Product Durometer Tensile Elongation Tear Data Sheet Comment
MED-4801 38 Type 00 290 psi 1140 % 55 ppi Download MED-4801 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 38 Type 00
Tensile 290 psi (2 MPa)
Elongation 1140 %
Tear 55 ppi (9.7 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure System Platinum
Extrusion Rate 200 g/minute
Mix Ratio 1:1
Work Time 24 hours
Comment Injection Molding Elastomer

View more

MED-4805 7 Type A 485 psi 1080 % 70 ppi Download MED-4805 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 7 Type A
Tensile 485 psi (3.34 MPa)
Elongation 1080 %
Tear 70 ppi (12.35 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure System Platinum
Extrusion Rate 55 g/minute
Mix Ratio 1:1
Specific Gravity 1.09
Work Time 50 hours
Comment Injection Molding Elastomer

View more

MED-4810 11 Type A 700 psi 1075 % 65 ppi Download MED-4810 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 11 Type A
Tensile 700 psi (4.83 MPa)
Elongation 1075 %
Tear 65 ppi (11.46 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure System Platinum
Extrusion Rate 100 g/minute
Mix Ratio 1:1
Specific Gravity 1.1
Stress at Strain 45 psi / 200 % (0.31 MPa / 200 %)
Work Time 70 hours
Comment Injection Molding Elastomer

View more

MED-4820 20 Type A 910 psi 875 % 125 ppi Download MED-4820 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 20 Type A
Tensile 910 psi (6.28 MPa)
Elongation 875 %
Tear 125 ppi (22.05 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure System Platinum
Extrusion Rate 75 g/minute
Mix Ratio 1:1
Specific Gravity 1.14
Stress at Strain 65 psi / 200 % (0.45 MPa / 200 %)
Work Time 72 hours
Comment Injection Molding Elastomer

View more

MED-4830 30 Type A 1,350 psi 750 % 150 ppi Download MED-4830 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,350 psi (9.31 MPa)
Elongation 750 %
Tear 150 ppi (26.46 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure System Platinum
Extrusion Rate 175 g/minute
Mix Ratio 1:1
Specific Gravity 1.13
Stress at Strain 175 psi / 200 % (1.21 MPa / 200 %)
Comment Injection Molding Elastomer

View more

MED-4840 43 Type A 1,190 560 % 245 ppi Download MED-4840 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 43 Type A
Tensile 1,190 psi (8.2 MPa)
Elongation 560 %
Tear 245 ppi (43.21 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure System Platinum
Cure Type Heat Cure
Extrusion Rate 225 g/minute
Mix Ratio 1:1
Rheology Thixotropic / Non-slump
Specific Gravity 1.12
Stress at Strain 450 psi / 200 % (3.1 MPa / 200 %)

View more

MED-4842 44 Type A 1,070 psi 400 % 250 ppi Download MED-4842 data sheet Injection Molding Elastomer, Resists Blocking

Product Details

Property Average Result
Durometer 44 Type A
Tensile 1,070 psi (7.38 MPa)
Elongation 400 %
Tear 250 ppi (44.09 kN/m)
Appearance White
Cure 10 minutes / 150 °C
Cure System Platinum
Extrusion Rate 215 g/minute
Mix Ratio 1:1
Specific Gravity 1.17
Stress at Strain 540 psi / 200 % (3.72 MPa / 200 %)
Comment Injection Molding Elastomer, Resists Blocking

View more

MED-4850 50 Type A 1,475 psi 675 % 240 ppi Download MED-4850 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,475 psi (10.17 MPa)
Elongation 675 %
Tear 240 ppi (42.33 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure System Platinum
Extrusion Rate 100 g/minute
Mix Ratio 1:1
Specific Gravity 1.14
Stress at Strain 400 psi / 200 % (2.76 MPa / 200 %)
Work Time 72 hours
Comment Injection Molding Elastomer

View more

MED-4860 60 Type A 1,350 psi 530 % 255 ppi Download MED-4860 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 60 Type A
Tensile 1,350 psi (9.31 MPa)
Elongation 530 %
Tear 255 ppi (44.97 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure System Platinum
Extrusion Rate 85 g/minute
Mix Ratio 1:1
Specific Gravity 1.15
Stress at Strain 600 psi / 200 % (4.14 MPa / 200 %)
Work Time 72 hours
Comment Injection Molding Elastomer

View more

MED-4870 70 Type A 1,500 psi 415 % 230 ppi Download MED-4870 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 70 Type A
Tensile 1,500 psi (10.34 MPa)
Elongation 415 %
Tear 230 ppi (40.56 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure System Platinum
Extrusion Rate 60 g/minute
Mix Ratio 1:1
Specific Gravity 1.16
Stress at Strain 750 psi / 200 % (5.17 MPa / 200 %)
Work Time 72 hours
Comment Injection Molding Elastomer

