sheet 1.52 Refractive Index firm gel for encapsulating LEDs, and to reduce lightloss for other optical applications.

Product Details

Property Average Result
Viscosity 360 cP (360 mPa*s)
Appearance Clear
Cure 30 minutes / 150 °C
Durometer 25 Type 00
Refractive Index 1.52
Specific Gravity 1.07
Comment 1.52 Refractive Index firm gel for encapsulating LEDs, and to reduce lightloss for other optical applications.

View more

LS1-3443 2,500 cP 6 mm N/A N/A Download LS1-3443 data sheet N/A

Product Details

Property Average Result
Viscosity 2,500 cP (2,500 mPa*s)
Penetration 6 mm
Appearance Clear
Specific Gravity 1

View more

LS3-3354 5,200 cP N/A 80 minutes 1:1 Download LS3-3354 data sheet Soft Gel;Excellent for phosphor coatings.

Product Details

Property Average Result
Viscosity 5,200 cP (5,200 mPa*s)
Work Time 80 minutes
Appearance Clear
Cure 1 minutes / 70 °C
Cure System Platinum
Durometer 60 Type 000
Mix Ratio 1:1
Operating Temperature -40 °C / 200 °C
Refractive Index 1.54
Comment Soft Gel;Excellent for phosphor coatings.

View more

Greases

Product Substrate Volatile Content Viscosity Data Sheet Comment
G-9010 Glass / Metal / Plastic 0.34 % 1,100,000 cP Download G-9010 data sheet A stiff methyl silicone/Teflon grease for high vacuum and pressure systems.

Product Details

Property Average Result
Viscosity 1,100,000 cP (1,100,000 mPa*s)
Specific Gravity 1.14
Volatile Content 0.34 %
Appearance Gray
Flow Rate 2.7 in (68.58 mm)
Operating Temperature -40 °C / 230 °C
Comment A stiff methyl silicone/Teflon grease for high vacuum and pressure systems.

View more

G-9020 Glass / Metal / Plastic 0.3 % 310,000 cP Download G-9020 data sheet A medium consistency methyl silicone grease for high vacuum and pressure systems.

Product Details

Property Average Result
Viscosity 310,000 cP (310,000 mPa*s)
Specific Gravity 1.08
Volatile Content 0.3 %
Appearance Translucent
Operating Temperature -40 °C / 230 °C
Comment A medium consistency methyl silicone grease for high vacuum and pressure systems.

View more

G-9030 Glass / Metal / Plastic 0.3 % 980,100 cP Download G-9030 data sheet A stiff methyl grease used lubricating . 0.3% Weight loss. For high vacuum and pressure systems.

Product Details

Property Average Result
Viscosity 980,100 cP (980,100 mPa*s)
Specific Gravity 1.11
Volatile Content 0.3 %
Appearance Gray
Extrusion Rate 53 g/minute
Operating Temperature -40 °C / 230 °C
Comment A stiff methyl grease used lubricating . 0.3% Weight loss. For high vacuum and pressure systems.

View more

LS-1246 Glass / Metal / Plastic N/A N/A Download LS-1246 data sheet N/A

Product Details

Property Average Result
Specific Gravity 1.1
Appearance Clear
Refractive Index 1.46

View more

Inks

Product Appearance Mix Ratio Non Volatile Content Viscosity Data Sheet Comment
R-1008-1 White 1 PART 70 % 1,150 cP Download R-1008-1 data sheet Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

Product Details

Property Average Result
Cure System Oxime
Viscosity 1,150 cP (1,150 mPa*s)
Non Volatile Content 70 %
Mix Ratio 1 PART
Appearance White
Cure 24 hours / RTV
Tack Free Time 40 minutes
Comment Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

View more

R-1008-2 Black 1 PART 70 % 1,150 cP Download R-1008-2 data sheet Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

Product Details

Property Average Result
Cure System Oxime
Viscosity 1,150 cP (1,150 mPa*s)
Non Volatile Content 70 %
Mix Ratio 1 PART
Appearance Black
Cure 24 hours / RTV
Specific Gravity 1.45
Tack Free Time 40 minutes
Comment Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

View more

R-1008-3 Red 1 PART 70 % 1,150 cP Download R-1008-3 data sheet Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

Product Details

Property Average Result
Cure System Oxime
Viscosity 1,150 cP (1,150 mPa*s)
Non Volatile Content 70 %
Mix Ratio 1 PART
Appearance Red
Cure 24 hours / RTV
Tack Free Time 40 minutes
Comment Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

View more

R-1008-4 Orange 1 PART 70 % 1,150 cP Download R-1008-4 data sheet Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

Product Details

Property Average Result
Cure System Oxime
Viscosity 1,150 cP (1,150 mPa*s)
Non Volatile Content 70 %
Mix Ratio 1 PART
Appearance Orange
Cure 24 hours / RTV
Tack Free Time 40 minutes
Comment Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

View more

R-1008-5 Yellow 1 PART 70 % 1,150 cP Download R-1008-5 data sheet Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

Product Details

Property Average Result
Cure System Oxime
Viscosity 1,150 cP (1,150 mPa*s)
Non Volatile Content 70 %
Mix Ratio 1 PART
Appearance Yellow
Cure 24 hours / RTV
Tack Free Time 40 minutes
Comment Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

