Refine results

Active filters Clear criteria

Apply

  • Show more

Add filters

Adhesives/Sealants

Refine results
Product Cure System Rheology Work Time Durometer Data Sheet Comment
CF2-3521-2 Platinum Thixotropic / non-slump 1 hours 35 Type A Download CF2-3521-2 data sheet Fuel Resistance

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 117 g/minute
Lap Shear 350 psi (2.41 MPa)
Durometer 35 Type A
Appearance Black
Cure 48 hours / RTV
Elongation 265 %
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.28
Tensile 600 psi (4.14 MPa)
Work Time 1 hours
Comment Fuel Resistance

View more

CF5-3521-2 Platinum Thixotropic / non-slump 3.5 hours 30 Type A Download CF5-3521-2 data sheet 50% M fluoro. Black and will RTV in 48 hrs

Product Details

Property Average Result
Cure System Platinum
Viscosity 240,000 cP (240,000 mPa*s)
Durometer 30 Type A
Appearance Black
Cure 48 hours / RTV
Elongation 275 %
Mix Ratio 1:1
Specific Gravity 1.3
Tear 35 ppi (6.17 kN/m)
Tensile 550 psi (3.79 MPa)
Work Time 3.5 hours
Comment 50% M fluoro. Black and will RTV in 48 hrs

View more

FS-3730 Acetoxy Thixotropic / non-slump N/A 33 Type A Download FS-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 180 g/minute
Lap Shear 350 psi (2.41 MPa)
Durometer 33 Type A
Appearance White
Cure 72 hours / RTV
Elongation 440 %
Mix Ratio 1 PART
Specific Gravity 1.4
Tack Free Time 25 minutes
Tear 55 ppi (9.7 kN/m)
Tensile 900 psi (6.21 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents.

View more

FS-3730-11 Acetoxy Thixotropic / non-slump N/A 40 Type A Download FS-3730-11 data sheet Lap Shear after 7 days *1) 275 psi (1.9 MPa)

Product Details

Property Average Result
Cure System Acetoxy
Lap Shear 275 psi (1.9 MPa)
Durometer 40 Type A
Appearance Dark Gray
Cure 72 hours / RTV
Elongation 275 %
Mix Ratio 1 PART
Specific Gravity 1.48
Tack Free Time 15 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Lap Shear after 7 days *1) 275 psi (1.9 MPa)

View more

FS-3730-2 Acetoxy Thixotropic / non-slump N/A 40 Type A Download FS-3730-2 data sheet Lap Shear after 7 days *3) 300 psi (2.1 MPa)

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 200 g/minute
Lap Shear 285 psi (1.97 MPa)
Durometer 40 Type A
Appearance Black
Cure 72 hours / RTV
Elongation 315 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.41
Tack Free Time 10 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 650 psi (4.48 MPa)
Comment Lap Shear after 7 days *3) 300 psi (2.1 MPa)

View more

FS-3775 Acetoxy Flowable / Self Leveling N/A 30 Type A Download FS-3775 data sheet High Temperature, Fuel Resistant

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 250 g/minute
Lap Shear 210 psi (1.45 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 400 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.29
Tack Free Time 8 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 450 psi (3.1 MPa)
Comment High Temperature, Fuel Resistant

View more

FS1-3730 Acetoxy Thixotropic / non-slump N/A 35 Type A Download FS1-3730 data sheet Bonds Aggressively

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 150 g/minute
Lap Shear 275 psi (1.9 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / 25 °C
Elongation 425 %
Mix Ratio 1 PART
Non Volatile Content 100 %
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.4
Tack Free Time 30 minutes
Tear 60 ppi (10.58 kN/m)
Tensile 850 psi (5.86 MPa)
Comment Bonds Aggressively

View more

FS3-3730 Acetoxy Thixotropic / non-slump N/A 35 Type A Download FS3-3730 data sheet 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 230 g/minute
Lap Shear 200 psi (1.38 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 400 %
Specific Gravity 1.35
Tack Free Time 15 minutes
Tear 50 ppi (8.82 kN/m)
Tensile 820 psi (5.66 MPa)
Comment 100%M Fluoro general all purpose adhesive for environments exposed to hydrocarbon fuels or solvents. Translucent. 200 psi (1.4 MPa) lap shear.

View more

FS9-3521 Platinum Flowable / Self Leveling 3 hours 29 Type A Download FS9-3521 data sheet 100% F, For applications requiring fuel and solvent resistance

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 50 g/minute
Lap Shear 280 psi (1.93 MPa)
Durometer 29 Type A
Appearance Brown
Cure 24 hours / RTV
Elongation 300 %
Mix Ratio 1:1
Specific Gravity 1.4
Tensile 750 psi (5.17 MPa)
Work Time 3 hours
Comment 100% F, For applications requiring fuel and solvent resistance

View more

R-1130 Oxime Thixotropic / non-slump N/A 35 Type A Download R-1130 data sheet Non-slump. Adhesive for a variety of substrates on or near electronic components. 485 psi (3.6 MPa), primed (SP-120) lap shear.