View more

MED-4880 80 Type A 1,030 psi 265 % 90 ppi Download MED-4880 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 80 Type A
Tensile 1,030 psi (7.1 MPa)
Elongation 265 %
Tear 90 ppi (15.87 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure System Platinum
Extrusion Rate 110 g/minute
Mix Ratio 1:1
Specific Gravity 1.16
Stress at Strain 650 psi / 100 % (4.48 MPa / 100 %)
Work Time 70 hours
Comment Injection Molding Elastomer

View more

MED-5440 30 Type A 1,250 psi 380 % 60 ppi Download MED-5440 data sheet 100M% Fluorosilicone Injection Molding Elastomer

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 380 %
Tear 60 ppi (10.58 kN/m)
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Extrusion Rate 40 g/minute
Mix Ratio 1:1
Specific Gravity 1.38
Comment 100M% Fluorosilicone Injection Molding Elastomer

View more

MED-5820 19 Type A 1,080 psi 890 % 90 ppi Download MED-5820 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 19 Type A
Tensile 1,080 psi (7.45 MPa)
Elongation 890 %
Tear 90 ppi (15.87 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Extrusion Rate 220 g/minute
Specific Gravity 1.08
Stress at Strain 90 psi / 200 % (0.62 MPa / 200 %)
Comment Injection Molding Elastomer

View more

MED-5830 30 Type A 1,340 psi 830 % 150 ppi Download MED-5830 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,340 psi (9.24 MPa)
Elongation 830 %
Tear 150 ppi (26.46 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure System Platinum
Extrusion Rate 145 g/minute
Specific Gravity 1.11
Stress at Strain 160 psi / 200 % (1.1 MPa / 200 %)
Comment Injection Molding Elastomer

View more

MED-5840 40 Type A 1,350 psi 680 % 160 ppi Download MED-5840 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 40 Type A
Tensile 1,350 psi (9.31 MPa)
Elongation 680 %
Tear 160 ppi (28.22 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Extrusion Rate 115 g/minute
Specific Gravity 1.12
Stress at Strain 300 psi / 200 % (2.07 Mpa / 200 %)
Comment Injection Molding Elastomer

View more

MED-5850 50 Type A 1,450 psi 550 % 190 ppi Download MED-5850 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,450 psi (10 MPa)
Elongation 550 %
Tear 190 ppi (33.51 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Extrusion Rate 75 g/minute
Specific Gravity 1.14
Stress at Strain 400 psi / 200 % (2.76 MPa / 200 %)
Comment Injection Molding Elastomer

View more

MED-5860 60 Type A 1,300 psi 425 % 200 ppi Download MED-5860 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 60 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 425 %
Tear 200 ppi (35.27 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Extrusion Rate 75 g/minute
Specific Gravity 1.14
Stress at Strain 700 psi / 200 % (4.83 MPa / 200 %)
Comment Injection Molding Elastomer

View more

MED-5870 68 Type A 1,250 psi 400 % 225 ppi Download MED-5870 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 68 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 400 %
Tear 225 ppi (39.68 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure System Platinum
Extrusion Rate 100 g/minute
Specific Gravity 1.14
Stress at Strain 900 psi / 200 % (6.21 MPa / 200 %)
Comment Injection Molding Elastomer

View more

MED1-4855 55 Type A 1,100 psi 475 % 240 ppi Download MED1-4855 data sheet Self-Lubricating Injection Molding Elastomer, High Lubrication

Product Details

Property Average Result
Durometer 55 Type A
Tensile 1,100 psi (7.59 MPa)
Elongation 475 %
Tear 240 ppi (42.33 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure System Platinum
Extrusion Rate 230 g/minute
Mix Ratio 1:1
Specific Gravity 1.15
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Comment Self-Lubricating Injection Molding Elastomer, High Lubrication

View more

MED50-5338 30 Type A 650 psi 350 % 37 ppi Download MED50-5338 data sheet 50M% Fluorosilicone Injection Molding Elastomer

Product Details

Property Average Result
Durometer 30 Type A
Tensile 650 psi (4.48 MPa)
Elongation 350 %
Tear 37 ppi (6.53 kN/m)
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Extrusion Rate 115 g/minute
Mix Ratio 1:1
Specific Gravity 1.25
Stress at Strain 300 psi / 200 % (2.07 Mpa / 200 %)
Work Time 16 hours
Comment 50M% Fluorosilicone Injection Molding Elastomer

View more