Coatings/Dispersions

Product Cure System Viscosity Non Volatile Content Durometer Data Sheet Comment
MED-2214 Platinum 3,700 cP 35 % 35 Type A Download MED-2214 data sheet One Part, Requires heat to cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,700 cP (3,700 mPa*s)
Non Volatile Content 35 %
Durometer 35 Type A
Appearance Translucent
Cure 60 minutes / 50 °C
Elongation 850 %
Mix Ratio 1 Part
Tear 170 ppi (29.98 kN/m)
Tensile 1,700 psi (11.72 MPa)
Comment One Part, Requires heat to cure

View more

MED-6400 Platinum 860 cP 35 % 30 Type A Download MED-6400 data sheet 1.43 R.I. in Xylene

Product Details

Property Average Result
Cure System Platinum
Viscosity 860 cP (860 mPa*s)
Non Volatile Content 35 %
Durometer 30 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Cure Type Heat Cure
Elongation 850 %
Mix Ratio 1:1
Refractive Index 1.43
Rheology Flowable/Self Leveling
Tear 160 ppi (28.22 kN/m)
Tensile 1,600 psi (11.03 MPa)

View more

MED-6600 Platinum 350 cP 35 % 25 Type A Download MED-6600 data sheet 1.46 R.I. in Xylene

Product Details

Property Average Result
Cure System Platinum
Viscosity 350 cP (350 mPa*s)
Non Volatile Content 35 %
Durometer 25 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 800 %
Mix Ratio 1:1
Refractive Index 1.46
Specific Gravity 1.1
Stress at Strain 300 psi / 300 % (2.07 Mpa / 300 %)
Tear 160 ppi (28.22 kN/m)
Tensile 1,200 psi (8.28 MPa)
Work Time 24 hours
Comment 1.46 R.I. in Xylene

View more

MED-6601 N/A N/A N/A 24 Type A Download MED-6601 data sheet 100% solids

Product Details

Property Average Result
Durometer 24 Type A
Appearance Translucent
Elongation 800 %
Stress at Strain 320 psi / 300 % (2.21 Mpa / 300 %)
Tear 150 ppi (26.46 kN/m)
Tensile 1,200 psi (8.28 MPa)
Comment 100% solids

View more

MED-6605 Acetoxy 700 cP 29 % 25 Type A Download MED-6605 data sheet One Part, in Xylene

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Durometer 25 Type A
Appearance Translucent
Cure 5 days / RTV
Elongation 980 %
Mix Ratio 1 PART
Refractive Index 1.40
Specific Gravity 1.09
Stress at Strain 110 psi / 300 % (0.76 Mpa / 300 %)
Tear 120 ppi (21.16 kN/m)
Tensile 1,500 psi (10.34 MPa)
Comment One Part, in Xylene

View more

MED-6615 Platinum 65 cP 32 % 72 Type 00 Download MED-6615 data sheet Silicone adhesive dispersed in heptane, cures rapidly with heat

Product Details

Property Average Result
Cure Type Heat Cure
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 30 minutes / RTV
Cure System Platinum
Durometer 72 Type 00
Elongation 750 %
Non Volatile Content 32 %
Substrate Primerless: Aluminum / Glass / PMMA / Silicone / With Primer: ABS / PEEK / Polycarbonate / Polyimide / Polysulphone / Polyetherimide / Polyurethane / Stainless steel
Tear 120 ppi (21.16 kN/m)
Tensile 1,060 psi (7.31 MPa)
Viscosity 65 cP (65 mPa*s)
Comment Silicone adhesive dispersed in heptane, cures rapidly with heat

View more

MED-6629 Platinum 400 cP 33 % 35 Type A Download MED-6629 data sheet High Strength Silicone Dispersion

Product Details

Property Average Result
Cure System Platinum
Viscosity 400 cP (400 mPa*s)
Non Volatile Content 33 %
Durometer 35 Type A
Appearance Translucent
Cure 75 minutes / 50 °C 60 minutes / 150 °C
Elongation 900 %
Mix Ratio 1:1
Refractive Index 1.46
Stress at Strain 305 psi / 300 % (2.1 Mpa / 300 %)
Tear 310 ppi (54.67 kN/m)
Tensile 1,800 psi (12.41 MPa)
Comment High Strength Silicone Dispersion

