Coatings/Dispersions

Product Cure System Viscosity Non Volatile Content Durometer Data Sheet Comment
CV1-1146-2 Oxime 1,125 cP N/A N/A Download CV1-1146-2 data sheet N/A

Product Details

Property Average Result
Viscosity 1,125 cP (1,125 mPa*s)
Appearance Black
Tack Free Time 2 hours
Cure System Oxime

View more

R-1009 Oxime 6,150 cP 32 % 45 Type A Download R-1009 data sheet High strength coating recommend for coating PCBs and other electronic assemblies.

Product Details

Property Average Result
Viscosity 6,150 cP (6,150 mPa*s)
Non Volatile Content 32 %
Appearance Translucent
Tack Free Time 1.5 hours
Cure 7 days / RTV
Cure System Oxime
Durometer 45 Type A
Elongation 650 %
Specific Gravity 1.1
Tear 95 ppi (16.75 kN/m)
Tensile 1,150 psi (7.93 MPa)
Comment High strength coating recommend for coating PCBs and other electronic assemblies.

View more

R-1082 Acetoxy 700 cP 29 % 25 Type A Download R-1082 data sheet Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

Product Details

Property Average Result
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Appearance Translucent
Cure 5 days / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 950 %
Refractive Index 1.41
Specific Gravity 1.09
Stress at Strain 160 psi / 300 % (1.1 Mpa / 300 %)
Tear 125 ppi (22.05 kN/m)
Tensile 1,425 psi (9.83 MPa)
Comment Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

View more

R-1182 Acetoxy N/A 7 % N/A Download R-1182 data sheet One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

Product Details

Property Average Result
Non Volatile Content 7 %
Appearance Translucent
Cure RTV
Cure System Acetoxy
Comment One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

View more

R-2180 Platinum 3,075 cP 20 % 40 Type A Download R-2180 data sheet High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

Product Details

Property Average Result
Viscosity 3,075 cP (3,075 mPa*s)
Non Volatile Content 20 %
Appearance Translucent
Cure 45 minutes / 75 °C 135 minutes / 150 °C
Cure System Platinum
Durometer 40 Type A
Elongation 1,050 %
Mix Ratio 1:1
Refractive Index 1.41
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Work Time 72 hours
Comment High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

View more

R-2180-2 Platinum 3,275 cP 20 % 45 Type A Download R-2180-2 data sheet Cure: 30 M / 25 C : 45 M / 75 C : 135 M / 150 C, 20% Solids

Product Details

Property Average Result
Viscosity 3,275 cP (3,275 mPa*s)
Non Volatile Content 20 %
Appearance Translucent
Cure 30 minutes / RTV 45 minutes / 75 °C 135 minutes / 150 °C
Cure System Platinum
Durometer 45 Type A
Elongation 1,000 %
Mix Ratio 1:1
Stress at Strain 140 psi / 100 % (0.97 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,650 psi (11.38 MPa)
Comment Cure: 30 M / 25 C : 45 M / 75 C : 135 M / 150 C, 20% Solids

View more

R-3930 Acetoxy 735 cP 60 % 30 Type A Download R-3930 data sheet 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

Product Details

Property Average Result
Viscosity 735 cP (735 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 30 Type A
Elongation 400 %
Specific Gravity 1.36
Tear 40 ppi (7.05 kN/m)
Tensile 750 psi (5.17 MPa)
Comment 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

View more

R-3975 Acetoxy 1,625 cP 60 % 25 Type A Download R-3975 data sheet Dispersion Coating, 60% Solids

Product Details

Property Average Result
Viscosity 1,625 cP (1,625 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 400 %
Mix Ratio 1 PART
Specific Gravity 1.29
Tear 35 ppi (6.17 kN/m)
Tensile 425 psi (2.93 MPa)
Comment Dispersion Coating, 60% Solids

View more

R1-3930-11 Acetoxy N/A N/A 40 Type A Download R1-3930-11 data sheet 240*3) psi (1.7Mpa) Lap Shear at 7 D @ R.T., H / Fed. Color Standard 36118

Product Details

Property Average Result
Appearance Gray
Tack Free Time 20 minutes
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 40 Type A
Elongation 325 %
Lap Shear 290 psi (2 MPa)
Specific Gravity 1.48
Tear 45 ppi (7.94 kN/m)
Tensile 725 psi (5 MPa)
Comment 240*3) psi (1.7Mpa) Lap Shear at 7 D @ R.T., H / Fed. Color Standard 36118

