Liquid Silicone Rubbers

Product Durometer Tensile Elongation Tear Data Sheet Comment
MED-4901 40 Type 00 285 psi 1135 % 55 ppi Download MED-4901 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 40 Type 00
Tensile 285 psi (1.97 MPa)
Elongation 1135 %
Tear 55 ppi (9.7 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure Rate Scorch 0.9 minutes
Cure Rate T90 1.2 minutes
Cure System Platinum
Extrusion Rate 160 g/minute
Mix Ratio 1:1
Specific Gravity 1.1
Stress at Strain 15 psi / 300 % (0.1 Mpa / 300 %)
Work Time 25 hours
Comment Injection Molding Elastomer

View more

MED-4905 7 Type A 350 psi 1000 % 70 ppi Download MED-4905 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 7 Type A
Tensile 350 psi (2.41 MPa)
Elongation 1000 %
Tear 70 ppi (12.35 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure Rate Scorch 0.65 minutes
Cure Rate T90 1.9 minutes
Cure System Platinum
Extrusion Rate 65 g/minute
Mix Ratio 1:1
Stress at Strain 40 psi / 200 % (0.28 MPa / 200 %)
Work Time 55 hours
Comment Injection Molding Elastomer

View more

MED-4910 10 Type A 450 psi 1000 % 65 ppi Download MED-4910 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 10 Type A
Tensile 450 psi (3.1 MPa)
Elongation 1000 %
Tear 65 ppi (11.46 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure Rate Scorch 1.4 minutes
Cure Rate T90 1.95 minutes
Cure System Platinum
Extrusion Rate 100 g/minute
Mix Ratio 1:1
Specific Gravity 1.07
Stress at Strain 45 psi / 200 % (0.31 MPa / 200 %)
Work Time 70 hours
Comment Injection Molding Elastomer

View more

MED-4920 20 Type A 750 psi 700 % 125 ppi Download MED-4920 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 20 Type A
Tensile 750 psi (5.17 MPa)
Elongation 700 %
Tear 125 ppi (22.05 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure Rate Scorch 1.5 minutes
Cure Rate T90 2.1 minutes
Cure System Platinum
Extrusion Rate 80 g/minute
Mix Ratio 1:1
Specific Gravity 1.14
Stress at Strain 65 psi / 200 % (0.45 MPa / 200 %)
Comment Injection Molding Elastomer

View more

MED-4930 30 Type A 800 psi 450 % 140 ppi Download MED-4930 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 30 Type A
Tensile 800 psi (5.52 MPa)
Elongation 450 %
Tear 140 ppi (24.69 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure Rate Scorch 1.3 minutes
Cure Rate T90 2.15 minutes
Cure System Platinum
Extrusion Rate 170 g/minute
Mix Ratio 1:1
Specific Gravity 1.13
Stress at Strain 175 psi / 200 % (1.21 MPa / 200 %)
Comment Injection Molding Elastomer

View more

MED-4940 40 Type A 1,190 psi 560% 246 ppi Download MED-4940 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 40 Type A
Tensile 1,190 psi (8.2 MPa)
Elongation 560%
Tear 246 ppi (43.39 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure Rate Scorch 1.5 minutes
Cure Rate T90 2.3 minutes
Cure System Platinum
Cure Type Heat Cure
Extrusion Rate 225 g/minute
Mix Ratio 1:1
Rheology Thixotropic / Non-slump
Specific Gravity 1.12
Stress at Strain 425 psi / 200 % (2.93 MPa / 200 %)

View more

MED-4942 40 Type A 850 psi 350 % 130 ppi Download MED-4942 data sheet Injection Molding Elastomer, Resists Blocking

Product Details

Property Average Result
Durometer 40 Type A
Tensile 850 psi (5.86 MPa)
Elongation 350 %
Tear 130 ppi (22.93 kN/m)
Appearance White
Cure 10 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.17
Comment Injection Molding Elastomer, Resists Blocking

View more

MED-4950 50 Type A 1,445 psi 700% 243 ppi Download MED-4950 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,445 psi (9.9 MPa)
Elongation 700%
Tear 243 ppi (42.86 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure Rate Scorch 1.4 minutes
Cure Rate T90 2.35 minutes
Cure System Platinum
Cure Type Heat Cure
Extrusion Rate 95 g/minute
Mix Ratio 1:1
Rheology Thixotropic / Non-slump
Specific Gravity 1.14
Stress at Strain 400 psi / 200 % (2.76 MPa / 200 %)

