High Consistency Rubbers

Product Durometer Tensile Elongation Tear Data Sheet Comment
MED-2174 50 Type A 1,300 psi 750 % 225 ppi Download MED-2174 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 750 %
Tear 225 ppi (39.68 kN/m)
Appearance Clear
Cure 5 minutes / 116 °C
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 4 hours / 205 °C
Specific Gravity 1.15
Stress at Strain 325 psi / 200 % (2.24 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4520 28 Type A 1,320 psi 950 % 135 ppi Download MED-4520 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 28 Type A
Tensile 1,320 psi (9.1 MPa)
Elongation 950 %
Tear 135 ppi (23.81 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 177 °C
Specific Gravity 1.1
Stress at Strain 105 psi / 200 % (0.72 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4535 35 Type A 1,300 psi 800 % 125 ppi Download MED-4535 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 35 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 800 %
Tear 125 ppi (22.05 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 177 °C
Specific Gravity 1.1
Stress at Strain 185 psi / 200 % (1.28 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4550 50 Type A 1,400 psi 750 % 195 ppi Download MED-4550 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,400 psi (9.66 MPa)
Elongation 750 %
Tear 195 ppi (34.39 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 177 °C
Specific Gravity 1.16
Stress at Strain 250 psi / 200 % (1.72 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4565 65 Type A 1,250 psi 700 % 200 ppi Download MED-4565 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 65 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 700 %
Tear 200 ppi (35.27 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 177 °C
Specific Gravity 1.21
Stress at Strain 375 psi / 200 % (2.59 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4714 15 Type A 715 psi 1385 % 155 ppi Download MED-4714 data sheet Low Durometer

Product Details

Property Average Result
Durometer 15 Type A
Tensile 715 psi (4.93 MPa)
Elongation 1385 %
Tear 155 ppi (27.34 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.08
Stress at Strain 40 psi / 200 % (0.28 MPa / 200 %)
Work Time 26 hours
Comment Low Durometer

View more

MED-4719 55 Type A 1,320 psi 665 % 220 ppi Download MED-4719 data sheet Excellent adhesion and fatigue resistance

Product Details

Property Average Result
Durometer 55 Type A
Tensile 1,320 psi (9.1 MPa)
Elongation 665 %
Tear 220 ppi (38.8 kN/m)
Appearance Translucent
Cure 10 minutes / 171 °C
Cure System Platinum
Cure Type Heat Cure
Mix Ratio 1:1
Specific Gravity 1.23
Stress at Strain 280 psi / 200 % (1.9 MPa / 200 %)
Work Time 8 hours
Comment Excellent adhesion and fatigue resistance

View more

MED-4720 25 Type A 1,390 psi 1240 % 190 ppi Download MED-4720 data sheet High Tear

Product Details

Property Average Result
Durometer 25 Type A
Tensile 1,390 psi (9.59 MPa)
Elongation 1240 %
Tear 190 ppi (33.51 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.1
Stress at Strain 75 psi / 200 % (0.52 MPa / 200 %)
Work Time 10 hours
Comment High Tear

View more

MED-4725 30 Type A 1,395 psi 890 % 135 ppi Download MED-4725 data sheet Low Tension Set

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,395 psi (9.62 MPa)
Elongation 890 %
Tear 135 ppi (23.81 kN/m)
Appearance Translucent
Cure 10 minutes / 171 °C
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 110 psi / 200 % (0.76 MPa / 200 %)
Work Time 2 hours
Comment Low Tension Set

View more

MED-4727 30 Type A 2,300 psi 1050 % 235 ppi Download MED-4727 data sheet High Strength, Low Modulus

Product Details

Property Average Result
Durometer 30 Type A
Tensile 2,300 psi (15.86 MPa)
Elongation 1050 %
Tear 235 ppi (41.45 kN/m)
Appearance Translucent
Cure 10 minutes / 171 °C
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 100 psi / 200 % (0.69 MPa / 200 %)
Work Time 2.5 hours
Comment High Strength, Low Modulus