View more

R2-3930-11 Acetoxy N/A N/A 35 Type A Download R2-3930-11 data sheet 315*3) psi (2.2Mpa) Lap Shear at 7 D @ R.T., H / Fed. Color Standard 36622

Product Details

Property Average Result
Appearance Light Gray
Tack Free Time 20 minutes
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 35 Type A
Elongation 415 %
Lap Shear 315 psi (2.17 MPa)
Specific Gravity 1.36
Tear 60 ppi (10.58 kN/m)
Tensile 900 psi (6.21 MPa)
Comment 315*3) psi (2.2Mpa) Lap Shear at 7 D @ R.T., H / Fed. Color Standard 36622

View more

R3-1075 Oxime 3,300 cP 60 % 40 Type A Download R3-1075 data sheet Dispersion Coating / Conformal, 60% Solids

Product Details

Property Average Result
Viscosity 3,300 cP (3,300 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Tack Free Time 80 minutes
Cure 7 days / 25 °C
Cure System Oxime
Dielectric Strength 1,250 volts/mil (48.75 kV/mm)
Durometer 40 Type A
Elongation 350 %
Mix Ratio 1 PART
Operating Temperature -65 °C / 240 °C
Solvent Xylene
Specific Gravity 1.06
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Dispersion Coating / Conformal, 60% Solids

View more

R3-3930-11 Acetoxy N/A N/A 40 Type A Download R3-3930-11 data sheet 375*3) psi (2.6Mpa) Lap Shear at 7 D @ R.T., H / Fed. Color Standard 36375

Product Details

Property Average Result
Appearance Gray
Tack Free Time 20 minutes
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 40 Type A
Elongation 400 %
Lap Shear 375 psi (2.59 MPa)
Specific Gravity 1.36
Tear 50 ppi (8.82 kN/m)
Tensile 815 psi (5.62 MPa)
Comment 375*3) psi (2.6Mpa) Lap Shear at 7 D @ R.T., H / Fed. Color Standard 36375

View more

Foams

Product Foam Density Viscosity Cure System Application Life Appearance Data Sheet Comment
CF1-3710-2 50 lbs/ft3 N/A Platinum N/A Gray Download CF1-3710-2 data sheet Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

Product Details

Property Average Result
Cure System Platinum
Foam Density 50 lbs/ft3 (0.8 g/cm3)
Appearance Gray
Cure 1 minutes / RTV
Extrusion Rate 1 g/minute
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Tack Free Time 10 minutes
Comment Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

View more

CF3-2350 25 lbs/ft³ 90,000 cP Platinum N/A Gray Download CF3-2350 data sheet Useful where stability at higher and lower temperatures is required.

Product Details

Property Average Result
Foam Density 25 lbs/ft³ (0.4 g/cm³)
Viscosity 90,000 cP (90,000 mPa*s)
Cure System Platinum
Appearance Gray
Cure 45 minutes / 100 °C
Cure Type RTV
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Specific Gravity 1.1

View more

R-2370 10 lbs/ft3 4,700 cP Tin 28 minutes Tan Download R-2370 data sheet Low Density / Soft, 10 lb/ft^3 (0.16 g/cm^3)

Product Details

Property Average Result
Viscosity 4,700 cP (4,700 mPa*s)
Cure System Tin
Foam Density 10 lbs/ft3 (0.16 g/cm3)
Application Life 28 minutes
Appearance Tan
Cure 10 minutes / RTV
Mix Ratio 100:6
Non Volatile Content 100 %
Comment Low Density / Soft, 10 lb/ft^3 (0.16 g/cm^3)

View more

R-2380 19 lbs/ft3 3,600 cP Tin 32 minutes Tan Download R-2380 data sheet Medium Density / Soft, 19 lb/ft^3 (0.31 g/cm^3)

Product Details

Property Average Result
Viscosity 3,600 cP (3,600 mPa*s)
Cure System Tin
Foam Density 19 lbs/ft3 (0.3 g/cm3)
Application Life 32 minutes
Appearance Tan
Cure 10 minutes / RTV
Mix Ratio 100:6
Non Volatile Content 100 %
Comment Medium Density / Soft, 19 lb/ft^3 (0.31 g/cm^3)

View more

SFM5-2350 25 lbs/ft3 52,500 cP Platinum N/A Black Download SFM5-2350 data sheet Cure in place versatile tough foam. Application life 6 minutes.