View more

R-1008-6 Green 1 PART 70 % 1,150 cP Download R-1008-6 data sheet Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

Product Details

Property Average Result
Cure System Oxime
Viscosity 1,150 cP (1,150 mPa*s)
Non Volatile Content 70 %
Mix Ratio 1 PART
Appearance Green
Cure 24 hours / RTV
Tack Free Time 40 minutes
Comment Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

View more

R-1008-7 Blue 1 PART 70 % 1,150 cP Download R-1008-7 data sheet Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

Product Details

Property Average Result
Cure System Oxime
Viscosity 1,150 cP (1,150 mPa*s)
Non Volatile Content 70 %
Mix Ratio 1 PART
Appearance Blue
Cure 24 hours / RTV
Tack Free Time 40 minutes
Comment Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

View more

R-1008-8 Violet 1 PART 70 % 1,150 cP Download R-1008-8 data sheet Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

Product Details

Property Average Result
Cure System Oxime
Viscosity 1,150 cP (1,150 mPa*s)
Non Volatile Content 70 %
Mix Ratio 1 PART
Appearance Violet
Cure 24 hours / RTV
Tack Free Time 40 minutes
Comment Available in clear (R-1008-0), white (R-1008-1), black (R-1008-2), red (R-1008-3), orange (R-1008-4), yellow (R-1008-5), green (R-1008-6), blue (R-1008-7), and violet (R-1008-8).

View more

R-2100-2 Black 1:1 60 % 900 cP Download R-2100-2 data sheet Available in white (R-2100-1), black (R-2100-2), red (R-2100-3), and green (R-2100-6). Dispersed in xylene.

Product Details

Property Average Result
Cure System Platinum
Viscosity 900 cP (900 mPa*s)
Non Volatile Content 60 %
Mix Ratio 1:1
Appearance Black
Cure 5 minutes / 150 °C
Tack Free Time 24 hours
Comment Available in white (R-2100-1), black (R-2100-2), red (R-2100-3), and green (R-2100-6). Dispersed in xylene.

View more

Liquid Silicone Rubbers

Product Durometer Tensile Elongation Tear Data Sheet Comment
FS-3511 40 Type A 1,150 psi 335 % 60 ppi Download FS-3511 data sheet LSR Fluoro Elastomer;For long term fuel or solvent exposure. Can be liquid injection molded and requires heat to cure. Recommend SP-120 or SP-201

Product Details

Property Average Result
Cure System Platinum
Durometer 40 Type A
Tensile 1,150 psi (7.93 MPa)
Elongation 335 %
Tear 60 ppi (10.58 kN/m)
Appearance Translucent
Cure 30 minutes / 150 °C
Extrusion Rate 35 g/minute
Mix Ratio 1:1
Specific Gravity 1.39
Work Time 24 hours
Comment LSR Fluoro Elastomer;For long term fuel or solvent exposure. Can be liquid injection molded and requires heat to cure. Recommend SP-120 or SP-201

View more

Low Viscosity Elastomers

Product Viscosity Durometer Work Time Tensile Data Sheet Comment
CF1-3510 70,000 cP 20 Type A 7 hours 185 psi Download CF1-3510 data sheet LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

Product Details

Property Average Result
Cure System Platinum
Viscosity 70,000 cP (70,000 mPa*s)
Durometer 20 Type A
Tensile 185 psi (1.28 MPa)
Elongation 135 %
Appearance Red
Mix Ratio 10:1
Specific Gravity 1.44
Work Time 7 hours
Comment LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

View more

CF19-2186 75,000 cP 25 Type A 15 minutes 1,100 psi Download CF19-2186 data sheet Dielectric properties are excellent for actuators and other applications where dielectric properties are critical

Product Details

Property Average Result
Cure System Platinum
Viscosity 75,000 cP (75,000 mPa*s)
Durometer 25 Type A
Tensile 1,100 psi (7.59 MPa)
Elongation 600 %
Appearance Translucent
Cure 30 minutes / 150 °C
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 1.11
Tear 80 ppi (14.11 kN/m)
Work Time 15 minutes
Comment Dielectric properties are excellent for actuators and other applications where dielectric properties are critical

View more

CF19-2615 1,300 cP 30 Type A 4 hours 120 psi Download CF19-2615 data sheet Versatile, clear coating, cure can be heat accelerated.

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,300 cP (1,300 mPa*s)
Durometer 30 Type A
Tensile 120 psi (0.83 MPa)
Elongation 100 %
Appearance Clear
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Refractive Index 1.41
Volume Resistivity 1,000,000,000,000,000 ohmcm
Work Time 4 hours
Comment Versatile, clear coating, cure can be heat accelerated.

View more

CV4-2500 1,500 cP 28 Type A N/A N/A Download CV4-2500 data sheet Low Outgassing clear coating, cure can be heat accelerated.

