High Consistency Rubbers

Product Durometer Tensile Elongation Tear Data Sheet Comment
MED-2045 40 Type A 1,500 psi 800 % 200 ppi Download MED-2045 data sheet Designed for Dissolving in Solvents

Product Details

Property Average Result
Durometer 40 Type A
Tensile 1,500 psi (10.34 MPa)
Elongation 800 %
Tear 200 ppi (35.27 kN/m)
Appearance Translucent
Cure 10 minutes / 171 °C
Cure Rate Scorch 0.7 minutes
Cure Rate T90 2.35 minutes
Cure System Platinum
Mix Ratio 100:0.7:0.16
Post Cure 2 hours / 148 °C
Specific Gravity 1.16
Stress at Strain 200 psi / 200 % (1.38 MPa / 200 %)
Comment Designed for Dissolving in Solvents

View more

MED-4014 15 Type A 700 psi 1,350 % 155 ppi Download MED-4014 data sheet Low modulus

Product Details

Property Average Result
Durometer 15 Type A
Tensile 700 psi (4.83 MPa)
Elongation 1,350 %
Tear 155 ppi (27.34 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure Rate Scorch 1.25 minutes
Cure Rate T90 2.5 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.08
Stress at Strain 40 psi / 200 % (0.28 MPa / 200 %)
Work Time 25 hours
Comment Low modulus

View more

MED-4019 55 Type A 1,290 psi 645 % 205 ppi Download MED-4019 data sheet Excellent adhesion and fatigue resistance

Product Details

Property Average Result
Durometer 55 Type A
Tensile 1,290 psi (8.9 MPa)
Elongation 645 %
Tear 205 ppi (36.2 kN/m)
Appearance Translucent
Cure 10 minutes / 171 °C
Cure System Platinum
Cure Type Heat Cure
Mix Ratio 1:1
Specific Gravity 1.23
Stress at Strain 310 psi / 200 % (2.1 MPa / 200 %)
Work Time 5 hours
Comment Excellent adhesion and fatigue resistance

View more

MED-4020 25 Type A 1,400 psi 1,250 % 190 ppi Download MED-4020 data sheet Low modulus with high tear

Product Details

Property Average Result
Durometer 25 Type A
Tensile 1,400 psi (9.66 MPa)
Elongation 1,250 %
Tear 190 ppi (33.51 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.95 minutes
Cure Rate T90 2.3 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.1
Stress at Strain 75 psi / 200 % (0.52 MPa / 200 %)
Work Time 10 hours
Comment Low modulus with high tear

View more

MED-4025 30 Type A 1,300 psi 900 % 130 ppi Download MED-4025 data sheet Low tension set

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 900 %
Tear 130 ppi (22.93 kN/m)
Appearance Translucent
Cure 10 minutes / 171 °C
Cure Rate Scorch 0.75 minutes
Cure Rate T90 2.8 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 105 psi / 200 % (0.72 MPa / 200 %)
Work Time 1.5 hours
Comment Low tension set

View more

MED-4027 30 Type A 2,300 psi 1,050 % 235 ppi Download MED-4027 data sheet Ultra-high tensile strength

Product Details

Property Average Result
Durometer 30 Type A
Tensile 2,300 psi (15.86 MPa)
Elongation 1,050 %
Tear 235 ppi (41.45 kN/m)
Appearance Translucent
Cure 10 minutes / 171 °C
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 100 psi / 200 % (0.69 MPa / 200 %)
Work Time 2.5 hours
Comment Ultra-high tensile strength

View more

MED-4032 30 Type A 1,200 psi 1,100 % 160 ppi Download MED-4032 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,200 psi (8.28 MPa)
Elongation 1,100 %
Tear 160 ppi (28.22 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 1 minutes
Cure Rate T90 3.05 minutes
Mix Ratio 100:1:1
Specific Gravity 1.1
Stress at Strain 140 psi / 200 % (0.97 MPa / 200 %)
Work Time 8 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4035 35 Type A 1,565 psi 1,055 % 195 ppi Download MED-4035 data sheet High Tear Strength

Product Details

Property Average Result
Durometer 35 Type A
Tensile 1,565 psi (10.79 MPa)
Elongation 1,055 %
Tear 195 ppi (34.39 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 195 psi / 200 % (1.34 MPa / 200 %)
Work Time 2 hours
Comment High Tear Strength

View more

MED-4042 40 Type A 1,500 psi 1000 % 160 ppi Download MED-4042 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 40 Type A
Tensile 1,500 psi (10.34 MPa)
Elongation 1000 %
Tear 160 ppi (28.22 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.8 minutes
Cure Rate T90 2.45 minutes
Mix Ratio 100:1:1
Specific Gravity 1.11
Stress at Strain 230 psi / 200 % (1.59 MPa / 200 %)
Work Time 2 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4050 50 Type A 1,500 psi 985 % 250 ppi Download MED-4050 data sheet High Tear Strength