Product Details

Property Average Result
Cure System Oxime
Extrusion Rate 70 g/minute
Lap Shear 485 psi (3.34 MPa)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 325 %
Flow Rate 0.5 in (12.7 mm)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.1
Tack Free Time 25 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 850 psi (5.86 MPa)
Comment Non-slump. Adhesive for a variety of substrates on or near electronic components. 485 psi (3.6 MPa), primed (SP-120) lap shear.

View more

R-1140 Acetoxy Thixotropic / non-slump N/A 30 Type A Download R-1140 data sheet Non-slump. General all purpose adhesive for a variety of substrates. 625 psi (4.3 MPa), primed (SP-120) lap shear.

Product Details

Property Average Result
Cure System Acetoxy
Lap Shear 625 psi (4.31 MPa)
Durometer 30 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 350 %
Flow Rate 1.5 in (38.1 mm)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.09
Tack Free Time 7 minutes
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Non-slump. General all purpose adhesive for a variety of substrates. 625 psi (4.3 MPa), primed (SP-120) lap shear.

View more

R-2145 Platinum Flowable / Self Leveling 15 minutes 45 Type A Download R-2145 data sheet Primerless Adhesive;Gray, tough, fast cure adhesive. Will RTV. 145 psi (1.0 MPa), unprimed and 600 psi (4.1 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 180 g/minute
Lap Shear 145 psi (1 MPa)
Durometer 45 Type A
Appearance Dark Gray
Cure 2 hours / 65 °C
Dielectric Strength 825 volts/mil (32.18 kV/mm)
Elongation 400 %
Mix Ratio 1:1
Specific Gravity 1.17
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Tear 150 ppi (26.46 kN/m)
Tensile 1,050 psi (7.24 MPa)
Work Time 15 minutes
Comment Primerless Adhesive;Gray, tough, fast cure adhesive. Will RTV. 145 psi (1.0 MPa), unprimed and 600 psi (4.1 MPa) primed (CF1-135) lap shear.

View more

R-2160 Platinum Flowable / Self Leveling 1.5 hours 20 Type A Download R-2160 data sheet Iron Red, flowable legacy high performance elastomer at elevated temperatures.

Product Details

Property Average Result
Cure System Platinum
Viscosity 280,000 cP (280,000 mPa*s)
Durometer 20 Type A
Appearance Red
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Elongation 625 %
Mix Ratio 10:1
Non Volatile Content 100 %
Operating Temperature -65 °C / 315 °C
Specific Gravity 1.2
Tear 140 ppi (24.69 kN/m)
Tensile 750 psi (5.17 MPa)
Volume Resistivity 100,000,000,000,000 ohmcm
Work Time 1.5 hours
Comment Iron Red, flowable legacy high performance elastomer at elevated temperatures.

View more

R-2550 Alkoxy Flowable / Self Leveling 6 hours 35 Type A Download R-2550 data sheet Resists breakdown at high temperatures. Translucent and 1 hr. pot life. Not recommended for deep section cures.

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 9,000 cP (9,000 mPa*s)
Durometer 35 Type A
Appearance Translucent
Cure 7 days / RTV
Elongation 175 %
Mix Ratio 100:0.5
Non Volatile Content 100 %
Operating Temperature -115 °C / 260 °C
Refractive Index 1.43
Specific Gravity 1.08
Tear 20 ppi (3.53 kN/m)
Tensile 500 psi (3.45 MPa)
Work Time 6 hours
Comment Resists breakdown at high temperatures. Translucent and 1 hr. pot life. Not recommended for deep section cures.

View more

R-2560 Alkoxy Flowable / Self Leveling 1 minutes 55 Type A Download R-2560 data sheet Resists breakdown at high temperatures. Red and 1 hr. pot life. Not recommended for deep section cures.

Product Details

Property Average Result
Cure System Alkoxy
Viscosity 31,000 cP (31,000 mPa*s)
Lap Shear 385 psi (2.66 MPa)
Durometer 55 Type A
Appearance Red
Cure 7 days / RTV
Elongation 125 %
Mix Ratio 100:0.5
Non Volatile Content 100 %
Operating Temperature -115 °C / 260 °C
Specific Gravity 1.41
Tack Free Time 2 hours
Tensile 700 psi (4.83 MPa)
Work Time 1 minutes
Comment Resists breakdown at high temperatures. Red and 1 hr. pot life. Not recommended for deep section cures.