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,500 cP (1,500 mPa*s)
Durometer 28 Type A
Appearance Clear
Cure 1 hours / 65 °C
Dielectric Strength 670 volts/mil (26.13 kV/mm)
Mix Ratio 1:1
Refractive Index 1.41
Tack Free Time 15 hours
Thermal Conductivity 0.15 W/(mK)
Volume Resistivity 200,000,000,000,000 ohmcm
Comment Low Outgassing clear coating, cure can be heat accelerated.

View more

EPM-2420 2,600 cP 30 Type A N/A 425 psi Download EPM-2420 data sheet Clear, self leveling and good adhesion to various plastics.

Product Details

Property Average Result
Cure System Platinum
Viscosity 2,600 cP (2,600 mPa*s)
Durometer 30 Type A
Tensile 425 psi (2.93 MPa)
Elongation 150 %
Appearance Clear
Cure 1 minutes / 65 °C
Ionic Content Cl <2 ppm
Ionic Content K <1 ppm
Ionic Content Na <8 ppm
Mix Ratio 1:1
Specific Gravity 1.01
Volatile Content 0.85 %
Comment Clear, self leveling and good adhesion to various plastics.

View more

EPM-2421 3,225 cP 50 Type A 3 hours 850 psi Download EPM-2421 data sheet N/A

Product Details

Property Average Result
Viscosity 3,225 cP (3,225 mPa*s)
Durometer 50 Type A
Tensile 850 psi (5.86 MPa)
Elongation 90 %
Appearance Clear
Dielectric Strength 610 volts/mil (23.79 kV/mm)
Lap Shear 250 psi (1.72 MPa)
Specific Gravity 1.02
Tack Free Time 5 hours
Volatile Content 0.70 %
Work Time 3 hours

View more

LS-6140 3,125 cP 50 Type A 3 hours 850 psi Download LS-6140 data sheet RTV; Low volatility

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,125 cP (3,125 mPa*s)
Durometer 50 Type A
Tensile 850 psi (5.86 MPa)
Elongation 90 %
Appearance Clear
Cure 15 minutes / 150 °C
Dielectric Strength 520 volts/mil (20.28 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <2 ppm
Ionic Content Na <4 ppm
Lap Shear 200 psi (1.38 MPa)
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 1.02
Tack Free Time 6 hours
Volume Resistivity 1,100,000,000,000,000 ohmcm
Work Time 3 hours
Comment RTV; Low volatility

View more

LS-6941 5,300 cP 50 Type A 5.5 hours 1,300 psi Download LS-6941 data sheet General use RTV clear adhesive

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,300 cP (5,300 mPa*s)
Durometer 50 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 95 %
Appearance Clear
Cure 15 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.41
Specific Gravity 1.03
Tack Free Time 15 hours
Tear 20 ppi (3.53 kN/m)
Volume Resistivity 1,000,000,000,000,000 ohmcm
Work Time 5.5 hours
Comment General use RTV clear adhesive

View more

LS-6943 5,400 cP 40 Type A N/A 900 psi Download LS-6943 data sheet 1.43 Refractive Index at 589nm. For applications requiring a broader operating temperature range.

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,400 cP (5,400 mPa*s)
Durometer 40 Type A
Tensile 900 psi (6.21 MPa)
Elongation 120 %
Appearance Clear
Cure 60 minutes / 60 °C
Mix Ratio 10:1
Operating Temperature -115 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.03
Comment 1.43 Refractive Index at 589nm. For applications requiring a broader operating temperature range.

View more

LS-6946 37,500 cP 30 Type A 2 hours 675 psi Download LS-6946 data sheet 1.46 Refractive Index at 589nm and contains fumed silica.

Product Details

Property Average Result
Cure System Platinum
Viscosity 37,500 cP (37,500 mPa*s)
Durometer 30 Type A
Tensile 675 psi (4.66 MPa)
Elongation 275 %
Appearance Translucent
Cure 30 minutes / 150 °C
Dielectric Strength 510 volts/mil (19.89 kV/mm)
Lap Shear 510 psi (3.52 MPa)
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.46
Specific Gravity 1.14
Tear 40 ppi (7.05 kN/m)
Volatile Content 0.20 %
Work Time 2 hours
Comment 1.46 Refractive Index at 589nm and contains fumed silica.

View more

LS-8941 21,500 cP 80 Type A 24 hours 1,250 psi Download LS-8941 data sheet Hard and flexible elastomer. Can be casted and liquid injection molded. Requires heat to cure. Recommend SP-120 or SP-201 for overmolding.

Product Details

Property Average Result
Cure System Platinum
Viscosity 21,500 cP (21,500 mPa*s)
Durometer 80 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 65 %
Appearance Clear
Cure 30 minutes / 150 °C
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.07
Tear 55 ppi (9.7 kN/m)
Work Time 24 hours
Comment Hard and flexible elastomer. Can be casted and liquid injection molded. Requires heat to cure. Recommend SP-120 or SP-201 for overmolding.