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,500 psi (10.34 MPa)
Elongation 985 %
Tear 250 ppi (44.09 kN/m)
Appearance Translucent Gray
Cure 10 minutes / 115 °C
Cure Rate Scorch 1.1 minutes
Cure Rate T90 2.6 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.16
Stress at Strain 300 psi / 200 % (2.07 Mpa / 200 %)
Work Time 3.5 hours
Comment High Tear Strength

View more

MED-4052 50 Type A 1,445 psi 1100 % 230 ppi Download MED-4052 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,445 psi (9.97 MPa)
Elongation 1100 %
Tear 230 ppi (40.56 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.7 minutes
Cure Rate T90 2.25 minutes
Mix Ratio 100:1:1
Specific Gravity 1.16
Stress at Strain 280 psi / 200 % (1.93 MPa / 200 %)
Work Time 9 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4055 55 Type A 1,700 psi 900 % 300 ppi Download MED-4055 data sheet Ultra-high tear strength

Product Details

Property Average Result
Durometer 55 Type A
Tensile 1,700 psi (11.72 MPa)
Elongation 900 %
Tear 300 ppi (52.91 kN/m)
Appearance Translucent
Cure 10 minutes / 138 °C
Cure Rate Scorch 1 minutes
Cure Rate T90 2.85 minutes
Cure System Platinum
Mix Ratio 1:1
Post Cure 4 hours / 177 °C
Specific Gravity 1.14
Stress at Strain 500 psi / 200 % (3.45 MPa / 200 %)
Work Time 2.5 hours
Comment Ultra-high tear strength

View more

MED-4062 60 Type A 1,400 psi 1000 % 250 ppi Download MED-4062 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 60 Type A
Tensile 1,400 psi (9.66 MPa)
Elongation 1000 %
Tear 250 ppi (44.09 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.7 minutes
Cure Rate T90 2.3 minutes
Mix Ratio 100:1:1
Specific Gravity 1.16
Stress at Strain 300 psi / 200 % (2.07 Mpa / 200 %)
Work Time 11 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4065 65 Type A 1,250 psi 1000 % 250 ppi Download MED-4065 data sheet High Tear Strength

Product Details

Property Average Result
Durometer 65 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 1000 %
Tear 250 ppi (44.09 kN/m)
Appearance Translucent Tan
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.85 minutes
Cure Rate T90 2.65 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.2
Stress at Strain 350 psi / 200 % (2.41 MPa / 200 %)
Work Time 6 hours
Comment High Tear Strength

View more

MED-4070 70 Type A 1,430 psi 750 % 300 ppi Download MED-4070 data sheet Abrasion / Fatigue Resistant

Product Details

Property Average Result
Durometer 70 Type A
Tensile 1,430 psi (9.86 MPa)
Elongation 750 %
Tear 300 ppi (52.91 kN/m)
Appearance Translucent
Cure 10 minutes / 138 °C
Cure Rate Scorch 0.9 minutes
Cure Rate T90 2.7 minutes
Cure System Platinum
Mix Ratio 1:1
Post Cure 4 hours / 177 °C
Specific Gravity 1.19
Stress at Strain 600 psi / 200 % (4.14 MPa / 200 %)
Work Time 2 hours
Comment Abrasion / Fatigue Resistant

View more

MED-4072 70 Type A 1,100 psi 875 % 240 ppi Download MED-4072 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 70 Type A
Tensile 1,100 psi (7.59 MPa)
Elongation 875 %
Tear 240 ppi (42.33 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.55 minutes
Cure Rate T90 1.9 minutes
Mix Ratio 100:1:1
Specific Gravity 1.22
Stress at Strain 450 psi / 200 % (3.1 MPa / 200 %)
Work Time 4 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4080 80 Type A 1,150 psi 700 % 225 ppi Download MED-4080 data sheet High Tear Strength

Product Details

Property Average Result
Durometer 80 Type A
Tensile 1,150 psi (7.93 MPa)
Elongation 700 %
Tear 225 ppi (39.68 kN/m)
Appearance Translucent Tan
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.8 minutes
Cure Rate T90 2.75 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.2
Stress at Strain 450 psi / 200 % (3.1 MPa / 200 %)
Work Time 8 hours
Comment High Tear Strength

View more

MED-4082 80 Type A 1,150 psi 900 % 200 ppi Download MED-4082 data sheet Can be Cured via Platinum or Peroxide