View more

MED-4735 35 Type A 1,535 psi 1055 % 195 ppi Download MED-4735 data sheet High Tear

Product Details

Property Average Result
Durometer 35 Type A
Tensile 1,535 psi (10.59 MPa)
Elongation 1055 %
Tear 195 ppi (34.39 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 180 psi / 200 % (1.24 MPa / 200 %)
Work Time 2 hours
Comment High Tear

View more

MED-4750 50 Type A 1,545 psi 1050 % 270 ppi Download MED-4750 data sheet High Tear

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,545 psi (10.66 MPa)
Elongation 1050 %
Tear 270 ppi (47.62 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.16
Stress at Strain 300 psi / 300 % / 200 % (2.07 Mpa / 300 % / 200 %)
Work Time 2.5 hours
Comment High Tear

View more

MED-4755 55 Type A 1,640 psi 875 % 310 ppi Download MED-4755 data sheet Ultra-high Tear

Product Details

Property Average Result
Durometer 55 Type A
Tensile 1,640 psi (11.31 MPa)
Elongation 875 %
Tear 310 ppi (54.67 kN/m)
Appearance Translucent
Cure 10 minutes / 138 °C
Cure System Platinum
Mix Ratio 1:1
Post Cure 4 hours / 177 °C
Specific Gravity 1.14
Stress at Strain 490 psi / 200 % (3.38 MPa / 200 %)
Work Time 2.5 hours
Comment Ultra-high Tear

View more

MED-4765 65 Type A 1,240 psi 1005 % 265 ppi Download MED-4765 data sheet High Tear

Product Details

Property Average Result
Durometer 65 Type A
Tensile 1,240 psi (8.55 MPa)
Elongation 1005 %
Tear 265 ppi (46.74 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.2
Stress at Strain 355 psi / 200 % (2.45 MPa / 200 %)
Work Time 6 hours
Comment High Tear

View more

MED-4770 70 Type A 1,415 psi 760 % 300 ppi Download MED-4770 data sheet Abrasion / Fatigue Resistant

Product Details

Property Average Result
Durometer 70 Type A
Tensile 1,415 psi (9.76 MPa)
Elongation 760 %
Tear 300 ppi (52.91 kN/m)
Appearance Translucent
Cure 10 minutes / 138 °C
Cure System Platinum
Mix Ratio 1:1
Post Cure 4 hours / 177 °C
Specific Gravity 1.19
Stress at Strain 595 psi / 200 % (4.1 MPa / 200 %)
Work Time 2.5 hours
Comment Abrasion / Fatigue Resistant

View more

MED-4780 80 Type A 1,155 psi 740 % 225 ppi Download MED-4780 data sheet High Tear

Product Details

Property Average Result
Durometer 80 Type A
Tensile 1,155 psi (7.97 MPa)
Elongation 740 %
Tear 225 ppi (39.68 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.2
Stress at Strain 450 psi / 200 % (3.1 MPa / 200 %)
Work Time 8.5 hours
Comment High Tear

View more

MED4-4515 50 Type A 1,650 psi 500 % 100 ppi Download MED4-4515 data sheet Non-Vinyl Specific Peroxide Precatalyzed

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,650 psi (11.38 MPa)
Elongation 500 %
Tear 100 ppi (17.64 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 249 °C
Specific Gravity 1.15
Stress at Strain 400 psi / 200 % (2.76 MPa / 200 %)
Comment Non-Vinyl Specific Peroxide Precatalyzed

View more

MED4-4516 70 Type A 1,300 psi 450 % 130 ppi Download MED4-4516 data sheet Non-Vinyl Specific Peroxide Precatalyzed

Product Details

Property Average Result
Durometer 70 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 450 %
Tear 130 ppi (22.93 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 249 °C
Specific Gravity 1.21
Stress at Strain 500 psi / 200 % (3.45 MPa / 200 %)
Comment Non-Vinyl Specific Peroxide Precatalyzed

View more