View more

LS1-6140 3,200 cP 50 Type A N/A 900 psi Download LS1-6140 data sheet Low volatility and requires heat to cure, long pot life for dispensing

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,200 cP (3,200 mPa*s)
Durometer 50 Type A
Tensile 900 psi (6.21 MPa)
Elongation 90 %
Appearance Clear
Cure 60 minutes / 150 °C
Dielectric Strength 530 volts/mil (20.67 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <2.5 ppm
Ionic Content Na <2.5 ppm
Lap Shear 270 psi (1.86 MPa)
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 1.02
Comment Low volatility and requires heat to cure, long pot life for dispensing

View more

LS1-6941 62,500 cP 50 Type A 24 hours 750 psi Download LS1-6941 data sheet Versatile and tough clear elastomer. Requires heat to cure.

Product Details

Property Average Result
Cure System Platinum
Viscosity 62,500 cP (62,500 mPa*s)
Durometer 50 Type A
Tensile 750 psi (5.17 MPa)
Elongation 305 %
Appearance Clear
Cure 30 minutes / 150 °C
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.03
Tear 80 ppi (14.11 kN/m)
Work Time 24 hours
Comment Versatile and tough clear elastomer. Requires heat to cure.

View more

LS2-6140 2,740 cP 50 Type A N/A 1,130 psi Download LS2-6140 data sheet Low Volatility, 1.41 Refractive Index at 589nm. Long pot life and requires heat to cure (80 C). Primerless adhesion to ceramic, plastics and metals. Tested per UL94 and passes V0.

Product Details

Property Average Result
Cure System Platinum
Viscosity 2,740 cP (2,740 mPa*s)
Durometer 50 Type A
Tensile 1,130 psi (7.79 MPa)
Elongation 150 %
Appearance Clear
Cure 60 minutes / 150 °C
Ionic Content Cl <2.5 ppm
Ionic Content K <2.5 ppm
Ionic Content Na <5 ppm
Lap Shear 477 psi (3.29 MPa)
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.03
Volatile Content 1 %
Volume Resistivity 1,100,000,000,000,000 ohmcm
Comment Low Volatility, 1.41 Refractive Index at 589nm. Long pot life and requires heat to cure (80 C). Primerless adhesion to ceramic, plastics and metals. Tested per UL94 and passes V0.

View more

R-2188 11,300 cP 20 Type A 8 hours 475 psi Download R-2188 data sheet Excellent dielectric properties, flexible cure with 14 hr pot life, tested per UL 94 and passed V1.

Product Details

Property Average Result
Cure System Platinum
Viscosity 11,300 cP (11,300 mPa*s)
Durometer 20 Type A
Tensile 475 psi (3.28 MPa)
Elongation 350 %
Appearance Translucent
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Ionic Content Cl <5 ppm
Ionic Content K <3 ppm
Ionic Content Na <1 ppm
Mix Ratio 1:1
Specific Gravity 1.05
Work Time 8 hours
Comment Excellent dielectric properties, flexible cure with 14 hr pot life, tested per UL 94 and passed V1.

View more

R-2613 4,000 cP 45 Type A 2 hours 1,140 psi Download R-2613 data sheet N/A

Product Details

Property Average Result
Cure System Platinum
Viscosity 4,000 cP (4,000 mPa*s)
Durometer 45 Type A
Tensile 1,140 psi (7.86 MPa)
Elongation 150 %
Appearance Clear
Work Time 2 hours

View more

R-2615 5,300 cP 50 Type A 4 hours 1,300 psi Download R-2615 data sheet Self leveling, low temperature cure versatile encapsulant

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,300 cP (5,300 mPa*s)
Durometer 50 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 95 %
Appearance Clear
Cure 15 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.41
Specific Gravity 1.03
Tear 20 ppi (3.53 kN/m)
Volume Resistivity 1,100,000,000,000,000 ohmcm
Work Time 4 hours
Comment Self leveling, low temperature cure versatile encapsulant

View more

R-2615-3 N/A 50 Type A 2 hours 1,000 psi Download R-2615-3 data sheet N/A

Product Details

Property Average Result
Viscosity 4,250 cP
Durometer 50 Type A
Tensile 1,000 psi (6.9 MPa)
Elongation 100 %
Appearance Red
Cure 30 minutes / 150 °C
Dielectric Strength 830 volts/mil (32.37 kV/mm)
Specific Gravity 1.06
Work Time 2 hours

View more

R-2655 5,400 cP 40 Type A N/A 900 psi Download R-2655 data sheet For applications requiring a broader operating temperature range

Product Details

Property Average Result
Cure System Platinum
Viscosity 5,400 cP (5,400 mPa*s)
Durometer 40 Type A
Tensile 900 psi (6.21 MPa)
Elongation 120 %
Appearance Clear
Cure 60 minutes / 100 °C
Mix Ratio 10:1
Operating Temperature -65 °C / 240 °C
Refractive Index 1.43
Specific Gravity 1.03
Comment For applications requiring a broader operating temperature range

View more

R2-6755 45,000 cP 20 Type A N/A 550 psi Download R2-6755 data sheet N/A

Product Details

Property Average Result
Cure System Platinum
Viscosity 45,000 cP (45,000 mPa*s)
Durometer 20 Type A
Tensile 550 psi (3.79 MPa)
Elongation 325 %
Appearance Translucent
Refractive Index 1.46
Specific Gravity 1.14
Stress at Strain 70 psi / 100 % (0.48 MPa / 100 %)
Tack Free Time 1 hours
Tear 25 ppi (4.41 kN/m)
Volatile Content 0.8 %

