Low Viscosity Elastomers

Product

Viscosity

Durometer

Work Time

Tensile

Data Sheet

Comment

70,000 cP

20 Type A

7 hours

185 psi

LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

Property	Average Result
Cure System	Platinum
Viscosity	70,000 cP (70,000 mPa*s)
Durometer	20 Type A
Tensile	185 psi (1.28 MPa)
Elongation	135 %
Appearance	Red
Mix Ratio	10:1
Specific Gravity	1.44
Work Time	7 hours
Comment	LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

1,300 cP

30 Type A

4 hours

120 psi

Versatile, clear coating, cure can be heat accelerated.

Property	Average Result
Cure System	Platinum
Viscosity	1,300 cP (1,300 mPa*s)
Durometer	30 Type A
Tensile	120 psi (0.83 MPa)
Elongation	100 %
Appearance	Clear
Cure	30 minutes / 150 °C
Dielectric Strength	500 volts/mil (19.5 kV/mm)
Mix Ratio	1:1
Refractive Index	1.41
Volume Resistivity	1,000,000,000,000,000 ohmcm
Work Time	4 hours
Comment	Versatile, clear coating, cure can be heat accelerated.