Product Details

Property Average Result
Durometer 80 Type A
Tensile 1,150 psi (7.93 MPa)
Elongation 900 %
Tear 200 ppi (35.27 kN/m)
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.6 minutes
Cure Rate T90 2.2 minutes
Mix Ratio 100:1:1
Specific Gravity 1.22
Stress at Strain 400 psi / 200 % (2.76 MPa / 200 %)
Work Time 16 hours
Comment Can be Cured via Platinum or Peroxide

View more

MED-4120 30 Type A 1,300 psi 950 % 140 ppi Download MED-4120 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 30 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 950 %
Tear 140 ppi (24.69 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure Rate Scorch 0.55 minutes
Cure Rate T90 2.1 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 177 °C
Specific Gravity 1.1
Stress at Strain 100 psi / 200 % (0.69 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4128 25 Type A 1,010 psi 800 % 70 ppi Download MED-4128 data sheet Low Tension Set, Uncatalyzed

Product Details

Property Average Result
Durometer 25 Type A
Tensile 1,010 psi (6.97 MPa)
Elongation 800 %
Tear 70 ppi (12.35 kN/m)
Appearance Translucent
Cure 10 minutes / 116 °C
Cure Rate Scorch 0.55 minutes
Cure Rate T90 1.65 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 200 °C
Specific Gravity 1.11
Stress at Strain 90 psi / 200 % (0.62 MPa / 200 %)
Comment Low Tension Set, Uncatalyzed

View more

MED-4135 35 Type A 1,250 psi 800 % 110 ppi Download MED-4135 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 35 Type A
Tensile 1,250 psi (8.62 MPa)
Elongation 800 %
Tear 110 ppi (19.4 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure Rate Scorch 0.55 minutes
Cure Rate T90 2.1 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 177 °C
Specific Gravity 1.1
Stress at Strain 190 psi / 200 % (1.31 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4150 50 Type A 1,400 psi 750 % 190 ppi Download MED-4150 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,400 psi (9.66 MPa)
Elongation 750 %
Tear 190 ppi (33.51 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure Rate Scorch 0.5 minutes
Cure Rate T90 1.9 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 177 °C
Specific Gravity 1.16
Stress at Strain 250 psi / 200 % (1.72 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4165 65 Type A 1,200 psi 700 % 225 ppi Download MED-4165 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 65 Type A
Tensile 1,200 psi (8.28 MPa)
Elongation 700 %
Tear 225 ppi (39.68 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure Rate Scorch 0.5 minutes
Cure Rate T90 1.7 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 177 °C
Specific Gravity 1.21
Stress at Strain 400 psi / 200 % (2.76 MPa / 200 %)
Comment Uncatalyzed

View more

MED-4174 50 Type A 1,200 psi 775 % 225 ppi Download MED-4174 data sheet Uncatalyzed

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,200 psi (8.28 MPa)
Elongation 775 %
Tear 225 ppi (39.68 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure Rate Scorch 0.55 minutes
Cure Rate T90 1.7 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 4 hours / 205 °C
Specific Gravity 1.15
Stress at Strain 325 psi / 200 % (2.24 MPa / 200 %)
Comment Uncatalyzed

View more

MED4-4115 50 Type A 1,600 psi 500 % 100 ppi Download MED4-4115 data sheet Non-Vinyl Specific Peroxide Precatalyzed

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,600 psi (11.03 MPa)
Elongation 500 %
Tear 100 ppi (17.64 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure Rate Scorch 0.65 minutes
Cure Rate T90 2.2 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 249 °C
Specific Gravity 1.15
Stress at Strain 400 psi / 200 % (2.76 MPa / 200 %)
Comment Non-Vinyl Specific Peroxide Precatalyzed

View more

MED4-4116 70 Type A 1,300 psi 450 % 125 ppi Download MED4-4116 data sheet Non-Vinyl Specific Peroxide Precatalyzed

Product Details

Property Average Result
Durometer 70 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 450 %
Tear 125 ppi (22.05 kN/m)
Appearance Translucent
Cure 5 minutes / 116 °C
Cure Rate Scorch 0.5 minutes
Cure Rate T90 2.05 minutes
Cure System Peroxide
Mix Ratio 1 PART
Post Cure 2 hours / 249 °C
Specific Gravity 1.21
Stress at Strain 550 psi / 200 % (3.79 MPa / 200 %)
Comment Non-Vinyl Specific Peroxide Precatalyzed

View more

SIL2-5020 21 Type A 1,620 psi 1185 % 195 ppi Download SIL2-5020 data sheet Designed For High Volume Extrusion Or Molding

Product Details

Property Average Result
Durometer 21 Type A
Tensile 1,620 psi (11.17 MPa)
Elongation 1185 %
Tear 195 ppi (34.39 kN/m)
Appearance Translucent
Cure 15 minutes / 165 °C
Cure Rate Scorch 0.15 minutes
Cure Rate T10 0.13 minutes
Cure Rate T90 0.29 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 65 psi / 200 % (0.45 MPa / 200 %)
Work Time 8 hours
Comment Designed For High Volume Extrusion Or Molding