View more

R21-2615 25,000 cP 75 Type A 2 hours 1,200 psi Download R21-2615 data sheet Hard clear elastomer with 2 hr pot life and LTV cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 25,000 cP (25,000 mPa*s)
Durometer 75 Type A
Tensile 1,200 psi (8.28 MPa)
Elongation 65 %
Appearance Clear
Cure 2 hours / 50 °C
Mix Ratio 1:1
Specific Gravity 1.07
Tear 35 ppi (6.17 kN/m)
Work Time 2 hours
Comment Hard clear elastomer with 2 hr pot life and LTV cure

View more

Pressure Sensitive Adhesives

Product Viscosity Non Volatile Content Data Sheet Comment
CV3-1161 1,300 cP 40 % Download CV3-1161 data sheet Clear silicone PSA for adhering and bonding silicone elastomers, metals, paper, glass, fabric, organic rubbers, some synthetics. Excellent for tapes on films such as polyester or kapton.Rlease force of PSA: 1.5 ppi. Same as CV-1161 with peroxide catalyst to reduce flow at higher temperatures. Recommended where low VOCs are of concern.

Product Details

Property Average Result
Cure System Peroxide
Non Volatile Content 40 %
Appearance White
Cure 20 minutes / 85 °C
Mix Ratio 100:1
Post Cure 20 minutes / 175 °C
Viscosity 1,300 cP (1,300 mPa*s)
Comment Clear silicone PSA for adhering and bonding silicone elastomers, metals, paper, glass, fabric, organic rubbers, some synthetics. Excellent for tapes on films such as polyester or kapton.Rlease force of PSA: 1.5 ppi. Same as CV-1161 with peroxide catalyst to reduce flow at higher temperatures. Recommended where low VOCs are of concern.

View more

PSA-1170 250 cP 50 % Download PSA-1170 data sheet Use for tapes and fasteners for temporarily adhering various substrates including metals, glass, silicone, and organic rubbers.

Product Details

Property Average Result
Cure System Non-Curing
Non Volatile Content 50 %
Appearance Translucent
Cure 90 minutes / 150 °C
Viscosity 250 cP (250 mPa*s)
Comment Use for tapes and fasteners for temporarily adhering various substrates including metals, glass, silicone, and organic rubbers.

View more

PSA-1180 3,300 cP 70 % Download PSA-1180 data sheet N/A

Product Details

Property Average Result
Cure System Non-Curing
Non Volatile Content 70 %
Cure 60 minutes / 85 °C
Viscosity 3,300 cP (3,300 mPa*s)

View more

PSA-1270 2,100 cP 50 % Download PSA-1270 data sheet N/A

Product Details

Property Average Result
Viscosity 2,100 cP (2,100 mPa*s)
Cure 30 minutes / 70 °C
Non Volatile Content 50 %

View more

Primers

Product Non Volatile Content Solvent Data Sheet Comment
CF1-135 4.5 % Naptha Download CF1-135 data sheet Use with addition cure silicones.

Product Details

Property Average Result
Non Volatile Content 4.5 %
Specific Gravity 0.77
Appearance Translucent
Cure System Condensation
Refractive Index 1.41
Comment Use with addition cure silicones.

View more

CF2-135 4.5 % Naptha Download CF2-135 data sheet Use with addition cure silicones.

Product Details

Property Average Result
Non Volatile Content 4.5 %
Specific Gravity 0.77
Appearance Translucent
Cure System Condensation
Comment Use with addition cure silicones.

View more

CF6-135 9 % Naptha Download CF6-135 data sheet Recommended where platinum inhibition is of concern.

Product Details

Property Average Result
Non Volatile Content 9 %
Specific Gravity 0.78
Appearance Translucent
Cure System Condensation
Comment Recommended where platinum inhibition is of concern.

View more

SP-120 4 % Naptha Download SP-120 data sheet Use with addition or condensation cure. Available in Red.

Product Details

Property Average Result
Non Volatile Content 4 %
Specific Gravity 0.77
Appearance Translucent
Cure System Condensation
Lap Shear 315 psi (2.17 MPa)
Comment Use with addition or condensation cure. Available in Red.

View more

SP-121 3.2 % Naptha Download SP-121 data sheet Use with addition or condensation cure.

Product Details

Property Average Result
Non Volatile Content 3.2 %
Specific Gravity 0.76
Appearance Red
Cure System Condensation
Lap Shear 300 psi (2.07 MPa)
Comment Use with addition or condensation cure.

View more

SP-124 10 % Naptha Download SP-124 data sheet Use with addition or condensation cure.

Product Details

Property Average Result
Non Volatile Content 10 %
Specific Gravity 0.79
Appearance Clear
Cure System Condensation
Comment Use with addition or condensation cure.

View more

SP-142 15 % Naptha Download SP-142 data sheet Recommended where platinum inhibition is of concern.

Product Details

Property Average Result
Non Volatile Content 15 %
Specific Gravity 0.79
Appearance Translucent
Cure System Condensation
Comment Recommended where platinum inhibition is of concern.