View more

MED-4960 60 Type A 1,300 psi 525 % 250 ppi Download MED-4960 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 60 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 525 %
Tear 250 ppi (44.09 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure Rate Scorch 1.05 minutes
Cure Rate T90 2.1 minutes
Cure System Platinum
Extrusion Rate 80 g/minute
Mix Ratio 1:1
Specific Gravity 1.15
Stress at Strain 600 psi / 200 % (4.14 MPa / 200 %)
Comment Injection Molding Elastomer

View more

MED-4970 70 Type A 1,325 psi 465 % 240 ppi Download MED-4970 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 70 Type A
Tensile 1,325 psi (9.14 MPa)
Elongation 465 %
Tear 240 ppi (42.33 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure Rate Scorch 1 minutes
Cure Rate T90 2.2 minutes
Cure System Platinum
Extrusion Rate 40 g/minute
Mix Ratio 1:1
Specific Gravity 1.22
Stress at Strain 825 psi / 200 % (5.69 MPa / 200 %)
Comment Injection Molding Elastomer

View more

MED-4971 68 Type A 875 psi 230 % 170 ppi Download MED-4971 data sheet High Clarity Injection Molding Elastomer

Product Details

Property Average Result
Durometer 68 Type A
Tensile 875 psi (6.03 MPa)
Elongation 230 %
Tear 170 ppi (29.98 kN/m)
Appearance Translucent
Cure 15 minutes / 150 °C
Cure Rate Scorch 0.65 minutes
Cure Rate T90 2.7 minutes
Cure System Platinum
Extrusion Rate 85 g/minute
Mix Ratio 1:1
Refractive Index 1.40
Specific Gravity 1.16
Stress at Strain 580 psi / 100 % (4 MPa / 100 %)
Comment High Clarity Injection Molding Elastomer

View more

MED-4980 80 Type A 1,000 psi 250 % 90 ppi Download MED-4980 data sheet Injection Molding Elastomer

Product Details

Property Average Result
Durometer 80 Type A
Tensile 1,000 psi (6.9 MPa)
Elongation 250 %
Tear 90 ppi (15.87 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure Rate Scorch 0.95 minutes
Cure Rate T90 2.05 minutes
Cure System Platinum
Extrusion Rate 107.5 g/minute
Mix Ratio 1:1
Specific Gravity 1.17
Stress at Strain 650 psi / 100 % (4.48 MPa / 100 %)
Comment Injection Molding Elastomer

View more

MED1-4955 55 Type A 1,165 psi 490 % 250 ppi Download MED1-4955 data sheet Self-Lubricating Injection Molding Elastomer, High Lubrication

Product Details

Property Average Result
Durometer 55 Type A
Tensile 1,165 psi (8.03 MPa)
Elongation 490 %
Tear 250 ppi (44.09 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure Rate Scorch 0.9 minutes
Cure Rate T90 2.2 minutes
Cure System Platinum
Extrusion Rate 240 g/minute
Mix Ratio 1:1
Specific Gravity 1.14
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Comment Self-Lubricating Injection Molding Elastomer, High Lubrication

View more

MED10-5440 30 Type A 1,250 psi 380 % 60 ppi Download MED10-5440 data sheet 100M% Fluorosilicone Injection Molding Elastomer

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 380 %
Tear 60 ppi (10.58 kN/m)
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Extrusion Rate 40 g/minute
Mix Ratio 1:1
Specific Gravity 1.38
Comment 100M% Fluorosilicone Injection Molding Elastomer

View more

MED2-4955 61 Type A 1,200 psi 490 % 250 ppi Download MED2-4955 data sheet Self-Lubricating Injection Molding Elastomer, Moderate Lubrication

Product Details

Property Average Result
Durometer 61 Type A
Tensile 1,200 psi (8.28 MPa)
Elongation 490 %
Tear 250 ppi (44.09 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure Rate Scorch 1.1 minutes
Cure Rate T90 1.8 minutes
Cure System Platinum
Extrusion Rate 235 g/minute
Mix Ratio 1:1
Specific Gravity 1.14
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Comment Self-Lubricating Injection Molding Elastomer, Moderate Lubrication

View more

MED30-4940-1 35 Type A 970 psi 570 % 210 ppi Download MED30-4940-1 data sheet Self-Lubricating Injection Molding Elastomer, Low Lubrication

Product Details

Property Average Result
Durometer 35 Type A
Tensile 970 psi (6.69 MPa)
Elongation 570 %
Tear 210 ppi (37.04 kN/m)
Appearance Translucent
Cure 5 minutes / 150 °C
Cure Rate Scorch 1 minutes
Cure Rate T90 2.5 minutes
Cure System Platinum
Extrusion Rate 350 g/minute
Mix Ratio 1:1
Specific Gravity 1.12
Stress at Strain 350 psi / 200 % (2.41 MPa / 200 %)
Work Time 72 hours
Comment Self-Lubricating Injection Molding Elastomer, Low Lubrication