View more

R-2630 Platinum Flowable / Self Leveling 15 hours 60 Type A Download R-2630 data sheet Carbon filled.

Product Details

Property Average Result
Cure System Platinum
Durometer 60 Type A
Appearance Black
Cure 30 minutes / 150 °C
Elongation 95 %
Mix Ratio 10:1
Operating Temperature -65 °C / 200 °C
Specific Gravity 1.1
Tear 40 ppi (7.05 kN/m)
Tensile 690 psi (4.76 MPa)
Volume Resistivity 6 ohmcm
Work Time 15 hours
Comment Carbon filled.

View more

R-2682-12 Platinum N/A N/A N/A Download R-2682-12 data sheet For applications requiring shorter processing times, easy clean-up, and consistent bond thickness. Adheres to silicone, and some metals or plastics. Sheet is 0.013 inches (0.3 mm) and cures on surfaces where the Activator is applied. Cures at room temperature or rapidly with heat.

Product Details

Property Average Result
Cure System Platinum
Lap Shear 100 psi (0.69 MPa)
Appearance Translucent
Application Life 4 minutes
Cure 4 hours / 65 °C
Comment For applications requiring shorter processing times, easy clean-up, and consistent bond thickness. Adheres to silicone, and some metals or plastics. Sheet is 0.013 inches (0.3 mm) and cures on surfaces where the Activator is applied. Cures at room temperature or rapidly with heat.

View more

R1-2145 Platinum Flowable / Self Leveling 1 minutes 45 Type A Download R1-2145 data sheet Primerless Adhesive;Gray tough, fast cure adhesive with 1 hour pot life. Will RTV. 145 psi (1.0 MPa), unprimed and 625 psi (4.3 MPa) primed (CF1-135) lap shear.

Product Details

Property Average Result
Cure System Platinum
Extrusion Rate 140 g/minute
Lap Shear 145 psi (1 MPa)
Durometer 45 Type A
Appearance Dark Gray
Cure 2 hours / 65 °C
Dielectric Strength 825 volts/mil (32.18 kV/mm)
Elongation 400 %
Mix Ratio 1:1
Specific Gravity 1.16
Stress at Strain 525 psi / 200 % (3.62 MPa / 200 %)
Tear 190 ppi (33.51 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 1 minutes
Comment Primerless Adhesive;Gray tough, fast cure adhesive with 1 hour pot life. Will RTV. 145 psi (1.0 MPa), unprimed and 625 psi (4.3 MPa) primed (CF1-135) lap shear.

View more

R33-2186 Platinum Flowable / Self Leveling 2 hours 20 Type A Download R33-2186 data sheet RTV Primerless Adhesive;Fast cure.

Product Details

Property Average Result
Cure System Platinum
Viscosity 124,350 cP (124,350 mPa*s)
Durometer 20 Type A
Appearance Translucent
Cure 24 hours / RTV
Elongation 725 %
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.12
Tear 150 ppi (26.46 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 2 hours
Comment RTV Primerless Adhesive;Fast cure.

View more

R33-2186-1 N/A Flowable / Self Leveling 2 hours 20 Type A Download R33-2186-1 data sheet N/A

Product Details

Property Average Result
Viscosity 80,000 cP (80,000 mPa*s)
Durometer 20 Type A
Appearance White
Elongation 740 %
Specific Gravity 1.12
Tear 135 ppi (23.81 kN/m)
Tensile 1,000 psi (6.9 MPa)
Work Time 2 hours

View more

R4-1140 Acetoxy Flowable / Self Leveling N/A 25 Type A Download R4-1140 data sheet Primerless Adhesive;Self leveling. General all purpose adhesive for a variety of substrates.

Product Details

Property Average Result
Cure System Acetoxy
Extrusion Rate 100 g/minute
Durometer 25 Type A
Appearance Translucent
Cure 72 hours / RTV
Elongation 750 %
Flow Rate 2 in (50.8 mm)
Mix Ratio 1 PART
Specific Gravity 1.12
Stress at Strain 110 psi / N/A (0.76 MPa / N/A)
Tack Free Time 10 minutes
Tear 100 ppi (17.64 kN/m)
Tensile 1,400 psi (9.66 MPa)
Volatile Content 2.4 %
Comment Primerless Adhesive;Self leveling. General all purpose adhesive for a variety of substrates.