View more

SP-270 15 % Naptha Download SP-270 data sheet Improved adhesion to gold - Recommended where platinum inhibition is of concern such as when bonding on polyphenylsulphone.

Product Details

Property Average Result
Non Volatile Content 15 %
Specific Gravity 0.8
Appearance Translucent
Cure System Condensation
Lap Shear 166 psi (1.14 MPa)
Refractive Index 1.40
Comment Improved adhesion to gold - Recommended where platinum inhibition is of concern such as when bonding on polyphenylsulphone.

View more

SP-271 20 % Naptha Download SP-271 data sheet Recommended where platinum inhibition is of concern.

Product Details

Property Average Result
Non Volatile Content 20 %
Specific Gravity 0.8
Appearance Translucent
Cure System Condensation
Refractive Index 1.40
Comment Recommended where platinum inhibition is of concern.

View more

Resins

Product Viscosity Durometer Appearance Data Sheet Comment
CF2-4721 130 cP 75 Type D Light Amber Download CF2-4721 data sheet Hard Resin;Contains vinyl-specific peroxide in 1.52 RI resin. Requires heat to cure and oxygen inhibited. Not recommended for general encapsulation.

Product Details

Property Average Result
Viscosity 130 cP (130 mPa*s)
Durometer 75 Type D
Appearance Light Amber
Cure 15 minutes / 150 °C
Cure System Peroxide
Non Volatile Content 100 %
Refractive Index 1.52
Specific Gravity 1.09
Comment Hard Resin;Contains vinyl-specific peroxide in 1.52 RI resin. Requires heat to cure and oxygen inhibited. Not recommended for general encapsulation.

View more

Specialty Polymers

Product Refractive Index Viscosity Mmol % Pt Appearance Data Sheet Comment
CAT-102 N/A N/A N/A N/A White Download CAT-102 data sheet N/A

Product Details

Property Average Result
Appearance White

View more

CAT-41 N/A N/A N/A N/A Translucent Yellow Download CAT-41 data sheet N/A

Product Details

Property Average Result
Appearance Translucent Yellow
Cure >120 °C

View more

CAT-50 1.40 N/A N/A 2.5 Light Amber Download CAT-50 data sheet N/A

Product Details

Property Average Result
Refractive Index 1.40
% Pt 2.5
Appearance Light Amber
Specific Gravity 0.98

View more

CAT-53 1.52 N/A N/A 2 Light Amber Download CAT-53 data sheet N/A

Product Details

Property Average Result
Refractive Index 1.52
% Pt 2
Appearance Light Amber
Specific Gravity 0.98

View more

CF-4721 1.52 125 cP 4.7 Vi/g N/A Clear Download CF-4721 data sheet 75 Type D with Dicumyl Peroxide Catalyst (Catalyst Not Included)

Product Details

Property Average Result
Refractive Index 1.52
Viscosity 125 cP (125 mPa*s)
Mmol 4.7 Vi/g
Appearance Clear
Cure 15 minutes / 150 °C
Durometer 75 Type D
Mix Ratio 100:1
Non Volatile Content 100 %
Specific Gravity 1.1
Volume Resistivity 63,000,000,000,000 ohmcm
Comment 75 Type D with Dicumyl Peroxide Catalyst (Catalyst Not Included)

View more

PLY-7511 1.41 1,000 cSt 1.1 Vi/g N/A Translucent Download PLY-7511 data sheet N/A

Product Details

Property Average Result
Refractive Index 1.41
Viscosity 1,000 cSt (1,006.97 mPa*s)
Mmol 1.1 Vi/g
Appearance Translucent
Specific Gravity 1.01

View more

PLY-7665 1.52 575 cSt 0.8 Vi/g N/A Translucent Download PLY-7665 data sheet N/A

Product Details

Property Average Result
Refractive Index 1.52
Viscosity 575 cSt (619.14 mPa*s)
Mmol 0.8 Vi/g
Appearance Translucent
Specific Gravity 1.08
Volatile Content 0.2 %

View more

XL-110 1.40 4 cSt 7 H/g N/A Translucent Download XL-110 data sheet N/A

Product Details

Property Average Result
Refractive Index 1.40
Viscosity 4 cSt (3.87 mPa*s)
Mmol 7 H/g
Appearance Translucent
Specific Gravity 0.97

View more

XL-112 1.40 40 cSt 6.5 H/g N/A Translucent Download XL-112 data sheet N/A

Product Details

Property Average Result
Refractive Index 1.40
Viscosity 40 cSt (38.68 mPa*s)
Mmol 6.5 H/g
Appearance Translucent
Specific Gravity 0.97

View more

XL-115 1.40 50 cSt 4.2 H/g N/A Translucent Download XL-115 data sheet N/A

Product Details

Property Average Result
Refractive Index 1.40
Viscosity 50 cSt (48.35 mPa*s)
Mmol 4.2 H/g
Appearance Translucent
Specific Gravity 0.97

View more

XL-119 N/A N/A 11.5 Vi/g N/A Clear Download XL-119 data sheet Compatible with a variety of silicone polymer systems for formulating silicone adhesives, elastomers and gels due to its reactivity and solubility with silicone