Product Details

Property Average Result
Viscosity 52,500 cP (52,500 mPa*s)
Cure System Platinum
Foam Density 25 lbs/ft3 (0.4 g/cm3)
Appearance Black
Cure 33 minutes / 100 °C
Dielectric Strength 190 volts/mil (7.41 kV/mm)
Mix Ratio 1:1
Specific Gravity 1.1
Volume Resistivity 2,200,000,000,000,000 ohmcm
Work Time 23 minutes
Comment Cure in place versatile tough foam. Application life 6 minutes.

View more

Gels

Product Viscosity Penetration Work Time Mix Ratio Data Sheet Comment
FS-3502-1 1,200 cP N/A N/A 1:1 Download FS-3502-1 data sheet Firm Fluoro Gel;Recommended for long term solvent / fuel exposure, 6,000 cP maximum mixed viscosity after 3 hrs

Product Details

Property Average Result
Viscosity 1,200 cP (1,200 mPa*s)
Appearance White
Cure 4 hours / 50 °C
Cure System Platinum
Durometer 10 Type 00
Mix Ratio 1:1
Comment Firm Fluoro Gel;Recommended for long term solvent / fuel exposure, 6,000 cP maximum mixed viscosity after 3 hrs

View more

GEL-3500 11,250 cP N/A 12 hours 1:1 Download GEL-3500 data sheet Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

Product Details

Property Average Result
Viscosity 11,250 cP (11,250 mPa*s)
Work Time 12 hours
Appearance Translucent
Cure 45 minutes / 150 °C
Cure System Platinum
Durometer 50 Type 00
Mix Ratio 1:1
Operating Temperature -65 °C / 220 °C
Comment Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

View more

GEL-8150 500 cP 5 mm 4 hours 1:1 Download GEL-8150 data sheet Soft High Tack Gel

Product Details

Property Average Result
Viscosity 500 cP (500 mPa*s)
Penetration 5 mm
Work Time 4 hours
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Refractive Index 1.40
Specific Gravity 0.97
Volatile Content 1 %
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft High Tack Gel

View more

GEL-8170 600 cP 9 mm N/A 1:1 Download GEL-8170 data sheet Very Soft High Tack Gel;Max viscosity after 6 hrs is 2,000 cP

Product Details

Property Average Result
Viscosity 600 cP (600 mPa*s)
Penetration 9 mm
Appearance Translucent
Cure 90 minutes / 80 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Very Soft High Tack Gel;Max viscosity after 6 hrs is 2,000 cP

View more

GEL-8250 650 cP 5 mm 2 hours 1:1 Download GEL-8250 data sheet Soft Med Tack Gel;For applications requiring a broader operating temperature range.

Product Details

Property Average Result
Viscosity 650 cP (650 mPa*s)
Penetration 5 mm
Work Time 2 hours
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -115 °C / 265 °C
Refractive Index 1.43
Specific Gravity 1
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft Med Tack Gel;For applications requiring a broader operating temperature range.

View more

GEL1-8155 14,500 cP 0.4 mm N/A 1:1 Download GEL1-8155 data sheet Soft Low Tack Gel;Viscosity increases ~ 1.5X in 24 hrs (¼” diameter foot, 1.5 seconds)

Product Details

Property Average Result
Viscosity 14,500 cP (14,500 mPa*s)
Penetration 0.4 mm
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Non Volatile Content 100 %
Operating Temperature -65 °C / 200 °C
Refractive Index 1.40
Comment Soft Low Tack Gel;Viscosity increases ~ 1.5X in 24 hrs (¼” diameter foot, 1.5 seconds)

View more

Low Viscosity Elastomers

Product Viscosity Durometer Work Time Tensile Data Sheet Comment
CF1-3510 70,000 cP 20 Type A 7 hours 185 psi Download CF1-3510 data sheet LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

Product Details

Property Average Result
Cure System Platinum
Viscosity 70,000 cP (70,000 mPa*s)
Durometer 20 Type A
Tensile 185 psi (1.28 MPa)
Elongation 135 %
Appearance Red
Mix Ratio 10:1
Specific Gravity 1.44
Work Time 7 hours
Comment LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

View more

CF19-2615 1,300 cP 30 Type A 4 hours 120 psi Download CF19-2615 data sheet Versatile, clear coating, cure can be heat accelerated.

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,300 cP (1,300 mPa*s)
Durometer 30 Type A
Tensile 120 psi (0.83 MPa)
Elongation 100 %
Appearance Clear
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Refractive Index 1.41
Volume Resistivity 1,000,000,000,000,000 ohmcm
Work Time 4 hours
Comment Versatile, clear coating, cure can be heat accelerated.