View more

SIL2-5030 31 Type A 1,690 psi 1140 % 215 ppi Download SIL2-5030 data sheet Designed for High Volume Extrusion or Molding

Product Details

Property Average Result
Durometer 31 Type A
Tensile 1,690 psi (11.66 MPa)
Elongation 1140 %
Tear 215 ppi (37.92 kN/m)
Appearance Translucent
Cure 15 minutes / 165 °C
Cure Rate Scorch 0.15 minutes
Cure Rate T10 0.14 minutes
Cure Rate T90 0.26 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.11
Stress at Strain 120 psi / 200 % (0.83 MPa / 200 %)
Work Time 5 hours
Comment Designed for High Volume Extrusion or Molding

View more

SIL2-5040 39 Type A 1,510 psi 1115 % 220 ppi Download SIL2-5040 data sheet Designed for High Volume Extrusion or Molding

Product Details

Property Average Result
Durometer 39 Type A
Tensile 1,510 psi (10.41 MPa)
Elongation 1115 %
Tear 220 ppi (38.8 kN/m)
Appearance Translucent
Cure 15 minutes / 165 °C
Cure Rate Scorch 0.15 minutes
Cure Rate T10 0.13 minutes
Cure Rate T90 0.29 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.15
Stress at Strain 140 psi / 200 % (0.97 MPa / 200 %)
Work Time 4 hours
Comment Designed for High Volume Extrusion or Molding

View more

SIL2-5050 50 Type A 1,350 psi 940 % 245 ppi Download SIL2-5050 data sheet Designed for High Volume Extrusion or Molding

Product Details

Property Average Result
Durometer 50 Type A
Tensile 1,350 psi (9.31 MPa)
Elongation 940 %
Tear 245 ppi (43.21 kN/m)
Appearance Translucent
Cure 15 minutes / 165 °C
Cure Rate Scorch 0.15 minutes
Cure Rate T10 0.15 minutes
Cure Rate T90 0.34 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.16
Stress at Strain 380 psi / 200 % (2.62 MPa / 200 %)
Work Time 4 hours
Comment Designed for High Volume Extrusion or Molding

View more

SIL2-5060 60 Type A 1,300 psi 920 % 255 ppi Download SIL2-5060 data sheet Designed for High Volume Extrusion or Molding

Product Details

Property Average Result
Durometer 60 Type A
Tensile 1,300 psi (8.97 MPa)
Elongation 920 %
Tear 255 ppi (44.97 kN/m)
Appearance Translucent
Cure 15 minutes / 165 °C
Cure Rate Scorch 0.15 minutes
Cure Rate T10 0.12 minutes
Cure Rate T90 0.2 minutes
Cure System Platinum
Mix Ratio 1:1
Specific Gravity 1.19
Stress at Strain 380 psi / 200 % (2.62 MPa / 200 %)
Work Time 11 hours
Comment Designed for High Volume Extrusion or Molding

View more

SIL2-5070 68 Type A 1,330 psi 855 % 260 ppi Download SIL2-5070 data sheet Designed for High Volume Extrusion or Molding

Product Details

Property Average Result
Durometer 68 Type A
Tensile 1,330 psi (9.17 MPa)
Elongation 855 %
Tear 260 ppi (45.86 kN/m)
Appearance Translucent
Cure 15 minutes / 165 °C
Cure Rate Scorch 0.1 minutes
Cure Rate T10 0.12 minutes
Cure Rate T90 2.8 minutes
Cure System Platinum
Mix Ratio 1:1
Post Cure 2 hours / 150 °C
Specific Gravity 1.2
Stress at Strain 360 psi / 200 % (2.48 MPa / 200 %)
Work Time 2 hours
Comment Designed for High Volume Extrusion or Molding

View more

SIL2-5080 80 Type A 1,140 psi 615 % 210 ppi Download SIL2-5080 data sheet Designed for High Volume Extrusion or Molding

Product Details

Property Average Result
Durometer 80 Type A
Tensile 1,140 psi (7.86 MPa)
Elongation 615 %
Tear 210 ppi (37.04 kN/m)
Appearance Translucent
Cure 15 minutes / 165 °C
Cure Rate Scorch 0.1 minutes
Cure Rate T10 0.15 minutes
Cure Rate T90 1.55 minutes
Cure System Platinum
Mix Ratio 1:1
Post Cure 2 hours / 150 °C
Specific Gravity 1.2
Stress at Strain 460 psi / 200 % (3.17 MPa / 200 %)
Work Time 20 hours
Comment Designed for High Volume Extrusion or Molding

View more