Product Details

Property Average Result
Appearance Clear
Cure System Non-Curing
Mix Ratio 1 PART
Mmol 11.5 Vi/g

View more

XL-128 N/A N/A N/A N/A Translucent Download XL-128 data sheet N/A

Product Details

Property Average Result
Appearance Translucent
Cure >70 °C

View more

XL-151 1.40 480 cSt 0.4 H/g N/A Translucent Download XL-151 data sheet For crosslinking silicone addition cure polymer systems, to form adhesives, sealant, rubbers and gels due to its reactivity with vinyl functional groups

Product Details

Property Average Result
Refractive Index 1.40
Viscosity 480 cSt
Mmol 0.4 H/g
Appearance Translucent
Cure System Non-Curing
Mix Ratio 1 PART
Volatile Content 0.2 %

View more

XL-7505 1.40 500 cP 0.16 H/g N/A Translucent Download XL-7505 data sheet N/A

Product Details

Property Average Result
Refractive Index 1.40
Viscosity 500 cP (500 mPa*s)
Mmol 0.16 H/g
Appearance Translucent
Volatile Content 1 %

View more

Thermally Conductive

Product Thermal Conductivity Mix Ratio Viscosity Extrusion Rate Cure System Data Sheet Comment
CF1-3800 1.25 W/(mK) 15:1 N/A N/A Platinum Download CF1-3800 data sheet 50% M Fluoro. Recommended for short term exposure to solvents and fuel. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 1.25 W/(mK)
Cure System Platinum
Tensile 125 psi (0.86 MPa)
Appearance White
Cure 30 minutes / 150 °C
Durometer 50 Type A
Elongation 50 %
Mix Ratio 15:1
Specific Gravity 1.53
Work Time 90 minutes
Comment 50% M Fluoro. Recommended for short term exposure to solvents and fuel. (Contains Boron Nitride)

View more

CV-2963 0.64 W/(mK) 20:1 N/A N/A Platinum Download CV-2963 data sheet Primed w/CF1-135, Contains Boron Nitride

Product Details

Property Average Result
Thermal Conductivity 0.64 W/(mK)
Cure System Platinum
Tensile 425 psi (2.93 MPa)
Appearance White
Cure 4 hours / 65 °C
Durometer 60 Type A
Elongation 250 %
Lap Shear 275 psi (1.9 MPa)
Mix Ratio 20:1
Specific Gravity 1.27
Tear 50 ppi (8.82 kN/m)
Work Time 2 hours
Comment Primed w/CF1-135, Contains Boron Nitride

View more

EPM-2490 1.49 W/(mK) 15:1 3,672,800 cP N/A Platinum Download EPM-2490 data sheet 1.5 W/mK, 160 psi lap shear primed w/CF1-135, 2 hr. pot life. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 1.49 W/(mK)
Viscosity 3,672,800 cP (3,672,800 mPa*s)
Cure System Platinum
Tensile 200 psi (1.38 MPa)
Appearance White
Durometer 75 Type A
Elongation 30 %
Flow Rate 0.3 in (7.62 mm)
Ionic Content Cl <3 ppm
Ionic Content K <3 ppm
Ionic Content Na <6 ppm
Lap Shear 160 psi (1.1 MPa)
Mix Ratio 15:1
Specific Gravity 1.53
Tack Free Time 4.5 hours
Tear 50 ppi (8.82 kN/m)
Work Time 2 hours
Comment 1.5 W/mK, 160 psi lap shear primed w/CF1-135, 2 hr. pot life. (Contains Boron Nitride)

View more

EPM1-2493 0.95 W/(mK) 1:1 36,000 cP N/A Platinum Download EPM1-2493 data sheet Recommended for bondlines 5 micron or greater.

Product Details

Property Average Result
Thermal Conductivity 0.95 W/(mK)
Viscosity 36,000 cP (36,000 mPa*s)
Cure System Platinum
Tensile 180 psi (1.24 MPa)
Appearance White
Cure 14 minutes / 150 °C
Dielectric Strength 465 volts/mil (18.14 kV/mm)
Durometer 65 Type A
Elongation 50 %
Ionic Content Cl <5 ppm
Ionic Content K <3 ppm
Ionic Content Na <5 ppm
Lap Shear 120 psi (0.83 MPa)
Mix Ratio 1:1
Specific Gravity 2.34
Tack Free Time 13 hours
Volatile Content 0.35 %
Volume Resistivity 34,000,000,000,000 ohmcm
Comment Recommended for bondlines 5 micron or greater.

View more

G-9340 0.68 W/(mK) N/A N/A N/A Non-Curing Download G-9340 data sheet Versatile, thermally conductive grease where thin bondlines or a compressible grease is needed. Non-curing.

Product Details

Property Average Result
Thermal Conductivity 0.68 W/(mK)
Cure System Non-Curing
Appearance White
Flow Rate 0.2 in (5.08 mm)
Specific Gravity 2.26
Comment Versatile, thermally conductive grease where thin bondlines or a compressible grease is needed. Non-curing.

