Product Cure System Viscosity Non Volatile Content Durometer Data Sheet Comment
MED-2014 Platinum 1,800 cP 35 % N/A Download MED-2014 data sheet One Part, Requires heat to cure

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,800 cP (1,800 mPa*s)
Non Volatile Content 35 %
Appearance Translucent
Cure 60 minutes / 50 °C 60 minutes / 150 °C 3 minutes / RTV
Elongation 900 %
Mix Ratio 1 PART
Solvent Xylene
Tear 160 ppi (28.22 kN/m)
Tensile 1,700 psi (11.72 MPa)
Comment One Part, Requires heat to cure

View more

MED-4159 Amine 200 cSt 53 % N/A Download MED-4159 data sheet Low Crosslink Density, Amino Functional Lubricious Silicone Coating

Product Details

Property Average Result
Cure System Amine
Viscosity 200 cSt
Non Volatile Content 53 %
Appearance Clear
Cure 7 days / RTV
Mix Ratio 1 PART
Solvent Stoddard Solvent & IPA
Comment Low Crosslink Density, Amino Functional Lubricious Silicone Coating

View more

MED-4162 Non-Curing 27,000 cP 31 % N/A Download MED-4162 data sheet Lubricious Coating

Product Details

Property Average Result
Cure System Non-Curing
Viscosity 27,000 cP (27,000 mPa*s)
Non Volatile Content 31 %
Appearance Translucent
Mix Ratio 1 PART
Solvent Xylene
Comment Lubricious Coating

View more

MED10-4161 Amine 140 cSt 33 % 25 Type 00 Download MED10-4161 data sheet Amino Functional Lubricious Silicone Coating

Product Details

Property Average Result
Cure System Amine
Viscosity 140 cSt (120.04 mPa*s)
Non Volatile Content 33 %
Durometer 25 Type 00
Appearance Clear
Cure 5 days / 25 °C
Mix Ratio 1 PART
Solvent Xylene
Specific Gravity 0.86
Comment Amino Functional Lubricious Silicone Coating

View more

MED10-6400 Platinum 800 cP 35 % 30 Type A Download MED10-6400 data sheet 1.43 R.I.

Product Details

Property Average Result
Cure System Platinum
Viscosity 800 cP (800 mPa*s)
Non Volatile Content 35 %
Durometer 30 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 800 %
Mix Ratio 1:1
Solvent Xylene
Tear 150 ppi (26.46 kN/m)
Tensile 1,500 psi (10.34 MPa)
Comment 1.43 R.I.

View more

MED10-6600 Platinum 400 cP 35 % 25 Type A Download MED10-6600 data sheet 1.46 R.I.

Product Details

Property Average Result
Cure System Platinum
Viscosity 400 cP (400 mPa*s)
Non Volatile Content 35 %
Durometer 25 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 750 %
Mix Ratio 1:1
Refractive Index 1.46
Solvent Xylene
Stress at Strain 325 psi / 300 % (2.24 Mpa / 300 %)
Tear 145 ppi (25.57 kN/m)
Tensile 1,200 psi (8.28 MPa)
Comment 1.46 R.I.

View more

MED10-6605 Acetoxy 700 cP 29 % 25 Type A Download MED10-6605 data sheet One Part

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Durometer 25 Type A
Appearance Translucent
Cure 5 days / RTV
Elongation 950 %
Mix Ratio 1 PART
Solvent Xylene
Stress at Strain 160 psi / 300 % (1.1 Mpa / 300 %)
Tear 125 ppi (22.05 kN/m)
Tensile 1,500 psi (10.34 MPa)
Comment One Part

View more

MED10-6607 Oxime 6,000 cP 35 % 40 Type A Download MED10-6607 data sheet One Part

Product Details

Property Average Result
Cure System Oxime
Viscosity 6,000 cP (6,000 mPa*s)
Non Volatile Content 35 %
Durometer 40 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 650 %
Mix Ratio 1 PART
Solvent Naptha
Specific Gravity 1.1
Tear 95 ppi (16.75 kN/m)
Tensile 1,200 psi (8.28 MPa)
Comment One Part

View more

MED10-6615 Platinum 65 cP 32 % 72 Type 00 Download MED10-6615 data sheet Silicone adhesive dispersed in heptane, cures rapidly with heat

Product Details

Property Average Result
Cure Type Heat Cure
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 30 minutes / RTV
Cure System Platinum
Durometer 72 Type 00
Elongation 750 %
Non Volatile Content 32 %
Substrate Primerless: Aluminum / Glass / PMMA / Silicone / With Primer: PEEK / Polycarbonate / Polyetherimide / ABS / Polyimide / Polysulphone / Polyurethane / Stainless steel
Tear 120 ppi (21.16 kN/m)
Tensile 1,060 psi (7.31 MPa)
Viscosity 65 cP (65 mPa*s)
Comment Silicone adhesive dispersed in heptane, cures rapidly with heat

View more

MED10-6640 Platinum 2,500 cP 20 % 40 Type A Download MED10-6640 data sheet Ultra High Tear

Product Details

Property Average Result
Cure System Platinum
Viscosity 2,500 cP (2,500 mPa*s)
Non Volatile Content 20 %
Durometer 40 Type A
Appearance Translucent
Cure 30 minutes / 25 °C 45 minutes / 75 °C 135 minutes / 150 °C
Elongation 1,000 %
Mix Ratio 1:1
Refractive Index 1.41
Solvent Xylene
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Comment Ultra High Tear

View more

MED10-6655 Acetoxy 700 cP 60 % 35 Type A Download MED10-6655 data sheet 100M% Fluorosilicone

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 60 %
Durometer 35 Type A
Appearance White
Cure 3 days / RTV
Elongation 425 %
Mix Ratio 1 PART
Solvent Butyl Acetate
Tear 45 ppi (7.94 kN/m)
Tensile 775 psi (5.34 MPa)
Comment 100M% Fluorosilicone

View more

MED10-6670 Platinum N/A 25 % N/A Download MED10-6670 data sheet Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Platinum
Non Volatile Content 25 %
Appearance Translucent
Cure 5 minutes / RTV
Mix Ratio 1:1
Solvent Xylene

View more

MED10-6671 Acetoxy N/A N/A N/A Download MED10-6671 data sheet RTV, Low Coefficient of Friction Coating

Product Details

Property Average Result
Cure System Acetoxy
Appearance Translucent
Cure 24 hours / RTV
Mix Ratio 1 Part
Comment RTV, Low Coefficient of Friction Coating

View more

MED11-6604 Acetoxy 250 cP 50 % 15 Type A Download MED11-6604 data sheet One Part, Smooth Finish

Product Details

Property Average Result
Cure System Acetoxy
Viscosity 250 cP (250 mPa*s)
Non Volatile Content 50 %
Durometer 15 Type A
Appearance Translucent
Cure 24 hours / RTV
Elongation 375 %
Mix Ratio 1 PART
Solvent THF
Specific Gravity 0.99
Tear 15 ppi (2.65 kN/m)
Tensile 75 psi (0.52 MPa)
Comment One Part, Smooth Finish

View more

MED16-6606 Acetoxy 95 cP 30 % 20 Type A Download MED16-6606 data sheet Silicone adhesive dispersed in heptane

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 20 Type A
Elongation 800 %
Non Volatile Content 30 %
Solvent Heptane
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate / Stainless steel
Tear 120 ppi (21.16 kN/m)
Tensile 1,200 psi (8.28 MPa)
Viscosity 95 cP (95 mPa*s)
Comment Silicone adhesive dispersed in heptane

View more