Adhesives/Sealants

Product Substrate Cure Type Mix Ratio Rheology Work Time Cure System Durometer Data Sheet Comment
MED-1000 Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate RTV 1 PART Flowable / Self Leveling N/A Acetoxy 25 Type A Download MED-1000 data sheet Medium flow, high extrusion rate

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 795 %
Extrusion Rate 2.5 g/minute
Specific Gravity 1.08
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate
Tack Free Time 12 minutes
Tear 75 ppi (13.23 kN/m)
Tensile 1,400 psi (9.66 MPa)
Comment Medium flow, high extrusion rate

View more

MED-1011 Primerless: Glass / Polyurethane / Silicone / Aluminum / Titanium / With Primer: Polycarbonate / Stainless steel RTV 1 PART Flowable / Self Leveling N/A Acetoxy 25 Type A Download MED-1011 data sheet Low flow

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 725 %
Extrusion Rate 90 g/minute
Flow Rate 1.1 in (27.94 mm)
Specific Gravity 1.12
Stress at Strain 115 psi / 200 % (0.79 MPa / 200 %)
Substrate Primerless: Glass / Polyurethane / Silicone / Aluminum / Titanium / With Primer: Polycarbonate / Stainless steel
Tack Free Time 13 minutes
Tear 100 ppi (17.64 kN/m)
Tensile 1,400 psi (9.66 MPa)
Comment Low flow

View more

MED-1031 Primerless: Glass / Polyurethane / Aluminum / Silicone / Titanium RTV 1 PART Thixotropic / non-slump N/A Oxime 35 Type A Download MED-1031 data sheet Non-acidic leaving group

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 7 days / RTV
Cure System Oxime
Durometer 35 Type A
Elongation 310 %
Extrusion Rate 70 g/minute
Specific Gravity 1.1
Stress at Strain 415 psi / 200 % (2.86 MPa / 200 %)
Substrate Primerless: Glass / Polyurethane / Aluminum / Silicone / Titanium
Tack Free Time 22 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 840 psi (5.79 MPa)
Comment Non-acidic leaving group

View more

MED-1037 Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate RTV 1 PART Thixotropic / non-slump N/A Acetoxy 30 Type A Download MED-1037 data sheet Low-slump, solvent-free translucent silicone

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 30 Type A
Elongation 565 %
Extrusion Rate 2.8 g/minute
Flow Rate 0.2 in (5.08 mm)
Specific Gravity 1.07
Stress at Strain 170 psi / 200 % (1.17 MPa / 200 %)
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium / With Primer: Polycarbonate
Tack Free Time 9 minutes
Tensile 730 psi (5.03 MPa)
Comment Low-slump, solvent-free translucent silicone

View more

MED-1040 Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium RTV 1 PART Flowable / Self Leveling N/A Acetoxy 23 Type A Download MED-1040 data sheet High flow

Product Details

Property Average Result
Cure Type RTV
Mix Ratio 1 PART
Rheology Flowable / Self Leveling
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 23 Type A
Elongation 340 %
Extrusion Rate 4 g/minute
Flow Rate 2.2 in (55.88 mm)
Specific Gravity 1.03
Substrate Primerless: Aluminum / Glass / Polyurethane / Silicone / Titanium
Tack Free Time 9.5 minutes
Tear 17 ppi (3 kN/m)
Tensile 265 psi (1.83 MPa)
Comment High flow

View more

MED1-4013 Primerless: Glass / Aluminum / PMMA / Polycarbonate / Silicone / Polyurethane / With Primer: ABS / Polyetherimide / PEEK / Polycarbonate / Polyimide / Polysulphone / Stainless steel / Polyurethane Heat Cure / RTV 1:1 Thixotropic / non-slump N/A Platinum 20 Type A Download MED1-4013 data sheet Quick cure, high extrusion rate

Product Details

Property Average Result
Cure Type Heat Cure / RTV
Mix Ratio 1:1
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 24 hours / RTV
Cure System Platinum
Durometer 20 Type A
Elongation 800 %
Peel Strength 17 lbf/in (2.98 kN/m)
Specific Gravity 1.11
Stress at Strain 120 psi / 200 % (0.83 MPa / 200 %)
Substrate Primerless: Glass / Aluminum / PMMA / Polycarbonate / Silicone / Polyurethane / With Primer: ABS / Polyetherimide / PEEK / Polycarbonate / Polyimide / Polysulphone / Stainless steel / Polyurethane
Tack Free Time 15 minutes
Tear 130 ppi (22.93 kN/m)
Tensile 1,000 psi (6.9 MPa)
Viscosity 80,000 cP (80,000 mPa*s)
Comment Quick cure, high extrusion rate

View more

MED2-4013 Primerless: Aluminum / Glass / PMMA / Silicone / With Primer: ABS / PEEK / Polycarbonate / Polyetherimide / Polyimide / Polysulphone / Polyurethane / Stainless steel Heat Cure 1:1 Thixotropic / non-slump N/A Platinum 15 Type A Download MED2-4013 data sheet Quick cure, high extrusion rate

Product Details

Property Average Result
Cure Type Heat Cure
Mix Ratio 1:1
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 15 minutes / 150 ┬░C
Cure System Platinum
Durometer 15 Type A
Elongation 800 %
Peel Strength 26 lbf/in (4.55 kN/m)
Specific Gravity 1.12
Stress at Strain 80 psi / 200 % (0.55 MPa / 200 %)
Substrate Primerless: Aluminum / Glass / PMMA / Silicone / With Primer: ABS / PEEK / Polycarbonate / Polyetherimide / Polyimide / Polysulphone / Polyurethane / Stainless steel
Tack Free Time 15 hours
Tear 130 ppi (22.93 kN/m)
Tensile 1,000 psi (6.9 MPa)
Viscosity 80,000 cP (80,000 mPa*s)
Comment Quick cure, high extrusion rate

View more

MED3-4013 Primerless: Aluminum / PMMA / Polyurethane / Glass / Polycarbonate / Silicone / With Primer: PEEK / Polyetherimide / Polysulphone / ABS / Polycarbonate / Stainless steel / Polyimide / Polyurethane Heat Cure / RTV 1:1 Thixotropic / non-slump N/A Platinum 20 Type A Download MED3-4013 data sheet Quick cure, high extrusion rate

Product Details

Property Average Result
Cure Type Heat Cure / RTV
Mix Ratio 1:1
Rheology Thixotropic / non-slump
Appearance Translucent
Cure 24 hours / RTV
Cure System Platinum
Durometer 20 Type A
Elongation 800 %
Peel Strength 23 lbf/in (4.03 kN/m)
Specific Gravity 1.12
Stress at Strain 125 psi / 200 % (0.86 MPa / 200 %)
Substrate Primerless: Aluminum / PMMA / Polyurethane / Glass / Polycarbonate / Silicone / With Primer: PEEK / Polyetherimide / Polysulphone / ABS / Polycarbonate / Stainless steel / Polyimide / Polyurethane
Tack Free Time 60 minutes
Tear 130 ppi (22.93 kN/m)
Tensile 1,000 psi (6.9 MPa)
Viscosity 80,000 cP (80,000 mPa*s)
Comment Quick cure, high extrusion rate

View more