View more

MED-6640 Platinum 3,000 cP 20 % 40 Type A Download MED-6640 data sheet Ultra High Tear, in Xylene

Product Details

Property Average Result
Cure System Platinum
Viscosity 3,000 cP (3,000 mPa*s)
Non Volatile Content 20 %
Durometer 40 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 1,000 %
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.41
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Work Time 24 hours
Comment Ultra High Tear, in Xylene

View more

MED-6655 Acetoxy 700 cP 60 % 35 Type A Download MED-6655 data sheet 100M% Fluorosilicone

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 60 %
Durometer 35 Type A
Appearance White
Cure 3 days / RTV
Cure Type RTV
Elongation 425 %
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Tack Free Time 80 minutes
Tear 45 ppi (7.94 kN/m)
Tensile 775 psi (5.34 MPa)
Comment 100M% Fluorosilicone

View more

MED-6670 Platinum N/A 25 % N/A Download MED-6670 data sheet Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Platinum
Non Volatile Content 25 %
Appearance Translucent
Cure 5 minutes / RTV
Mix Ratio 1:1
Specific Gravity 0.96
Work Time 24 hours
Comment Low Coefficient of Friction Coating

View more

MED-6671 Acetoxy N/A N/A N/A Download MED-6671 data sheet RTV, Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Acetoxy
Appearance Translucent
Cure 24 hours / RTV
Mix Ratio 1 Part
Comment RTV, Low Coefficient of Friction Coating

View more

MED1-4161 Condensation 140 cSt 33 % 25 Type 00 Download MED1-4161 data sheet 25 '00' durometer lubricious coating

Product Details

Property Average Result
Cure System Condensation
Viscosity 140 cSt (121.43 mPa*s)
Non Volatile Content 33 %
Durometer 25 Type 00
Appearance Clear
Cure 5 days / 25 °C
Mix Ratio 1 Part
Solvent Xylene
Specific Gravity 0.87
Comment 25 '00' durometer lubricious coating

View more

MED6-6606 Acetoxy 95 cP 30 % 20 Type A Download MED6-6606 data sheet Silicone adhesive dispersed in heptane

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 3 days / RTV
Cure System Acetoxy
Durometer 20 Type A
Elongation 800 %
Non Volatile Content 30 %
Specific Gravity 1.11
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate / Stainless steel
Tear 115 ppi (20.28 kN/m)
Tensile 1,190 psi (8.21 MPa)
Viscosity 95 cP (95 mPa*s)
Comment Silicone adhesive dispersed in heptane

View more

Foams

Product Foam Density Viscosity Cure System Application Life Appearance Data Sheet Comment
MED-2310 N/A 40,000 cP Platinum 2 minutes White Download MED-2310 data sheet Low Density

Product Details

Property Average Result
Viscosity 40,000 cP (40,000 mPa*s)
Cure System Platinum
Application Life 2 minutes
Appearance White
Mix Ratio 1:1
Comment Low Density

View more

Gels

Product Viscosity Penetration Work Time Mix Ratio Data Sheet Comment
MED-6311 500 cP 2.6 mm N/A 1:1 Download MED-6311 data sheet Low penetration, high strength gel

Product Details

Property Average Result
Penetration 2.6 mm
Viscosity 500 cP (500 mPa*s)
Mix Ratio 1:1
Appearance Clear
Cure 3.5 hours / 160 °C
Specific Gravity 0.97
Volatile Content 0.1 %
Comment Low penetration, high strength gel

View more

MED1-6300 1,000 cP 5 mm N/A 1:1 Download MED1-6300 data sheet Medium penetration, soft responsive gel

Product Details

Property Average Result
Penetration 5 mm
Viscosity 1,000 cP (1,000 mPa*s)
Mix Ratio 1:1
Appearance Translucent
Cure 5 hours / 140 °C
Cure System Platinum
Non Volatile Content 99.9 %
Specific Gravity 0.98
Volatile Content 0.1 %
Comment Medium penetration, soft responsive gel