View more

R-2165 0.5 W/(mK) 1:1 4,000 cP N/A Platinum Download R-2165 data sheet 0.6 W/mK, versatile, moderate thermally conductive silicone. Will RTV.

Product Details

Property Average Result
Thermal Conductivity 0.5 W/(mK)
Viscosity 4,000 cP (4,000 mPa*s)
Cure System Platinum
Tensile 500 psi (3.45 MPa)
Appearance Gray
Cure 10 minutes / 150 °C
Dielectric Strength 700 volts/mil (27.3 kV/mm)
Durometer 60 Type A
Elongation 100 %
Mix Ratio 1:1
Volume Resistivity 1,000,000,000,000,000 ohmcm
Work Time 10 minutes
Comment 0.6 W/mK, versatile, moderate thermally conductive silicone. Will RTV.

View more

R-2175 0.4 W/(mK) 1:1 2,000 cP N/A Platinum Download R-2175 data sheet 0.4 W/mk, pourable, heat resistant, tested per UL94 and passed V0. Will RTV.

Product Details

Property Average Result
Thermal Conductivity 0.4 W/(mK)
Viscosity 2,000 cP (2,000 mPa*s)
Cure System Platinum
Tensile 525 psi (3.62 MPa)
Appearance Black
Cure 60 minutes / 150 °C
Dielectric Strength 580 volts/mil (22.62 kV/mm)
Durometer 50 Type A
Elongation 130 %
Mix Ratio 1:1
Volume Resistivity 43,000,000,000,000 ohmcm
Work Time 1 hours
Comment 0.4 W/mk, pourable, heat resistant, tested per UL94 and passed V0. Will RTV.

View more

R-2930 1.46 W/(mK) 15:1 N/A N/A Platinum Download R-2930 data sheet Smooth Paste;1.45 W/mK, 3 hr. pot life. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 1.46 W/(mK)
Cure System Platinum
Tensile 260 psi (1.79 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 880 volts/mil (34.32 kV/mm)
Durometer 80 Type A
Elongation 20 %
Flow Rate 0.3 inches (7.62 mm)
Mix Ratio 15:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.55
Work Time 3 hours
Comment Smooth Paste;1.45 W/mK, 3 hr. pot life. (Contains Boron Nitride)

View more

R-2939 0.75 W/(mK) 15:1 70,000 cP N/A Platinum Download R-2939 data sheet 0.75 W/mK, 4 hr. pot life. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 0.75 W/(mK)
Viscosity 70,000 cP (70,000 mPa*s)
Cure System Platinum
Tensile 300 psi (2.07 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 810 volts/mil (31.59 kV/mm)
Durometer 70 Type A
Elongation 70 %
Mix Ratio 15:1
Specific Gravity 1.34
Tear 45 ppi (7.94 kN/m)
Work Time 4 hours
Comment 0.75 W/mK, 4 hr. pot life. (Contains Boron Nitride)

View more

R-2940 0.84 W/(mK) 20:1 N/A N/A Platinum Download R-2940 data sheet Smooth Paste;0.8 W/mK, 5 hr. pot life.

Product Details

Property Average Result
Thermal Conductivity 0.84 W/(mK)
Cure System Platinum
Tensile 700 psi (4.83 MPa)
Appearance Gray
Cure 30 minutes / 150 °C
Dielectric Strength 450 volts/mil (17.55 kV/mm)
Durometer 90 Type A
Elongation 35 %
Mix Ratio 20:1
Specific Gravity 2.41
Tack Free Time 24 hours
Tear 65 ppi (11.46 kN/m)
Work Time 5 hours
Comment Smooth Paste;0.8 W/mK, 5 hr. pot life.

View more

R-2949 0.75 W/(mK) 15:1 75,000 cP N/A Platinum Download R-2949 data sheet For applications requiring a broader operating temperature range. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 0.75 W/(mK)
Viscosity 75,000 cP (75,000 mPa*s)
Cure System Platinum
Tensile 275 psi (1.9 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 920 volts/mil (35.88 kV/mm)
Durometer 75 Type A
Elongation 50 %
Mix Ratio 15:1
Specific Gravity 1.37
Tear 45 ppi (7.94 kN/m)
Work Time 3.5 hours
Comment For applications requiring a broader operating temperature range. (Contains Boron Nitride)

View more

SCV1-2599 1.6 W/(mK) 15:1 3,750,000 cP N/A Platinum Download SCV1-2599 data sheet Primed w/CF1-135, Contains Boron Nitride

Product Details

Property Average Result
Thermal Conductivity 1.6 W/(mK)
Viscosity 3,750,000 cP (3,750,000 mPa*s)
Cure System Platinum
Tensile 200 psi (1.38 MPa)
Appearance White
Cure 7 days / RTV
Dielectric Strength 540 volts/mil (21.06 kV/mm)
Durometer 75 Type A
Elongation 30 %
Lap Shear 150 psi (1.03 MPa)
Mix Ratio 15:1
Specific Gravity 1.53
Tear 50 ppi (8.82 kN/m)
Volume Resistivity 530,000,000,000,000 ohmcm
Work Time 2 hours
Comment Primed w/CF1-135, Contains Boron Nitride

View more