View more

MED50-5438 31 Type A 650 psi 350 % 36 ppi Download MED50-5438 data sheet 50M% Fluorosilicone Injection Molding Elastomer

Product Details

Property Average Result
Durometer 31 Type A
Tensile 650 psi (4.48 MPa)
Elongation 350 %
Tear 36 ppi (6.35 kN/m)
Appearance Translucent
Cure 30 minutes / 150 °C
Cure Rate Scorch 1.35 minutes
Cure Rate T90 2.85 minutes
Cure System Platinum
Extrusion Rate 115 g/minute
Mix Ratio 1:1
Specific Gravity 1.25
Stress at Strain 300 psi / 200 % (2.07 Mpa / 200 %)
Work Time 16 hours
Comment 50M% Fluorosilicone Injection Molding Elastomer

View more

SIL-5920 19 Type A 1,080 psi 890 % 90 ppi Download SIL-5920 data sheet Designed For High Volume Injection Molding

Product Details

Property Average Result
Durometer 19 Type A
Tensile 1,080 psi (7.45 MPa)
Elongation 890 %
Tear 90 ppi (15.87 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure Rate Scorch 0.2 minutes
Cure Rate T10 0.15 minutes
Cure Rate T90 0.45 minutes
Cure System Platinum
Extrusion Rate 220 g/minute
Mix Ratio 1:1
Specific Gravity 1.08
Stress at Strain 90 psi / 200 % (0.62 MPa / 200 %)
Comment Designed For High Volume Injection Molding

View more

SIL-5930 30 Type A 1,340 psi 830 % 150 ppi Download SIL-5930 data sheet Designed for High Volume Injection Molding

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,340 psi (9.24 MPa)
Elongation 830 %
Tear 150 ppi (26.46 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure Rate Scorch 0.15 minutes
Cure Rate T10 0.14 minutes
Cure Rate T90 0.3 minutes
Cure System Platinum
Extrusion Rate 145 g/minute
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 160 psi / 200 % (1.1 MPa / 200 %)
Comment Designed for High Volume Injection Molding

View more

SIL-5940 40 Type A 1,350 psi 680 % 160 ppi Download SIL-5940 data sheet Designed for High Volume Injection Molding

Product Details

Property Average Result
Durometer 40 Type A
Tensile 1,350 psi (9.31 MPa)
Elongation 680 %
Tear 160 ppi (28.22 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure Rate Scorch 0.15 minutes
Cure Rate T10 0.14 minutes
Cure Rate T90 0.35 minutes
Cure System Platinum
Extrusion Rate 100 g/minute
Mix Ratio 1:1
Specific Gravity 1.12
Stress at Strain 300 psi / 200 % (2.07 Mpa / 200 %)
Comment Designed for High Volume Injection Molding

View more

SIL-5950 50 Type A 1,450 psi 550 % 190 ppi Download SIL-5950 data sheet Designed for High Volume Injection Molding

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,450 psi (10 MPa)
Elongation 550 %
Tear 190 ppi (33.51 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure Rate T10 0.12 minutes
Cure System Platinum
Extrusion Rate 70 g/minute
Mix Ratio 1:1
Specific Gravity 1.14
Stress at Strain 400 psi / 200 % (2.76 MPa / 200 %)
Comment Designed for High Volume Injection Molding

View more

SIL-5960 60 Type A 1,300 psi 425 % 200 ppi Download SIL-5960 data sheet Designed for High Volume Injection Molding

Product Details

Property Average Result
Durometer 60 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 425 %
Tear 200 ppi (35.27 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure Rate Scorch 0.1 minutes
Cure Rate T10 0.11 minutes
Cure Rate T90 0.5 minutes
Cure System Platinum
Extrusion Rate 70 g/minute
Mix Ratio 1:1
Specific Gravity 1.14
Stress at Strain 700 psi / 200 % (4.83 MPa / 200 %)
Comment Designed for High Volume Injection Molding

View more

SIL-5970 68 Type A 1,250 psi 400 % 225 ppi Download SIL-5970 data sheet Designed for High Volume Injection Molding

Product Details

Property Average Result
Durometer 68 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 400 %
Tear 225 ppi (39.68 kN/m)
Appearance Translucent
Cure 5 minutes / 165 °C
Cure Rate Scorch 0.1 minutes
Cure Rate T10 0.11 minutes
Cure Rate T90 0.45 minutes
Cure System Platinum
Extrusion Rate 100 g/minute
Mix Ratio 1:1
Specific Gravity 1.14
Stress at Strain 900 psi / 200 % (6.21 MPa / 200 %)
Comment Designed for High Volume Injection Molding

View more