View more

Coatings/Dispersions

Product Cure System Durometer Data Sheet Comment
Acetoxy 40 Type A Download data sheet 240*3) psi (1.7Mpa) Lap Shear at 7 D @ R.T., H / Fed. Color Standard 36118

Product Details

Property Average Result
Appearance Gray
Tack Free Time 20 minutes
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 40 Type A
Elongation 325 %
Lap Shear 290 psi (2 MPa)
Specific Gravity 1.48
Tear 45 ppi (7.94 kN/m)
Tensile 725 psi (5 MPa)
Comment 240*3) psi (1.7Mpa) Lap Shear at 7 D @ R.T., H / Fed. Color Standard 36118

CV1-1146-2 Oxime N/A Download CV1-1146-2 data sheet N/A

Product Details

Property Average Result
Viscosity 1,125 cP (1,125 mPa*s)
Appearance Black
Tack Free Time 2 hours
Cure System Oxime

View more

R-1009 Oxime 45 Type A Download R-1009 data sheet High strength coating recommend for coating PCBs and other electronic assemblies.

Product Details

Property Average Result
Viscosity 6,150 cP (6,150 mPa*s)
Non Volatile Content 32 %
Appearance Translucent
Tack Free Time 1.5 hours
Cure 7 days / RTV
Cure System Oxime
Durometer 45 Type A
Elongation 650 %
Specific Gravity 1.1
Tear 95 ppi (16.75 kN/m)
Tensile 1,150 psi (7.93 MPa)
Comment High strength coating recommend for coating PCBs and other electronic assemblies.

View more

R-1082 Acetoxy 25 Type A Download R-1082 data sheet Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

Product Details

Property Average Result
Viscosity 700 cP (700 mPa*s)
Non Volatile Content 29 %
Appearance Translucent
Cure 5 days / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 950 %
Refractive Index 1.41
Specific Gravity 1.09
Stress at Strain 160 psi / 300 % (1.1 Mpa / 300 %)
Tear 125 ppi (22.05 kN/m)
Tensile 1,425 psi (9.83 MPa)
Comment Great adhesion to a variety of substrates. Not recommended where corrosion is of concern.

View more

R-1182 Acetoxy N/A Download R-1182 data sheet One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

Product Details

Property Average Result
Non Volatile Content 7 %
Appearance Translucent
Cure RTV
Cure System Acetoxy
Comment One Part and cures at room temperature. Acetic acid cure by-product therefore not recommended where corrosion is of concern.

View more

R-2180 Platinum 40 Type A Download R-2180 data sheet High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

Product Details

Property Average Result
Viscosity 3,075 cP (3,075 mPa*s)
Non Volatile Content 20 %
Appearance Translucent
Cure 45 minutes / 75 °C 135 minutes / 150 °C
Cure System Platinum
Durometer 40 Type A
Elongation 1,050 %
Mix Ratio 1:1
Refractive Index 1.41
Stress at Strain 150 psi / 100 % (1.03 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,700 psi (11.72 MPa)
Work Time 72 hours
Comment High strength coating and primer is recommended to increase adhesion. Requires heat to cure.

View more

R-2180-2 Platinum 45 Type A Download R-2180-2 data sheet Cure: 30 M / 25 C : 45 M / 75 C : 135 M / 150 C, 20% Solids

Product Details

Property Average Result
Viscosity 3,275 cP (3,275 mPa*s)
Non Volatile Content 20 %
Appearance Translucent
Cure 30 minutes / RTV 45 minutes / 75 °C 135 minutes / 150 °C
Cure System Platinum
Durometer 45 Type A
Elongation 1,000 %
Mix Ratio 1:1
Stress at Strain 140 psi / 100 % (0.97 MPa / 100 %)
Tear 300 ppi (52.91 kN/m)
Tensile 1,650 psi (11.38 MPa)
Comment Cure: 30 M / 25 C : 45 M / 75 C : 135 M / 150 C, 20% Solids

View more

R-3930 Acetoxy 30 Type A Download R-3930 data sheet 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

Product Details

Property Average Result
Viscosity 735 cP (735 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 30 Type A
Elongation 400 %
Specific Gravity 1.36
Tear 40 ppi (7.05 kN/m)
Tensile 750 psi (5.17 MPa)
Comment 100%M Fluoro, fuel and hydrocarbon solvent resistant high strength coating.