View more

MED2-6300 1,000 cP 10 mm N/A 1:1 Download MED2-6300 data sheet Low penetration, firm cohesive gel

Product Details

Property Average Result
Penetration 10 mm
Viscosity 1,000 cP (1,000 mPa*s)
Mix Ratio 1:1
Appearance Translucent
Cure 5 hours / 140 °C
Cure System Platinum
Non Volatile Content 99.9 %
Refractive Index 1.40
Specific Gravity 0.97
Volatile Content 0.1 %
Comment Low penetration, firm cohesive gel

View more

MED3-6300 1,000 cP 15 mm N/A 3:1 Download MED3-6300 data sheet High penetration, soft responsive gel

Product Details

Property Average Result
Penetration 15 mm
Viscosity 1,000 cP (1,000 mPa*s)
Mix Ratio 3:1
Appearance Translucent
Cure 5 hours / 140 °C
Cure System Platinum
Specific Gravity 0.97
Volatile Content 0.1 %
Comment High penetration, soft responsive gel

View more

MED3-6311 500 cP 2.6 mm N/A 3:1 Download MED3-6311 data sheet High Purity, Low Penetration, High Strength Gel

Product Details

Property Average Result
Penetration 2.6 mm
Viscosity 500 cP (500 mPa*s)
Mix Ratio 3:1
Appearance Translucent
Cure 3.5 hours / 160 °C
Cure System Platinum
Non Volatile Content 99.9 %
Specific Gravity 0.97
Volatile Content 0.1 %
Comment High Purity, Low Penetration, High Strength Gel

View more

Low Viscosity Elastomers

Product Viscosity Durometer Work Time Tensile Data Sheet Comment
MED-4211 97,800 cP 25 Type A N/A 685 psi Download MED-4211 data sheet Flowable

Product Details

Property Average Result
Durometer 25 Type A
Viscosity 97,800 cP (97,800 mPa*s)
Tensile 685 psi (4.72 MPa)
Appearance Translucent
Cure 3 minutes / 150 °C
Cure System Platinum
Elongation 530 %
Mix Ratio 10:1
Post Cure 1 hour / 150 °C
Specific Gravity 1.1
Comment Flowable

View more

MED-4244 130,000 cP 40 Type A 4 hours 865 psi Download MED-4244 data sheet Flowable, Medium Durometer

Product Details

Property Average Result
Durometer 40 Type A
Viscosity 130,000 cP (130,000 mPa*s)
Work Time 4 hours
Tensile 865 psi (5.97 MPa)
Appearance Translucent
Cure 3 minutes / 177 °C
Cure System Platinum
Elongation 350 %
Mix Ratio 10:1
Post Cure 1 hour / 150 °C
Specific Gravity 1.1
Stress at Strain 480 psi / 200 % (3.31 MPa / 200 %)
Tear 150 ppi (26.46 kN/m)
Comment Flowable, Medium Durometer

View more

MED-4286 6,350 cP 55 Type 000 17.5 hours 45 psi Download MED-4286 data sheet Ultra Soft Elastomer

Product Details

Property Average Result
Viscosity 6,350 cP (6,350 mPa*s)
Durometer 55 Type 000
Work Time 17.5 hours
Tensile 45 psi (0.31 MPa)
Cure 45 minutes / 150 °C
Cure System Platinum
Cure Type Heat Cure
Elongation 475 %
Mix Ratio 1:1
Stress at Strain 8 psi / 200 % (0.06 MPa / 200 %)

View more

MED-6210 16,000 cP 50 Type A 4 hours 930 psi Download MED-6210 data sheet Clear, 1.43 R.I.

Product Details

Property Average Result
Durometer 50 Type A
Viscosity 16,000 cP (16,000 mPa*s)
Work Time 4 hours
Tensile 930 psi (6.41 MPa)
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Elongation 140 %
Mix Ratio 1:1
Refractive Index 1.43
Specific Gravity 1.05
Tear 35 ppi (6.17 kN/m)
Comment Clear, 1.43 R.I.