View more

R-3975 Acetoxy 25 Type A Download R-3975 data sheet Dispersion Coating, 60% Solids

Product Details

Property Average Result
Viscosity 1,625 cP (1,625 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 25 Type A
Elongation 400 %
Mix Ratio 1 PART
Specific Gravity 1.29
Tear 35 ppi (6.17 kN/m)
Tensile 425 psi (2.93 MPa)
Comment Dispersion Coating, 60% Solids

View more

R1-3930-1 Acetoxy 37 Type A Download R1-3930-1 data sheet Slight addition of heat will accelerate cure

Product Details

Property Average Result
Appearance White
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 37 Type A
Elongation 334 %
Mix Ratio 1 PART
Tack Free Time 273 minutes
Tear 52 ppi (9 kN/m)
Tensile 739 psi (5.09 MPa)
Comment Slight addition of heat will accelerate cure

View more

R3-1075 Oxime 40 Type A Download R3-1075 data sheet Dispersion Coating / Conformal, 60% Solids

Product Details

Property Average Result
Viscosity 3,300 cP (3,300 mPa*s)
Non Volatile Content 60 %
Appearance Translucent
Tack Free Time 80 minutes
Cure 7 days / 25 °C
Cure System Oxime
Dielectric Strength 1,250 volts/mil (48.75 kV/mm)
Durometer 40 Type A
Elongation 350 %
Mix Ratio 1 PART
Operating Temperature -65 °C / 240 °C
Solvent Xylene
Specific Gravity 1.06
Tear 40 ppi (7.05 kN/m)
Tensile 700 psi (4.83 MPa)
Comment Dispersion Coating / Conformal, 60% Solids

View more

R4-3930-11 Acetoxy 45 Type A Download R4-3930-11 data sheet For protecting or bonding hardware components exposed to gasoline or aviation fuels

Product Details

Property Average Result
Appearance Gray
Cure 72 hours / RTV
Cure System Acetoxy
Durometer 45 Type A
Elongation 480 %
Mix Ratio 1:1
Tear 71 ppi (13 kN/m)
Tensile 750 psi (5 MPa)
Comment For protecting or bonding hardware components exposed to gasoline or aviation fuels

View more

Electrically Conductive/Static Dissipative

Product Volume Resistivity Viscosity Cure System Durometer Tensile Data Sheet Comment
R-1505 8 ohmcm N/A Oxime 75 Type A 525 psi Download R-1505 data sheet 8 ohmcm. Static Dissipation

Product Details

Property Average Result
Volume Resistivity 8 ohmcm
Cure System Oxime
Durometer 75 Type A
Tensile 525 psi (3.62 MPa)
Appearance Black
Cure 7 days / 25 °C
Dielectric Strength 10 volts/mil (0.39 kV/mm)
Elongation 25 %
Flow Rate 0.1 in (2.54 mm)
Lap Shear 290 psi (2 MPa)
Mix Ratio 1 PART
Non Volatile Content 100 %
Specific Gravity 1.23
Tack Free Time 10 minutes
Thermal Conductivity 0.3 W/(mK)
Comment 8 ohmcm. Static Dissipation

View more

R-2631 70 ohmcm N/A Platinum 45 Type A 615 psi Download R-2631 data sheet Carbon filled.

Product Details

Property Average Result
Volume Resistivity 70 ohmcm
Cure System Platinum
Durometer 45 Type A
Tensile 615 psi (4.24 MPa)
Appearance Black
Cure 30 minutes / 150 °C
Elongation 275 %
Extrusion Rate 100 g/minute
Mix Ratio 1:1
Specific Gravity 1.08
Tear 55 ppi (9.7 kN/m)
Comment Carbon filled.

View more

R-2637 0.01 ohmcm N/A Platinum 60 Type A 210 psi Download R-2637 data sheet Electrically Conductive RTV Silicone. Mixes to smooth paste, can be screen printed.

Product Details

Property Average Result
Volume Resistivity 0.01 ohmcm
Cure System Platinum
Durometer 60 Type A
Tensile 210 psi (1.45 MPa)
Appearance Tan
Cure 30 minutes / 150 °C
Dielectric Strength 5 volts/mil (0.2 kV/mm)
Elongation 275 %
Mix Ratio 20:1
Specific Gravity 3.6
Tack Free Time 5 hours
Thermal Conductivity 1.5 W/(mK)
Work Time 4 hours
Comment Electrically Conductive RTV Silicone. Mixes to smooth paste, can be screen printed.

View more

Foams

Product Foam Density Viscosity Cure System Application Life Appearance Data Sheet Comment
CF1-3710-2 50 lbs/ft3 N/A Platinum N/A Gray Download CF1-3710-2 data sheet Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

Product Details

Property Average Result
Cure System Platinum
Foam Density 50 lbs/ft3 (0.8 g/cm3)
Appearance Gray
Cure 1 minutes / RTV
Extrusion Rate 1 g/minute
Mix Ratio 1:1
Operating Temperature -65 °C / 240 °C
Tack Free Time 10 minutes
Comment Cure in place fuel resistant foam for short term fuel exposure, application life 10 minutes

View more

CF3-2350 25 lbs/ft³ 90,000 cP Platinum N/A Gray Download CF3-2350 data sheet Useful where stability at higher and lower temperatures is required.

Product Details

Property Average Result
Foam Density 25 lbs/ft³ (0.4 g/cm³)
Viscosity 90,000 cP (90,000 mPa*s)
Cure System Platinum
Appearance Gray
Cure 45 minutes / 100 °C
Cure Type RTV
Mix Ratio 1:1
Rheology Flowable / Self Leveling
Specific Gravity 1.1

View more

R-2370 10 lbs/ft3 4,700 cP Tin 28 minutes Tan Download R-2370 data sheet Low Density / Soft, 10 lb/ft^3 (0.16 g/cm^3)

Product Details

Property Average Result
Viscosity 4,700 cP (4,700 mPa*s)
Cure System Tin
Foam Density 10 lbs/ft3 (0.16 g/cm3)
Application Life 28 minutes
Appearance Tan
Cure 10 minutes / RTV
Mix Ratio 100:6
Non Volatile Content 100 %
Comment Low Density / Soft, 10 lb/ft^3 (0.16 g/cm^3)

View more

SFM5-2350 25 lbs/ft3 52,500 cP Platinum N/A Black Download SFM5-2350 data sheet Cure in place versatile tough foam. Application life 6 minutes.

Product Details

Property Average Result
Viscosity 52,500 cP (52,500 mPa*s)
Cure System Platinum
Foam Density 25 lbs/ft3 (0.4 g/cm3)
Appearance Black
Cure 33 minutes / 100 °C
Dielectric Strength 190 volts/mil (7.41 kV/mm)
Mix Ratio 1:1
Specific Gravity 1.1
Volume Resistivity 2,200,000,000,000,000 ohmcm
Work Time 23 minutes
Comment Cure in place versatile tough foam. Application life 6 minutes.

View more

Gels

Product Viscosity Work Time Mix Ratio Data Sheet Comment
GEL-3500 11,250 cP 12 hours 1:1 Download GEL-3500 data sheet Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

Product Details

Property Average Result
Viscosity 11,250 cP (11,250 mPa*s)
Work Time 12 hours
Appearance Translucent
Cure 45 minutes / 150 °C
Cure System Platinum
Durometer 50 Type 00
Mix Ratio 1:1
Operating Temperature -65 °C / 220 °C
Comment Firm Fluoro Gel;Recommended for short term exposure to fuels and solvent

View more

GEL-8150 500 cP 4 hours 1:1 Download GEL-8150 data sheet Soft High Tack Gel

Product Details

Property Average Result
Viscosity 500 cP (500 mPa*s)
Penetration 5 mm
Work Time 4 hours
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Refractive Index 1.40
Specific Gravity 0.97
Volatile Content 1 %
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft High Tack Gel

View more

GEL-8170 600 cP N/A 1:1 Download GEL-8170 data sheet Very Soft High Tack Gel;Max viscosity after 6 hrs is 2,000 cP

Product Details

Property Average Result
Viscosity 600 cP (600 mPa*s)
Penetration 9 mm
Appearance Translucent
Cure 90 minutes / 80 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -65 °C / 200 °C
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Very Soft High Tack Gel;Max viscosity after 6 hrs is 2,000 cP

View more

GEL-8250 650 cP 2 hours 1:1 Download GEL-8250 data sheet Soft Med Tack Gel;For applications requiring a broader operating temperature range.

Product Details

Property Average Result
Viscosity 650 cP (650 mPa*s)
Penetration 5 mm
Work Time 2 hours
Appearance Translucent
Cure 30 minutes / 100 °C
Cure System Platinum
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Operating Temperature -115 °C / 265 °C
Refractive Index 1.43
Specific Gravity 1
Volume Resistivity 1,000,000,000,000,000 ohmcm
Comment Soft Med Tack Gel;For applications requiring a broader operating temperature range.

View more

GEL1-8155 14,500 cP N/A 1:1 Download GEL1-8155 data sheet Soft Low Tack Gel;Viscosity increases ~ 1.5X in 24 hrs (¼” diameter foot, 1.5 seconds)

Product Details

Property Average Result
Viscosity 14,500 cP (14,500 mPa*s)
Penetration 0.4 mm
Appearance Translucent
Cure 30 minutes / 150 °C
Cure System Platinum
Mix Ratio 1:1
Non Volatile Content 100 %
Operating Temperature -65 °C / 200 °C
Refractive Index 1.40
Comment Soft Low Tack Gel;Viscosity increases ~ 1.5X in 24 hrs (¼” diameter foot, 1.5 seconds)

View more

Liquid Silicone Rubbers

Product Durometer Tensile Elongation Tear Data Sheet Comment
FS-3511 40 Type A 1,150 psi 335 % 60 ppi Download FS-3511 data sheet LSR Fluoro Elastomer;For long term fuel or solvent exposure. Can be liquid injection molded and requires heat to cure. Recommend SP-120 or SP-201