View more

MED-6215 3,800 cP 50 Type A 5 hours 1,250 psi Download MED-6215 data sheet Clear, 1.41 R.I.

Product Details

Property Average Result
Durometer 50 Type A
Viscosity 3,800 cP (3,800 mPa*s)
Work Time 5 hours
Tensile 1,250 psi (8.62 MPa)
Appearance Clear
Cure 15 minutes / 150 °C
Cure System Platinum
Elongation 100 %
Mix Ratio 10:1
Specific Gravity 1.03
Tack Free Time 16 hours
Comment Clear, 1.41 R.I.

View more

MED-6219 25,500 cP 75 Type A 2.5 hours 1,300 psi Download MED-6219 data sheet Clear, 1.41 R.I., Low Viscosity, High Durometer

Product Details

Property Average Result
Durometer 75 Type A
Viscosity 25,500 cP (25,500 mPa*s)
Work Time 2.5 hours
Tensile 1,300 psi (8.97 MPa)
Appearance Clear
Cure 2 hours / 50 °C
Cure System Platinum
Elongation 65 %
Mix Ratio 1:1
Specific Gravity 1.07
Tear 35 ppi (6.17 kN/m)
Comment Clear, 1.41 R.I., Low Viscosity, High Durometer

View more

MED-6233 73,500 cP 50 Type A 52 hours 740 psi Download MED-6233 data sheet Clear, 1.41 R.I.

Product Details

Property Average Result
Durometer 50 Type A
Viscosity 73,500 cP (73,500 mPa*s)
Work Time 52 hours
Tensile 740 psi (5.1 MPa)
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Elongation 380 %
Mix Ratio 1:1
Refractive Index 1.41
Specific Gravity 1.04
Tear 80 ppi (14.11 kN/m)
Comment Clear, 1.41 R.I.

View more

MED-6820 66,000 cP 40 Type A 4.5 hours 670 psi Download MED-6820 data sheet 1.43 R.I., Optically Clear

Product Details

Property Average Result
Durometer 40 Type A
Viscosity 66,000 cP (66,000 mPa*s)
Work Time 4.5 hours
Tensile 670 psi (4.62 MPa)
Appearance Clear
Cure 30 minutes / 150 °C
Cure System Platinum
Elongation 210 %
Mix Ratio 1:1
Refractive Index 1.43
Specific Gravity 1.43
Tear 40 ppi (7.05 kN/m)
Comment 1.43 R.I., Optically Clear

View more

MED2-4420 22,000 cP 20 Type A 3 minutes 585 psi Download MED2-4420 data sheet Low Viscosity, Rapid RTV Cure

Product Details

Property Average Result
Durometer 20 Type A
Viscosity 22,000 cP (22,000 mPa*s)
Work Time 3 minutes
Tensile 585 psi (4.03 MPa)
Appearance Translucent
Cure 15 minutes / 150 °C
Cure System Platinum
Elongation 500 %
Mix Ratio 1:1
Specific Gravity 1.07
Comment Low Viscosity, Rapid RTV Cure

View more

MED3-4420 91,250 cP 23 Type A 15 minutes 1,000 psi Download MED3-4420 data sheet Flowable

Product Details

Property Average Result
Durometer 23 Type A
Viscosity 91,250 cP (91,250 mPa*s)
Work Time 15 minutes
Tensile 1,000 psi (6.9 MPa)
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Elongation 600 %
Mix Ratio 1:1
Specific Gravity 1.11
Tear 75 ppi (13.23 kN/m)
Comment Flowable

View more

MED4-4420 24,000 cP 17 Type A 35 minutes 700 psi Download MED4-4420 data sheet RTV

Product Details

Property Average Result
Durometer 17 Type A
Viscosity 24,000 cP (24,000 mPa*s)
Work Time 35 minutes
Tensile 700 psi (4.83 MPa)
Appearance Translucent
Cure 15 minutes / 150 °C
Cure System Platinum
Elongation 600 %
Mix Ratio 1:1
Tear 35 ppi (6.17 kN/m)
Comment RTV

View more