Product Details

Property Average Result
Cure System Platinum
Durometer 40 Type A
Tensile 1,150 psi (7.93 MPa)
Elongation 335 %
Tear 60 ppi (10.58 kN/m)
Appearance Translucent
Cure 30 minutes / 150 °C
Extrusion Rate 35 g/minute
Mix Ratio 1:1
Specific Gravity 1.39
Work Time 24 hours
Comment LSR Fluoro Elastomer;For long term fuel or solvent exposure. Can be liquid injection molded and requires heat to cure. Recommend SP-120 or SP-201

View more

Low Viscosity Elastomers

Product Viscosity Durometer Work Time Tensile Data Sheet Comment
CF1-3510 70,000 cP 20 Type A 7 hours 185 psi Download CF1-3510 data sheet LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

Product Details

Property Average Result
Cure System Platinum
Viscosity 70,000 cP (70,000 mPa*s)
Durometer 20 Type A
Tensile 185 psi (1.28 MPa)
Elongation 135 %
Appearance Red
Mix Ratio 10:1
Specific Gravity 1.44
Work Time 7 hours
Comment LCE Fluoro Elastomer;100% Fluorosilicone, flowable mixed viscosity, and 7 hr. pot life.

View more

CF19-2615 1,300 cP 30 Type A 4 hours 120 psi Download CF19-2615 data sheet Versatile, clear coating, cure can be heat accelerated.

Product Details

Property Average Result
Cure System Platinum
Viscosity 1,300 cP (1,300 mPa*s)
Durometer 30 Type A
Tensile 120 psi (0.83 MPa)
Elongation 100 %
Appearance Clear
Cure 30 minutes / 150 °C
Dielectric Strength 500 volts/mil (19.5 kV/mm)
Mix Ratio 1:1
Refractive Index 1.41
Volume Resistivity 1,000,000,000,000,000 ohmcm
Work Time 4 hours
Comment Versatile, clear coating, cure can be heat accelerated.

View more

Primers

Product Non Volatile Content Solvent Data Sheet Comment
CF1-135 4.5 % Naptha Download CF1-135 data sheet Use with addition cure silicones.

Product Details

Property Average Result
Non Volatile Content 4.5 %
Specific Gravity 0.77
Appearance Translucent
Cure System Condensation
Refractive Index 1.41
Comment Use with addition cure silicones.

View more

CF1-141 6 % IPA Download CF1-141 data sheet Addition Cure Systems, IPA Based, 6% Solids

Product Details

Property Average Result
Non Volatile Content 6 %
Specific Gravity 0.8
Appearance Red
Cure System Hydrolysis
Comment Addition Cure Systems, IPA Based, 6% Solids

View more

CF6-135 9 % Naptha Download CF6-135 data sheet Recommended where platinum inhibition is of concern.

Product Details

Property Average Result
Non Volatile Content 9 %
Specific Gravity 0.78
Appearance Translucent
Cure System Condensation
Comment Recommended where platinum inhibition is of concern.

View more

SP-120 4 % Naptha Download SP-120 data sheet Use with addition or condensation cure. Available in Red.

Product Details

Property Average Result
Non Volatile Content 4 %
Specific Gravity 0.77
Appearance Translucent
Cure System Condensation
Lap Shear 315 psi (2.17 MPa)
Comment Use with addition or condensation cure. Available in Red.

View more

SP-121 3.2 % Naptha Download SP-121 data sheet Use with addition or condensation cure.

Product Details

Property Average Result
Non Volatile Content 3.2 %
Specific Gravity 0.76
Appearance Red
Cure System Condensation
Lap Shear 300 psi (2.07 MPa)
Comment Use with addition or condensation cure.

View more

SP-270 15 % Naptha Download SP-270 data sheet Improved adhesion to gold - Recommended where platinum inhibition is of concern such as when bonding on polyphenylsulphone.

Product Details

Property Average Result
Non Volatile Content 15 %
Specific Gravity 0.8
Appearance Translucent
Cure System Condensation
Lap Shear 166 psi (1.14 MPa)
Refractive Index 1.40
Comment Improved adhesion to gold - Recommended where platinum inhibition is of concern such as when bonding on polyphenylsulphone.

View more

Resins

Product Viscosity Durometer Appearance Data Sheet Comment
CF2-4721 130 cP 75 Type D Light Amber Download CF2-4721 data sheet Hard Resin;Contains vinyl-specific peroxide in 1.52 RI resin. Requires heat to cure and oxygen inhibited. Not recommended for general encapsulation.

Product Details

Property Average Result
Viscosity 130 cP (130 mPa*s)
Durometer 75 Type D
Appearance Light Amber
Cure 15 minutes / 150 °C
Cure System Peroxide
Non Volatile Content 100 %
Refractive Index 1.52
Specific Gravity 1.09
Comment Hard Resin;Contains vinyl-specific peroxide in 1.52 RI resin. Requires heat to cure and oxygen inhibited. Not recommended for general encapsulation.

View more

Specialty Polymers

Product Refractive Index Viscosity Mmol % Pt Appearance Data Sheet Comment
CF-4721 1.52 125 cP 4.7 Vi/g N/A Clear Download CF-4721 data sheet 75 Type D with Dicumyl Peroxide Catalyst (Catalyst Not Included)

Product Details

Property Average Result
Refractive Index 1.52
Viscosity 125 cP (125 mPa*s)
Mmol 4.7 Vi/g
Appearance Clear
Cure 15 minutes / 150 °C
Durometer 75 Type D
Mix Ratio 100:1
Non Volatile Content 100 %
Specific Gravity 1.1
Volume Resistivity 63,000,000,000,000 ohmcm
Comment 75 Type D with Dicumyl Peroxide Catalyst (Catalyst Not Included)

View more

Thermally Conductive

Product Thermal Conductivity Mix Ratio Viscosity Extrusion Rate Cure System Data Sheet Comment
CF1-3800 1.25 W/(mK) 15:1 N/A N/A Platinum Download CF1-3800 data sheet 50% M Fluoro. Recommended for short term exposure to solvents and fuel. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 1.25 W/(mK)
Cure System Platinum
Tensile 125 psi (0.86 MPa)
Appearance White
Cure 30 minutes / 150 °C
Durometer 50 Type A
Elongation 50 %
Mix Ratio 15:1
Specific Gravity 1.53
Work Time 90 minutes
Comment 50% M Fluoro. Recommended for short term exposure to solvents and fuel. (Contains Boron Nitride)

View more

R-2930 1.46 W/(mK) 15:1 N/A N/A Platinum Download R-2930 data sheet Smooth Paste;1.45 W/mK, 3 hr. pot life. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 1.46 W/(mK)
Cure System Platinum
Tensile 260 psi (1.79 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 880 volts/mil (34.32 kV/mm)
Durometer 80 Type A
Elongation 20 %
Flow Rate 0.3 inches (7.62 mm)
Mix Ratio 15:1
Operating Temperature -65 °C / 240 °C
Specific Gravity 1.55
Work Time 3 hours
Comment Smooth Paste;1.45 W/mK, 3 hr. pot life. (Contains Boron Nitride)

View more

R-2939 0.75 W/(mK) 15:1 70,000 cP N/A Platinum Download R-2939 data sheet 0.75 W/mK, 4 hr. pot life. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 0.75 W/(mK)
Viscosity 70,000 cP (70,000 mPa*s)
Cure System Platinum
Tensile 300 psi (2.07 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 810 volts/mil (31.59 kV/mm)
Durometer 70 Type A
Elongation 70 %
Mix Ratio 15:1
Specific Gravity 1.34
Tear 45 ppi (7.94 kN/m)
Work Time 4 hours
Comment 0.75 W/mK, 4 hr. pot life. (Contains Boron Nitride)

View more

R-2940 0.84 W/(mK) 20:1 N/A N/A Platinum Download R-2940 data sheet Smooth Paste;0.8 W/mK, 5 hr. pot life.

Product Details

Property Average Result
Thermal Conductivity 0.84 W/(mK)
Cure System Platinum
Tensile 700 psi (4.83 MPa)
Appearance Gray
Cure 30 minutes / 150 °C
Dielectric Strength 450 volts/mil (17.55 kV/mm)
Durometer 90 Type A
Elongation 35 %
Mix Ratio 20:1
Specific Gravity 2.41
Tack Free Time 24 hours
Tear 65 ppi (11.46 kN/m)
Work Time 5 hours
Comment Smooth Paste;0.8 W/mK, 5 hr. pot life.

View more

R-2949 0.75 W/(mK) 15:1 75,000 cP N/A Platinum Download R-2949 data sheet For applications requiring a broader operating temperature range. (Contains Boron Nitride)

Product Details

Property Average Result
Thermal Conductivity 0.75 W/(mK)
Viscosity 75,000 cP (75,000 mPa*s)
Cure System Platinum
Tensile 275 psi (1.9 MPa)
Appearance White
Cure 30 minutes / 150 °C
Dielectric Strength 920 volts/mil (35.88 kV/mm)
Durometer 75 Type A
Elongation 50 %
Mix Ratio 15:1
Specific Gravity 1.37
Tear 45 ppi (7.94 kN/m)
Work Time 3.5 hours
Comment For applications requiring a broader operating temperature range. (Contains Boron Nitride)

View more